• 대한기계학회논문집
• /
• 제19권9호
• /
• pp.2105-2113
• /
• 1995

The compressive tests under impact conditions were performed to establish a design guide for impact damage tolerance. The composition of layup was selected for the real cases of composite aircraft structure. The energy level of visible of visible damage threshold was determined as 7 Joules. It was found that the normalized bending stiffnesses in the direction of closely fixed boundary affected the area of damage. Graphite/epoxy used in the tests exhibited 60% reduction in compression strength at the energy level of visible damage threshold. Wet-conditioned specimens represented 9% reduction in residual compressive strength in comparison with room temperature ambient specimens. In this study, a design factor of 2.1 was proposed for the low velocity impact damage.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1144-1145
• /
• 2006

In this paper, the fundamental attributes, phase composition of three pre-alloyed powders for diamond tools by water atomization were investigated. The density, hardness, bend strength and bending modulus of their hot pressing samples were examined. The results showed that the three pre-alloyed powders have excellent low temperature sintering characteristics. The physical and mechanical properties of the samples were found to be nearly the same as those of fine cobalt powders.

• 한국분말재료학회지
• /
• 제6권1호
• /
• pp.75-80
• /
• 1999

The formation of $n-TiO_2$ powder by oxidation of Ti-ethoxied vapor in a flat flame burner reactor maintained under 20 torr has been studied. The produced powder were characterized in terms of crystal structure, chemical composition by XRD and TEM. The results showed that the powder consisted of loose agglomerated anatase and rutile particles and their size were about 10 nm and 20 nm, respectively. In the course of synthesis, changes of the flame color were happened to each condition during heating up the bubbler. The flame color transition phenomena reveled that a critical precursor delivery rate was needed for the powder formation (obtainable powder yield). The critical precursor delivery rate was estimated by a simple function of the bubbler temperature and the carrier gas flow rate. The critical precursor delivery rate was reviewed as an important variable of the nanopowder synthesis.

• Corrosion Science and Technology
• /
• 제10권5호
• /
• pp.162-166
• /
• 2011

Effects of chemical compositions and manufacturing conditions on mechanical properties and microstructures were investigated in order to obtain galvannealed high strength dual phase steel sheets with superior mechanical properties and coating properties. An intercritical annealing between Ac1 and Ac3 was conducted to produce the DP (dual phase) steel sheets, followed by quenching to room temperature. The purposes of Al addition are to reduce the iron oxidation with chemical composition (Si, Mn etc.) and to improve the wettability by liquid zinc. The present study will focus on the characterization for making dual phase steel sheets and enhancing the galvanizability of Al added DP steel sheets about continuous annealing line in CGL.

• 한국세라믹학회지
• /
• 제37권1호
• /
• pp.12-20
• /
• 2000

Dielectric property of Ba-modified 0.65Pb(Mg1/3Nb2/3)O3-0.35PbTiO3 ceramics having compositions near the morphotropic phase boundary was investigated. For the specimens having Ba contents between 0 and 20 at%, the average transition temperature was decreased linearly with increasing Ba contents and the degree of hysteresis was also decreased with increasing Ba contents. The maximum dielectric constants (K), electric field induced polarization(P) and electrically-induced strain(S) were found to exihibit a maximum value at∼3 at% of Ba. The increase of S and the decrease of hysteresis by minor additions of Ba impurities indicated the development of new higher perfomance actuator materials. The composition of Ba-PMN-PT (10/65/35) may be appropriate for capacitor materials because of low hysteresis and high polarization.

• 한국세라믹학회지
• /
• 제37권8호
• /
• pp.774-780
• /
• 2000

In order to improve luminescence prperty of phosphors, we have synthesized Zn2SiO4:Mn phosphors by a new chemical synthetic route, i.e., the homogeneous precipitation method. This method has featured that the formation of phosphoris completed at relatively low temperature of 105$0^{\circ}C$ and the particle morphology exhibits spherical shape to be well-dispersed and uniform size. At all the Mn concentration explored, phosphors prepared by this method have exhibited the improved emission intensities. In particular, the emission intensities of phosphors with Mn doping contents between 1 at% and 3.5 at% were higher about 40% than that of commercial phosphor. On the other hand, the decay time has been decreased from 23 ms to 11 ms with increasing Mn concentration. In addition, the phosphor composition containing 3 at% Mn has displayed the most saturated color.

