• Korean Journal of Materials Research
• /
• v.22 no.5
• /
• pp.227-236
• /
• 2012

Ionomer is a thermoplastic that is composed of covalent bonds and ionic bonds. It is possible to use this material in processes such as injection molding or extrusion molding due to the material's high oil resistance, weatherproof characteristics, and shock resistance. In this study, a new ionomer having a multifunctional group was prepared by a stepwise neutralization system with the addition of acidic and salt additives. In step I, to increase the contents of the multifunctional group and the acid degree in ethylene acrylic acid (EAA), MGA was added to the ionomer resin (EAA). A new ionomer was prepared via the traditional preparation method of the ionic cross-linking process. In step II, metal salt was added to the mixture of EAA and MGA. The extrusion process was performed using a twin extruder (L/D = 40, size : ${\varphi}30$). Ionomer film was prepared for evaluation of gas permeability by using the compression molding process. The degree of neutralized and ionic cross-linked new ionomer was confirmed by FT-IR and XRD analysis. In order to estimate the neutralization of the new ionomer film, various properties such as gas permeation and mechanical properties were measured. The physical strength and anti-scratch property of the new ionomer were improved with increase of the neutralization degree. The gas barrier property of the new ionomer was improved through the introduction of an ionic site. Also, the ionic degree of cross-linking and gas barrier property of the ionomer membrane prepared by stepwise neutralization were increased.

• Membrane Journal
• /
• v.17 no.1
• /
• pp.54-60
• /
• 2007

In this research, the cation-exchange membrane (SS membrane) containing sulfonic acid group was prepared by radiation induced grafted polymerization onto a porous hollow fiber membrane to effectively remove ammonia which was produced by urea decomposition for peritoneum dialysis system. And the metal ionic cross-linking cation-exchange membrane (SS-M membrane) was prepared by the adsorption of metallic ions (Cu, Ni, Zn) to the SS membranes. The pure water flux and adsorption capacities of ammonia to SS and SS-M membranes were examined. The pure water flux of SS membrane decreased rapidly with the density of $SO_3H$ group increasing. As the metallic ions were adsorbed to the SS membrane, the pure water flux was increased. The adsorption capacities of ammonia at the SS membrane increased with increasing of density of $SO_3H$ group. The ion-exchange capacity of ammonia of the SS membrane was approximately proportional 1 : 1 to the density of $SO_3H$ group. The SS membrane had higher adsorption capacities than the SS-M membrane. The highest adsorption capacities of SS and SS-M membrane appeared the highest pH 9.

• Journal of the Korean Electrochemical Society
• /
• v.19 no.3
• /
• pp.101-106
• /
• 2016

In this study, we prepared an ionic liquid composite solid polymer electrolyte (PEO-LiTFSI-$Pyr_{14}TFSI$) with poly(ethylen oxide), lithium bis(trifluoromethanesulfonyl)imide, N-butyl-N-methylpyrrolidinium bis(trifluoromethanesulfonyl)imide by blending-cross linking process. Although the PEO-LiTFSI-$Pyr_{14}TFSI$ composite solid polymer electrolyte displayed a small peak at 4.4 V, it had high electrochemical oxidation stability up to 5.7 V. Ionic conductivity of the PEO-LiTFSI-$Pyr_{14}TFSI$ composite solid polymer electrolyte increased with increasing temperature from $10^{-6}S\;cm^{-1}$ at $30^{\circ}C$ to $10^{-4}S\;cm^{-1}$ at $70^{\circ}C$. To investigate the electrochemical properties, the PEO-LiTFSI-$Pyr_{14}TFSI$ composite solid polymer electrolyte assembled with $LiFePO_4$ cathode and Li-metal anode. At 0.1 C-rate, the cell delivered $40mAh\;g^{-1}$ for $30^{\circ}C$, $69.8mAh\;g^{-1}$ for $40^{\circ}C$ and $113mAh\;g^{-1}$ for $50^{\circ}C$, respectively. The PEO-LiTFSI-$Pyr_{14}TFSI$ solid polymer electrolyte exhibited good charge-discharge performance in Li/SPE/$LiFePO_4$ cells at $50^{\circ}C$.