• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.28 no.6
• /
• pp.235-242
• /
• 2018

High temperature electrical conductivity of Aluminum Nitride (AlN) ceramics sintered with $Y_2O_3$ as a sintering aid has been investigated with respect to various sintering conditions and MgO-dopant. When magnesium oxide is added as a dopant, liquid glass-film and crystalline phases such as spinel, perovskite are formed as second phases, which affects their electrical properties. According to high temperature impedance analysis, MgO doping leads to reduction of activation energy and electrical resistivity due to AlN grains. On the other hand, the activation energy and electrical resistivity due to grain boundary were increased by MgO doping. This is a result of the formation of liquid glass film in the grain boundary, which contains Mg ions, or the elevation of schottky barrier due to the precipitation of Mg in the grain boundary. For the annealed sample of MgO doped AlN, the electrical resistivity and activation energy were increased further compared to MgO doped AlN, which results from diffusion of Mg in the grains from grain boundary as shown in the microstructure.

• Journal of Powder Materials
• /
• v.28 no.4
• /
• pp.293-300
• /
• 2021

We investigate the effect of phosphorous content on the microstructure and magnetic properties of Fe_83.2Si_5.33-0.33xB_10.67-0.67xP_xCu_0.8 (x = 1-4 at.%) nanocrystalline soft magnetic alloys. The simultaneous addition of Cu and P to nanocrystalline alloys reportedly decreases the nanocrystalline size significantly, to 10-20 nm. In the P-containing nanocrystalline alloy, P atoms are distributed in an amorphous residual matrix, which suppresses grain growth, increases permeability, and decreases coercivity. In this study, nanocrystalline ribbons with a composition of Fe_83.2Si_5.33-0.33xB_10.67-0.67xP_xCu_0.8 (x = 1-4 at.%) are fabricated by rapid quenching melt-spinning and thermal annealing. It is demonstrated that the addition of a small amount of P to the alloy improves the glass-forming ability and increases the resistance to undesirable Fe_x(B,P) crystallization. Among the alloys investigated in this work, an Fe_83.2Si₅B₁₀P₁Cu_0.8 nanocrystalline ribbon annealed at 460℃ exhibits excellent soft-magnetic properties including low coercivity, low core loss, and high saturation magnetization. The uniform nanocrystallization of the Fe_83.2Si₅B₁₀P₁Cu_0.8 alloy is confirmed by high-resolution transmission electron microscopy analysis.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.4
• /
• pp.136-142
• /
• 2022

The crystal structure, grain growth behavior, and dielectric properties of BaTiO₃ have been studied with the addition of Dy₂O₃. The powders were synthesized at ratios of (100-x)BaTiO₃-xDy₂O₃ (mol%, x = 0, 0.5, 1.0, 2.0) by a conventional solid-state synthesis, and the powder compacts were sintered at 1250℃ for 2 hours in air. As the amount of added Dy₂O₃ was increased, the crystal structure of the sintered samples changed from a tetragonal to a pseudo-cubic structure, and the tetragonality decreased. In addition, a secondary phase of Ba₁₂Dy_4.67Ti₈O₃₅ appeared when Dy₂O₃ was added. The average grain size after sintering decreased and abnormal grains appeared as the amount of Dy₂O₃ increased. It can be explained that the grain growth behavior of the Dy₂O₃ added-BaTiO₃ occurs due to the two-dimensional nucleation and growth, and is governed by the interface reaction. Further, the correlation between crystal structure, microstructure, and dielectric properties was discussed.

• Journal of the Korean Vacuum Society
• /
• v.21 no.5
• /
• pp.233-241
• /
• 2012

We have deposited the bilayer consisted of the underlayer and the overlayer by using DC magnetron sputter on Single crystal MgO (001) substrate. This bilayer was fabricated at fixed annealing temperature and time. We have controlled agglomeration effect by changing of the bilayer thickness. Finally, we have made the self-organization and nano-structured film. In this processing, we have made nano-dot which consists of the underlayer and the overlayer, unlike the existing method called the agglomeration effect in the single layer. The underlayer has deposited using Ti, Cr and Co. And the overlayer has deposited with Ag. Through the analysis of Atomic force microscopy (AFM), the microstructure of underlayer is observed by AFM to confirm the formation of nano-dot. As the nano-dot through above processing, we have found that the nano-dot has the different shape. As a result, when we manufactured nano-dot through the agglomeration effect of bi-layer, the best matching material is Ti for underlayer. And also, we have found that MgO/Ti/Ag samples have been grown expitaxially toward the direction of MgO (001) by X-ray Diffraction analysis.

