• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.368-368
• /
• 2007

Zinc oxide (ZnO) has drawn much interest as a potential transparent conducting oxide (TCO) for applying to solar cell and front electrode of electro-luminescent devices. For the enhancement of electrical property of TCOs, dopant introduction and hybridization with conductive nanoparticles have been investigated. In this work, ZnO films were formed on glass substrate by using photochemical solution deposition of Ag nanoparticles dispersed or various metal (Ag, Cd, In, or Sn) contained photosensitive ZnO solutions. The usage of photosensitive solution permits us to obtain a micron-sized direct patterning of ZnO film without using conventional dry etching procedure. The structural, optical, and electrical characteristics of ZnO films with the introduction of metal dopants with/without Ag nanoparticles have been investigated to check whether there is a combined effect between metal dopants and Ag nanoparticles on the characteristics of ZnO film. The phase formation and crystallinity of ZnO film were monitored with X-ray diffractometer. The optical transmittance measurement was carried out using UV-VIS-NIR spectrometer and the electrical properties such as sheet resistance and conductivity were observed by using four-point probe.

• 한국세라믹학회지
• /
• 제39권3호
• /
• pp.240-244
• /
• 2002

$Gd_2O_3,\;CeO_2$ 및 $NH_4Br$ 분말을 사용하여 GdOBr:Ce 형광체를 고상 반응으로 합성하였다. GdOBr:Ce 형광체는 370nm UV 여기 하에 410∼430nm의 영역에서 청색 발광스펙트럼을 보였으며, 2mol%의 Ce 농도에서 최대 발광특성을 나타냈다. FED용 형광체로의 응용 가능성을 알아보기 위해 GdOBr:Ce 형광체의 음극서 발광(CL)을 측정하였다. CL의 경우 PL과 동일한 영역인 410∼430nm에서 발광을 나타냈으며, Ce 농도가 1mol%일 때 발광의 최대치를 보였다. CL에서의 degradation 효과를 보기 위해 전자선을 10분간 조사하여 상용형광체와 비교하였다. 이로부터 GdOBr:Ce 형광체를 FED용 청색 형광체로 응용할 수 있는 가능성을 확인하였다.

• Journal of Radiation Protection and Research
• /
• 제41권2호
• /
• pp.179-183
• /
• 2016

Background: As an important detecting device, TLD is a widely used in the radiation monitoring. It is essential for us to study the property of detecting element. The aim of this study is to calculate the thermo-luminescence efficiency of TL elements. Materials and Methods: A batch of thermo-luminescence elements were irradiated by the filtered X-ray beams of average energies in the range 40-200 kVp, 662 keV $^{137}Cs$ gamma rays and then the amounts of lights were measured by the TL reader. The deposition energies in elements were calculated by theory formula and Monte Carlo simulation. The unit absorbed dose in elements by photons with different energies corresponding to the amounts of lights was calculated, which is called the thermo luminescent efficiency (${\eta}^{(E)}$). Because of the amounts of lights can be calculated by the absorbed dose in elements multiply ${\eta}^{(E)}$, the ${\eta}^{(E)}$ can be calculated by the experimental data (the amounts of lights) divided by absorbed dose. Results and Discussion: The deviation of simulation results compared with theoretical calculation results were less than 5%, so the absorbed dose in elements was calculated by simulation results in here. The change range of ${\eta}^{(E)}$ value, relative to 662 keV $^{137}Cs$ gamma rays, is about 30% in the energy range of 33 keV to 662 keV, is in accordance by the comparison with relevant foreign literatures. Conclusion: The ${\eta}^{(E)}$ values can be used for updating the amounts of lights that are got by the direct ratio assumed relations with deposition energy in TL elements, which can largely reduce the error of calculation results of the amounts of lights. These data can be used for the design of individual dosimeter which used TLD-2000 thermo-luminescence elements, also have a certain reference value for manufacturer to improve the energy-response performance of TL elements by formulation adjustment.

