• 한국태양에너지학회:학술대회논문집
• /
• 2009.04a
• /
• pp.235-240
• /
• 2009

Crystlline silicon solar cells markets are increasing at rapid pace. now, crystlline silicon solar cells markets screen-printing solar cell is occupying. screen-printing solar cells manufacturing process are very quick, there is a strong point which is a low cost. but silicon and metal contact, uses Ag & Al pates. because of, high contact resistance, high series resistance and sintering inside process the electric conductivity decreases with 1/3. and In pastes ingredients uses Ag where $80{\sim}90%$ is metal of high cost. because of low cost solar cells descriptions is difficult. therefore BCSC(Buried Contact Solar Cell) is developed. and uses light-induced plating, ln-line galvanization developed equipments. Ni/Cu matel contact solar cells researches. in Germany Fraunhofer ISE. In order to manufacture high-efficiency solar cells, metal selections are important. metal materials get in metal resistance does small, to be electric conductivity does highly. efficiency must raise an increase with rise of the curve factor where the contact resistance of the silicon substrate and is caused by few with decrement of series resistance. Ni metal materials the price is cheap, Ti comes similar resistance. Cu and Ag has the electric conductivity which is similar. and Cu price is cheap. In this paper, Ni/Cu/Ag metal contact cell with screen printing manufactured, silicon metal contact comparison and analysis.

• Current Photovoltaic Research
• /
• v.8 no.3
• /
• pp.94-101
• /
• 2020

This study was trying to focus on achieving high efficiency of multi junction solar cell with thin film silicon solar cells. The proposed thin film Si-Ge/c-Si tandem junction solar cell concept with a combination of low-cost thin-film silicon solar cell technology and high-efficiency c-Si cells in a monolithically stacked configuration. The tandem junction solar cells using amorphous silicon germanium (a-SiGe:H) as an absorption layer of upper sub-cell were simulated through ASA (Advanced Semiconductor Analysis) simulator for acquiring the optimum structure. Graded Ge composition - effect of E_g profiling and inserted buffer layer between absorption layer and doped layer showed the improved current density (J_sc) and conversion efficiency (η). 13.11% conversion efficiency of the tandem junction solar cell was observed, which is a result of showing the possibility of thin film Si-Ge/c-Si tandem junction solar cell.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.1125-1128
• /
• 2009

Conversion of light energy to electrical energy by using a solar cell has long been considered as one of the option for an electrical energy supply in the future. In the past, commercial use was restricted largely to remote area applications where conventional electricity is expensive. Recently, the major application of the solar cells changed to become generation of residential electricity in urban areas where the electricity is already supplied by the conventional grid. This paper covers the current market and technology status of the solar cells and future prospect of their terrestrial applications. Reviewing market trend, this paper discusses high efficiency approach in silicon solar cells, low cost approach in silicon solar cells and finally covers future prospects of silicon solar cells.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.438-438
• /
• 2009

We have investigated the effect of forming gas annealing for Upgraded Metallurgical Grade (UMG)-silicon solar cell in order to obtain low-cost high-efficiency cell using post deposition anneal at a relatively low temperature. We have observed that high concentration hydrogenation effectively passivated the defects and improved the minority carrier lifetime, series resistance and conversion efficiency. It can be attributed to significantly improved hydrogen-passivation in high concentration hydrogen process. This improvement can be explained by the enhanced passivation of silicon solar cell with antireflection layer due to hydrogen re-incorporation. The results of this experiment represent a promising guideline for improving the high-efficiency solar cells by introducing an easy and low cost process of post hydrogenation in optimized condition.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.1054-1056
• /
• 2002

High temperature Kermal diffusion from $POCl_3$ source usually used for conventional process through put of a cell manufacturing line and potentially reduce cell efficiency through bulk like time degradation. To fabricate high efficiency solar cells with minimal thermal processing, spin-on-doping(SOD) technique can be employed to emitter diffusion of a silicon solar cell. A technique is presented to emitter doping of a mono-crystalline solar cell using spin-on doping (SOD). Moreover it is shown that the sheet resistance variation with RTA temperature and time fer mono-crystalline and multi-crystalline silicon samples. This novel SOD technique was successfully used to produces 11.3% efficiency l04mm by 104mm size mono-crystalline silicon solar cells.