• Journal of the Korea Concrete Institute
• /
• v.14 no.1
• /
• pp.118-125
• /
• 2002

Hydration is the main reason for the growth of the material properties. An exact parameter to control the chemical and physical process is not the time, but the degree of hydration. Therefore, it is reasonable that development of all material properties and the formation of microstructure should be formulated in terms of degree of hydration. Mathematical formulation of degree of hydration is based on combination of reaction rate functions. The effect of moisture conditions as well as temperature on the rate of reaction is considered in the degree of hydration model. This effect is subdivided into two contributions: water shortage and water distribution. The former is associated with the effect of W/C ratio on the progress of hydration. The water needed for progress of hydration do not exist and there is not enough space for the reaction products to form. The tatter is associated with the effect of free capillary water distribution in the pore system. Physically absorption layer does not contribute to progress of hydration and only free water is available for further hydration. In this study, the effects of chemical composition of cement, W/C ratio, temperature, and moisture conditions on the degree of hydration are considered. Parameters that can be used to indicate or approximate the real degree of hydration are liberated heat of hydration, amount of chemically bound water, and chemical shrinkage, etc. Thus, the degree of heat liberation and adiabatic temperature rise could be determined by prediction of degree of hydration.

• Journal of Chest Surgery
• /
• v.41 no.2
• /
• pp.177-188
• /
• 2008

Background: To evaluate the effects of inhaled nitric oxide (NO) and sphingosine 1-phosphate (S1P) as potential therapeutic agents of acute lung injury, we analyzed the morphology in vivo of the pulmonary microstructure using intravital videomicroscopy in a rat model of acute lung injury. Material and Method: Sprague Dawley rats were divided into five groups: a control group that underwent normal saline aspiration, an acute lung injury (ALI) group that underwent hydrochloric acid aspiration, and three treatment groups that underwent hydrochloric acid aspiration and were administered therapeutic agents- the S1P group, the NO group, and the S1P+NO group (n=7 per group). To quantify alveolar compliance and interstitial edema, the diameters of all measurable alveoli and interalveolar septa were averaged at one and two hours after aspiration. Alveolar compliance was determined according to diameter changes during the respiratory cycle and the change in tidal volume. Result: At two hours after aspiration, the mean alveolar compliance (% change) in the All group decreased significantly versus the control group of rats (respiratory cycle: 1.9% for the ALI group vs 6.5% for the control group, p=0.03; tidal volume: 3.2% for the ALI group vs 9.1% for the control group, p=0.003) and versus the NO group (tidal volume: 3.2% for the ALI group vs 16.9% for the NO group, p=0.001). At two hours after aspiration, the mean interalveolar septal thickness in the NO group tended to be smaller as compared to that in the All group ($15.2{\mu}m$ for the ALI group vs $12.3{\mu}m$ for the NO group, p=0.06). S1P did not exert a significant effect on the pulmonary microstructure of the injured rat lung. Conclusion: Improved alveolar compliance and reduced interstitial edema, observed by intravital videomicroscopy, suggest that inhaled NO ameliorates lung injury.

• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.68 no.3
• /
• pp.167-174
• /
• 2023

This study investigated the microstructure and water absorption characteristics of the Korean adzuki bean (Vigna angularis L.) cultivar under accelerated storage. The germination rate, acid value, redness (a^*), and yellowness (b^*) values showed no significant differences after three months of storage compared to pre-storage under low temperatures (4℃). However, a statistically significant difference was observed under accelerated high temperatures (45℃). In particular, after storage for three months, the germination rate and acid value were 0% and 33.63 mg KOH/100g, respectively, under accelerated high temperatures. After storage for three months, the holes, hilum damage, and spaces between the seed coat and cotyledon shortened the time and speed of water absorption under accelerated high temperatures compared to that under low temperatures. Conversely, further research is required to investigate the reason for the low rate of parallel water absorption.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.7
• /
• pp.4835-4841
• /
• 2015