• 한국분말재료학회지
• /
• 제25권1호
• /
• pp.12-18
• /
• 2018

Cost-effective functional phosphor nanoparticles are prepared by introducing low-cost $SiO_2$ spheres to rare-earth phosphor ($YVO_4:Eu^{3+}$, $YVO_4:Er^{3+}$, and $YVO_4:Nd^{3+}$) shells using a sol-gel synthetic method. These functional nanoparticles are characterized by X-ray diffraction, X-ray photoelectron spectroscopy, transmission electron microscopy, and general photoluminescence spectra. The $SiO_2$ sphere occupying the interior of the conventional phosphor is advantageous in significantly reducing the cost of expensive rare-earth phosphor nanoparticles. The sol-gel process facilitates the core-shell structure formation; the rare-earth shell phosphor has strong interactions with chelating agents on the surfaces of $SiO_2$ nanoparticles and thus forms layers of several nanometers in thickness. The photoluminescence wavelength is simply tuned by replacing the active materials of $Eu^{3+}$, $Er^{3+}$, and $Nd^{3+}$. Moreover, the photoluminescent properties of the core-shell nanoparticles can be optimized by manipulating the specific contents of active materials in the phosphors. Our simple approach substitutes low-cost $SiO_2$ for expensive rare-earth-based phosphor materials to realize cost-effective phosphor nanoparticles for various applications.

• 한국재료학회지
• /
• 제21권12호
• /
• pp.644-649
• /
• 2011

[ $A_{3-2x/3}Al_{1-z}In_{z}O_4F:Eu_x^{3+}$ ](A = Ca, Sr, Ba, x = -0.15, z = 0, 0.1) oxyfluoride phosphors were simply prepared by the solid-state method at $1050^{\circ}C$ in air. The phosphors had the bright red photoluminescence (PL) spectra of an $A_{3-2x/3}Al_{1-z}In_{z}O_4F$ for $Eu^{3+}$ activator. X-ray diffraction (XRD) patterns of the obtained red phosphors were exhibited for indexing peak positions and calculating unit-cell parameters. Dynamic excitation and emission spectra of $Eu^{3+}$ activated red oxyfluoride phosphors were clearly monitored. Red and blue shifts gradually occurred in the emission spectra of $Eu^{3+}$ activated $A_3AlO_4F$ oxyfluoride phosphors when $Sr^{2+}$ by $Ca^{2+}$ and $Ba^{2+}$ ions were substituted, respectively. The concentration quenching as a function of $Eu^{3+}$ contents in $A_{3-2x/3}AlO_4F:Eu^{3+}$ (A = Ca, Sr, Ba) was measured. The interesting behaviors of defect-induced $A_{3-2x/3}Al_{1-z}In_{z}O_{4-{\alpha}}F_{1-{\delta}}$ phosphors with $Eu^{3+}$ activator are discussed based on PL spectra and CIE coordinates. Substituting $In^{3+}$ into the $Al^{3+}$ position in the $A_{3-2x/3}AlO_4F:Eu^{3+}$ oxyfluorides resulted in the relative intensity of the red emitted phosphors noticeably increasing by seven times.

