• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2001.11a
• /
• pp.7-7
• /
• 2001

The increasing interest in light weight materials coupled to the need for cost -effective processing have combined to create a significant opportunity for aluminum P/M. particularly in the automotive industry in order to reduce fuel emissions and improve fuel economy at affordable prices. Additional potential markets for Al PIM parts include hand tools. Where moving parts against gravity represents a challenge; and office machinery, where reciprocating forces are important. Aluminum PIM adds light weight, high compressibility. low sintering temperatures. easy machinability and good corrosion resistance to all advantages of conventional iron bm;ed P/rv1. Current commercial alloys are pre-mixed of either the AI-Si-Mg or AL-Cu-Mg-Si type and contain 1.5% ethylene bis-stearamide as an internal lubricant. The powder is compacted in closed dies at pressure of 200-500Mpa and sintered in nitrogen at temperatures between $580~630^{\circ}C$ in continuous muffle furnace. For some applications no further processing is required. although most applications require one or more secondary operations such as sizing and finishing. These sccondary operations improve the dimension. properties or appearance of the finished part. Aluminum is often considered difficult to sinter because of the presence of a stable surface oxide film. Removal of the oxide in iron and copper based is usually achieved through the use of reducing atmospheres. such as hydrogen or dissociated ammonia. In aluminum. this occurs in the solid st,lte through the partial reduction of the aluminum by magncsium to form spinel. This exposcs the underlying metal and facilitates sintering. It has recently been shown that < 0.2% Mg is all that is required. It is noteworthy that most aluminum pre-mixes contain at least 0.5% Mg. The sintering of aluminum alloys can be further enhanced by selective microalloying. Just 100ppm pf tin chnnges the liquid phase sintering kinetics of the 2xxx alloys to produce a tensile strength of 375Mpa. an increilse of nearly 20% over the unmodified alloy. The ductility is unnffected. A similar but different effect occurs by the addition of 100 ppm of Pb to 7xxx alloys. The lend changes the wetting characteristics of the sintering liquid which serves to increase the tensile strength to 440 Mpa. a 40% increase over unmodified aIloys. Current research is predominantly aimed at the development of metal matrix composites. which have a high specific modulus. good wear resistance and a tailorable coefficient of thermal expnnsion. By controlling particle clustering and by engineering the ceramic/matrix interface in order to enhance sintering. very attractive properties can be achicved in the ns-sintered state. I\t an ils-sintered density ilpproaching 99%. these new experimental alloys hnve a modulus of 130 Gpa and an ultimate tensile strength of 212 Mpa in the T4 temper. In contest. unreinforcecl aluminum has a modulus of just 70 Gpa.

• Journal of the Korean Society for Heat Treatment
• /
• v.37 no.4
• /
• pp.163-171
• /
• 2024

SCR420H steel is a low-carbon chromium alloy steel designed for carburizing heat treatment. Recently, research is being conducted on high-temperature carburization heat treatment to reduce costs and CO₂ emissions by shortening the carburization time to meet the international carbon neutral policy. However, this high-temperature carburization heat treatment coarsens the steel grains and causes a decrease in mechanical properties. In this study, a large amount of Ti was added to increase the grain refinement effect in the high-temperature carburizing process. We investigated the microstructure and precipitates of SCR420H steel without Ti (Al steel) and with Ti (AlTi steel). Thermodynamic calculations showed that the AlN and (Ti,Nb)(C,N) precipitated in Al steel, while (Ti,Nb)(C,N) and Ti₄C₂S₂ precipitated in AlTi steel. Addition of Ti increases the fraction of bainite after reheating process. Transmission electron microscopy analysis shows that small amounts of AlN and (Ti,Nb)(C,N) precipitates are formed in the Al steel. The addition of Ti increases the density of (Ti,Nb)(C,N) precipitates and induces the formation of Ti₄C₂S₂ precipitates, increasing the grain coarsening temperature (GCT) under all heat treatment conditions. Higher reheating temperatures also resulted in higher GCT values due to increased precipitation.