• New & Renewable Energy
• /
• v.1 no.1 s.1
• /
• pp.37-43
• /
• 2005

High-efficiency silicon solar cells have potential applications on mobile electronics and electrical vehicles. The fabrication processes of the high efficiency cells necessitate com placated fabrication precesses and expensive materials. Ti/Pd/Ag metal contact has been used only for limited area In spite of good stability and low contact resistance because of Its expensive material cost and precesses. Screen printed contact formed by Ag paste causes a low fill factor and a high shading loss of commercial solar cells because of high contact resistance and a low aspect ratio. Low cost Ni/Cu metal contact has been formed by using a low cost electroless and electroplating. Nickel silicide formation at the interface enhances stability and reduces the contact resistance resulting In an energy conversion efficiency of $20.2\%\;on\;0.50{\Omega}cm$ FZ wafer. Tapered contact structure has been applied to large area solar cells with $6.7\times6.7cm^2$ in order to reduce power losses by the front contact The tapered front metal contact Is easily formed by the electroplating technique producing $45cm^2$ solar cells with an efficiency of $21.4\%$ on $21.4\%\;on\;2{\Omega}cm$ FZ wafer.

• 한국태양에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.350-355
• /
• 2009

The crysralline silicon solar cell where the solar cell market grows rapidly is occupying of about 85% or more high efficiency and low cost endeavors many crystalline solar cells. The fabricaion process of high efficiency crystalline silicon solar cells necessitate complicated fabrication processes and Ti/Pd/AG contact, This metal contacts have only been used in limited areas in spite of their good srability and low contact resistance because of expensive materials and process. Commercial solar cells with screen-printed solar cells formed by using Ag paste suffer from loe fill factor and high contact resistance and low aspect ratio. Ni and Cu metal contacts have been formed by using electroless plating and light-induced electro plating techniques to replace the Ti/Pd/Ag and screen-printed Ag contacts. Copper and Silver can be plated by electro & light-induced plating method. Light-induced plating makes use the photovoltaic effect of solar cell to deposit the metal on the front contact. The cell is immersed into the electrolytic plating bath and irradiated at the front side by light source, which leads to a current density in the front side grid. Electroless plated Ni/ Electro&light-induced plated Cu/ Light-induced plated Ag contact solar cells result in an energy conversion efficiency of 16.446 % on 0.2~0.6${\Omega}$ cm, $20{\times}20mm^2$, CZ(Czochralski) wafer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.434-435
• /
• 2009

The crystalline silicon solar cell where the solar cell market grows rapidly is occupying of about 85% or more. high-efficiency and low cost endeavors many crystalline silicon solar cells. the fabrication processes of high-efficiency crystalline silicon solar cells necessitate complicated fabrication processes and Ti/Pd/Ag contact, however, this contact formation processed by expensive materials. Ni/Cu contact formation is good alternative. in this paper, according to temperature Ni silicide makes, produced Ni/Cu contact solar cell and measured conversion efficiency.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.223-224
• /
• 2008

Important element are low cost, high-efficiency crystalline silicon solar cells. in this paper, Will be able to contribute in low cost, high-efficiency silicon solar cells, Applies oxide/nitride passivation, produced screen-printed solar cells. and the Measures efficiency, and evaluated a justice quality oxide/nitride passivation screen-printed solar cells.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.06a
• /
• pp.250-253
• /
• 2007

An evaporated Ti/Pd/Ag contact system is most widely used to make high-efficiency silicon solar cells, however, the system is not cost effective due to expensive materials and vacuum techniques. Commercial solar cells with screen-printed contacts formed by using Ag paste suffer from a low fill factor and a high shading loss because of high contact resistance and low aspect ratio. Low-cost Ni and Cu metal contacts have been formed by using electroless plating and electroplating techniques to replace the Ti/Pd/Ag and screen-printed Ag contacts. Ni/Cu alloy is plated on a silicon substrate by electro-deposition of the alloy from an acetate electrolyte solution, and nickel-silicide formation at the interface between the silicon and the nickel enhances stability and reduces the contact resistance. It was, therefore, found that nickel-silicide was suitable for high-efficiency solar cell applications. The Ni contact was formed on the front grid pattern by electroless plating followed by anneal ing at $380{\sim}400^{\circ}C$ for $15{\sim}30$ min at $N_{2}$ gas to allow formation of a nickel-silicide in a tube furnace or a rapid thermal processing(RTP) chamber because nickel is transformed to NiSi at $380{\sim}400^{\circ}C$. The Ni plating solution is composed of a mixture of $NiCl_{2}$ as a main nickel source. Cu was electroplated on the Ni layer by using a light induced plating method. The Cu electroplating solution was made up of a commercially available acid sulfate bath and additives to reduce the stress of the copper layer. The Ni/Cu contact was found to be well suited for high-efficiency solar cells and was successfully formed by using electroless plating and electroplating, which are more cost effective than vacuum evaporation. In this paper, we investigated low-cost Ni/Cu contact formation by electroless and electroplating for crystalline silicon solar cells.