• The Korean Journal of Ceramics
• /
• 제2권2호
• /
• pp.76-82
• /
• 1996

PLZT ceramics having two nominal compositions, $Pb_{1-3x/2}La_xV_{x/2}(Zr_{03}Ti_{03})O_3$ and $Pb_{1-x}La_x(Zr_{0.2}Ti_{0.5})_{1-x/4}V_{x/4}O_3$ (V: vacancy) with x=0.00~0.30, were prepared. The physical, structural, and dielectric properties were investigated by X-ray diffraction, scanning electron microscopy, Raman spectroscopy, and measurements of bulk density and dielectric constant. The two series with A-stie and B-site vacancies showed different physical, structural, dielectric properties, and, specially, Curie temperature. In comparison to PLZT with B-site vacancies, PLZT with A-site vacancies showed high Curie temperatures and low maxima of dielectric constant. Consequently, it is evident that the properties of PLZT ceramics depend on the vacancy formula adopted as a batch composition in preparation.

• 한국세라믹학회지
• /
• 제29권2호
• /
• pp.143-151
• /
• 1992

Partially stabilized alpha-sialon composition (X=0.1) powder was hot-pressed at 1800~200$0^{\circ}C$ for 0~90 min with 30 MPa. Sintering behavior, phase changes and mechanical properties for the specimens were studied. As sintering temperature was raised from 1800 to 190$0^{\circ}C$, the relative density tended to increase and reached 99% of theoretical at 190$0^{\circ}C$. However the amount of alpha-sialon decreased because alpha-sialon transformed to beta-Si3N4 and yttrium rich silicate glass. In the case of hot-pressing at 190$0^{\circ}C$ for various times, densification increased with sintering time and full densification above 99% of theoretical was attained by 30 min. The amount of alpha-sialon decreased with sintering time. The maximum strength of 825 MPa was obtained by hot-pressing at 190$0^{\circ}C$ for 60 min.

• 한국세라믹학회지
• /
• 제35권10호
• /
• pp.1085-1093
• /
• 1998

Amorphous alumina powder prepared by the fast calcination of aluminum trihydroxide(Al(OH)3 gibbsite) for 0.5 second at 580$^{\circ}C$ was investigated rehydration propeties. Phase composition crystal size and mor-phology surface area pore volume and pore size distribution of pesudo-boehmite and bayerite crystals changed with temperature time water/alumina ratio and particle size when amorphous alumina rehydrated with water. Phase compositions were examined with XRD and DTA and crystal sized morphologies were investigaed with SEM and TEM. Also rehydration properties of amorphous alumina were in-vestigated by measuring the surface area pore volume and pore size distribution.

• 한국표면공학회지
• /
• 제29권5호
• /
• pp.424-429
• /
• 1996

Thin films of Ti-Ni alloy were formed by sputtering under various Ar gas pressures and r. f. powers to investigate the optimum sputtering conditions and to demonstrate their shape memory effect. The composition and structure of the films were examined by electron micro-probe analysis and scanning electron microscope. These films were annealed in order to crystallize them. The mechanical property of the annealed films was evaluated by a conventional bending test. The transformation tmeperatures were determined by differential scanning calorimetry. The shape memory behaviour was examined quantiatatively by changing in sample temperature under various constant loads. It was found that the Ar gas pressure had a critical effect on the mechanical property of the thin film,s although the r.f. power also affected it. The films formed at a high Ar gas pressure were too brittle to be bent successfully. However, the films formed at a low Ar gas pressur could be bent and their shape memory behavior was found to be comparable with that of bulk Ti-Ni alloys.