The effect of particle size and compaction pressure on the thermoelectric properties of n-type $FeSi_2$ was investigated. The starting powders with various particle size were pressed into a compact (compaction pressure; $70{\sim}220kg/cm^2$). The compact specimens were sintered at 1473 K for 7 h and annealed at 1103 K for 100 h under Ar atmosphere to transform to the semiconducting ${\beta}$-phase. The microstructure and phases of the specimens were observed by SEM, XRD and EDS. The electrical conductivity and Seebeck coefficient were measured simultaneously for the same specimen at r.t.~1023 K in Ar atmosphere. The electrical conductivity increased with decreasing particle size and hence the increases of relative density of the sintered body and the amount of residual metallic phase ${\varepsilon}$-FeSi due to a increase of the electrical conductivity. The Seebeck coefficient exhibited the maximum value at about 700~800 K and decreased with decreasing particle size. This must be due to a increase of residual metallic phase ${\varepsilon}$-FeSi. On the other hand, the change of compaction pressure appeared to have little effect on the thermoelectric properties. Consequently, the power factor would be affected more by particle size than compaction pressure.

• Journal of Powder Materials
• /
• v.13 no.5 s.58
• /
• pp.327-335
• /
• 2006

In the development of new hydrogen absorbing materials for a next generation of metal hydride electrodes for rechargeable batteries, metastable Mg-Ni-based compounds find currently special attention. Amor phous-nanocrystalline $Mg_{63}Ni_{30}Y_7$ and $Mg_{50}Ni_{30}Y_{20}$ alloys were produced by mechanical alloying and melt-spinning and characterized by means of XRD, TEM and DSC. On basis of mechanically alloyed Mg-Ni-Y powders, complex hydride electrodes were fabricated and their electrochemical behaviour in 6M KOH (pH=14,8) was investigated. The electrodes made from $Mg_{63}Ni_{30}Y_7$ powders, which were prepared under use of a SPEX shaker mill, with a major fraction of nanocrystalline phase reveal a higher electrochemical activity far hydrogen reduction and a higher maximum discharge capacity (247 mAh/g) than the electrodes from alloy powder with predominantly amorphous microstructure (216 mAh/g) obtained when using a Retsch planetary ball mill at low temperatures. Those discharge capacities are higher that those fur nanocrystalline $Mg_2Ni$ electrodes. However, the cyclic stability of those alloy powder electrodes was low. Therefore, fundamental stability studies were performed on $Mg_{63}Ni_{30}Y_7$ and $Mg_{50}Ni_{30}Y_{20}$ ribbon samples in the as-quenched state and after cathodic hydrogen charging by means of anodic and cathodic polarisation measurements. Gradual oxidation and dissolution of nickel governs the anodic behaviour before a passive state is attained. A stabilizing effect of higher fractions of yttrium in the alloy on the passivation was detected. During the cathodic hydrogen charging process the alloys exhibit a change in the surface state chemistry, i.e. an enrichment of nickel-species, causing preferential oxidation and dissolution during subsequent anodization. The effect of chemical pre-treatments in 1% HF and in $10\;mg/l\;YCl_3/1%\;H_2O_2$ solution on the surface degradation processes was investigated. A HF treatment can improve their anodic passivation behavior by inhibiting a preferential nickel oxidation-dissolution at low polarisation, whereas a $YCl_3/H_2O_2$ treatment has the opposite effect. Both pre-treatment methods lead to an enhancement of cathodically induced surface degradation processes.

• Journal of Conservation Science
• /
• v.25 no.4
• /
• pp.399-409
• /
• 2009

Outdoor iron artefacts are easily corroded by affection of environmental pollutants directly. Especially they need to be removed $Cl^-$ ions, but outdoor iron artefacts are excluded for desalination owing to their special features. Therefore this study contains the conservation processes of an iron stele of the Joseon Dynasty as the sample as well as desalination experiments that were carried out the desalting method using spill pads and the immersion desalting method together in order to compare. Desalting methods were compared by analyses such as an optical and metallurgical microscope, SEM-EDS, pH meter, Ion Chromatography and X-ray diffraction. As a result of the analysis, the optical and metallurgical microscopy show that the corrosion products are constituted by the layers and the metallurgical microstructure is a white cast iron. The SEM-EDS results of corrosion products detected mainly Fe, O, and especially Cl upto 2.48wt%. The results of pH and anion analysis for the washing solution, the desalting method using spill pads shows the similar effect to the immersion desalting method. As a result of XRD analysis before and after desalting corrosion products, goethite, magnetite, lepidocrocite and akaganeite are detected before desalting, but akaganeite is not detected after desalting at the desalting methode using spill pads, which indicates to have an effect on desalination. Therefore the results show that the desalting method using spill pads has an effect on desalination similar to the immersing desalting method.