• The Korean Journal of Ceramics
• /
• 제7권1호
• /
• pp.20-25
• /
• 2001

PbTiO$_3$ thin films were prepared by low-pressure thermal plasma deposition on (100)Pt/(100)MgO substrates. Mist of source material in which metal alkoxides are dissolved in 2-methoxyethanol was introduced into plasma through heating furnace and deposited onto substrates at $600^{\circ}C$. As-deposited PbTiO$_3$/Pt/MgO thin film prepared at 1.33$\times$10$^4$ Pa was grown epitaxially, but was consisted of many rectangular shaped grains, with many grain boundaries and it was impossible to measure electric properties. As-deposited film prepared at 1.00$\times$10$^4$ Pa showed weak peaks of X-ray diffraction and the film was not grown epitaxially. On the other hand, the film after annealed at $700^{\circ}C$ showed strong diffraction peaks and epitaxial growth was also observed. For annealed film, moreover, no clear grain boundaries were observed. The value of ${\varepsilon}_r$, tan${\delta}$, Pr and Ec of annealed film were 160, 3.2%, 10.4${\mu}$C.cm$^-2$ and 51.2kV.cm$^-1$, respectively. Since the composition, Pb/Ti, measured by EDS attaching to SEM changed point by point, the distribution of composition in annealed film was investigated and found out several relations between composition and electric properties. At stoichiometric composition, Pr and Ec showed the lowest value and they gradually became large as composition deviated from stoichiometric one. Moreover, the value of ${\varepsilon}_r$ became gradually large as the ratio of Ti became high.

• 한국재료학회지
• /
• 제5권1호
• /
• pp.55-62
• /
• 1995

알콕사이드를 원료로 하고 용매로는 에탄올과 증류수를 사용하여 cordierite 분말을 제조하였다. 촉매로는 HCl을 사용하였다. 촉매의 양은 HCl/TEOS 몰비를 0.1, 0.3, 0.5mol/mol비로 각각 반응시켜 촉매의 양에 따른 합성된 분말의 특성을 조사하였다. 0.1 mol/mol비로 제조된 분말의 $\alpha$-cordierite의 결정화 온도가 $1050^{\circ}C$인 반면 0.3 및 0.5mol/mol비로 제조된 분말의 $\alpha$-cordierite 결정화 온도는 $950^{\circ}C$였다. 또한 0.1mol/mol비로 제조된 분말의 경우에서는 $MgAl_{2}O_{4}$상이 $1300^{\circ}C$까지 존재하였다. 그러나 0.3 및 0.5mol/mol비로 제조된 분말의 경우에서는 $1300^{\circ}C$에서 $\alpha$-cordierite상만이 존재하였다.

• 한국재료학회지
• /
• 제17권3호
• /
• pp.147-151
• /
• 2007

Cu-free multi-component sol, of which final oxide composition becomes $Bi_{1.9}Pb{0.35}SrCaO,\;Bi_{1.8}Pb_{0.2}SrCaO\;and\;Bi_{1.5}SrCaO$, respectively, was prepared through sol-gel route and coated on a bare Cu substrate. Starting materials were metal-alkoxides as follows.; [$Bi(OC_{2}H_{5})_{3}\;Pb(O^{1}C_{3}H_{7})_{2},\;Sr(O^{i}C_{3}H_{7})_{2},\;Ca(OC_{2}H_{5})_{2}$] as a reagent grade. Transparent light yellowish sol was obtained in the case of $Bi_{1.9}Pb_{0.35}SrCaO\;and\;Bi_{1.8}Pb_{0.2}SrCaO$ composition and $Bi_{1.5}SrCaO$ composition's sol was light greenish. Each sol was repeatedly dip-coated on Cu substrate four times and pre-heated at $400^{\circ}C$ and finally heat-treated in the range of $740{\sim}900^{\circ}C$. In the results, crystalline phases confirmed by XRD were (2201) orthorhombic and monoclinic phases. However, only $Bi_{1.9}Pb_{0.35}SrCaO_{x}$ composition showed pseudo-superconductive behavior after heat-treatment at $900^{\circ}C$ for 12 seconds and then onset temperature was 77 K, even though it did not exhibit zero resistance below Tc.