• 한국결정성장학회지
• /
• 제25권6호
• /
• pp.272-279
• /
• 2015

$Y_2O_3:Eu^{3+}$는 우수한 적색 발광 특성을 가지고 있는 형광체로 최근 고화질 디스플레이에 대한 수요가 증가함에 따라 관련 연구가 활발히 진행되고 있다. 본 연구에서는 RF 열플라즈마 합성법과 고상법을 이용하여 $Y_2O_3:Eu^{3+}$ 적색 형광체를 합성하였으며, 합성 방법에 따른 $Y_2O_3:Eu^{3+}$ 적색 형광체의 결정 구조, 미세 구조, 발광 특성의 차이를 XRD, TEM, PL 분석을 통해 비교하였다. 고상법으로 합성된 $Y_2O_3:Eu^{3+}$ 적색 형광체의 입자는 약 $10{\sim}20{\mu}m$ 크기를 가지는 반면, RF 열플라즈마 합성법을 통해 합성된 적색 형광체는 반응부는 약 100 nm, 필터부는 약 30 nm의 크기를 갖는 나노 형광체로 확인되었다. 합성된 모든 분말들은 PL 측정결과 611 nm($^5D_0{\rightarrow}^7F_2$)에서 발광하는 것을 확인하였으며, 결정 크기와 입도가 증가할수록 PL intensity가 증가하였다. 또한, 추가 열처리 공정이 필요 없는 one-step 공정의 RF 열플라즈마 공정을 통해 합성된 $Y_2O_3:Eu^{3+}$ 적색 나노 형광체는 고상법으로 합성된 적색 형광체와 비슷한 발광 특성을 보이는 것을 확인할 수 있었다.

• 한국방사선학회논문지
• /
• 제3권4호
• /
• pp.35-38
• /
• 2009

최근 의료영상분야에서 형광체와 광도전체 물질을 이용한 디지털 평판형 X선 영상검출기가 폭넓게 이용되고 있다. 본 연구는 CsI:Na 형광체층과 광민감도가 우수한 비정질 셀레늄(a-Se)층의 이중 접합구조로 구성된 변환구조 설계를 위한 몬테카를로 시뮬레이션과 X선에 대한 광학적 및 전기적 반응특성을 조사하였다. 먼저 CsI:Na의 발광스펙트럼과 a-Se의 광흡수 스펙트럼을 측정하여 X선에 의한 신호 변환특성을 분석하였다. 또한, 인가전기장의 함수에 따른 X선 민감도을 측정하여 상용화된 a-Se($500{\mu}m$)의 직접변환 검출기와 비교 평가하였다. 측정결과로부터, $10V/{\mu}m$에서 CsI:Na($180{\mu}m$)/a-Se($30{\mu}m$) 변환센서의 X선 민감도는 $7.31nC/mR-cm^2$ 이고, a-Se($500{\mu}m$) 검출기는 $3.95nC/mR-cm^2$로 약 2배 정도 높은 값을 보였다.

• Korean Chemical Engineering Research
• /
• 제44권3호
• /
• pp.284-288
• /
• 2006

분무열분해법을 이용하여$(Ca,Sr)_{2-y}MgSi_2O_7:Eu^{2+}{_y}$ 형광체 분말을 제조하고 $Eu^{2+}$의 농도, 후열처리온도 변화 및 Ca/Sr 비에 따른 발광특성을 조사하였다. 또한, Ca/Sr의 비를 변화시켜 발광특성의 변화를 관찰하였다. $Ca_2MgSi_2O_7$나 $Sr_2MgSi_2O_7$ 분말 모두 $1,000^{\circ}C$ 이상의 온도에서 열처리를 했을 때 순수한 정방정계 상이 제조되었다. $Ca_2MgSi_2O_7:Eu^{2+}{_y}$ 녹색 형광체는 $Eu^{2+}(y)$의 농도가 5 mol％, 후열처리 온도가 $1,250^{\circ}C$ 일 때 가장 높은 발광 강도는 보였다. ${(Ca_{1-x},Sr_x)}_{1.95}MgSi_2O_7:{Eu^{2+}}_{0.05}$의 발광 파장은 Sr의 농도가 증가함에 따른 결정장 감소로 인해 524nm에서 456nm로 점진적으로 blue shift 되었다. $Sr_2MgSi_2O_7:Eu^{2+}$는 Sr 자리에 약 10 mol％ Ca를 치환시킴으로써 청색 형광체의 발광 강도는 크게 향상되었다. 제조된 분말들은 치밀하지 못하고 다공성 구조를 가져 후열처리 전에는 구형을 유지하였으나 열처리($900{\sim}1,300^{\circ}C$) 후에는 구형의 형상을 잃고 입자들 간의 응집이 발생하였다.