• 한국전기전자재료학회논문지
• /
• 제20권4호
• /
• pp.332-336
• /
• 2007

In this study, multilayer piezoelectric transformer was manufactured using the PMN-PNN-PZT ceramic and then the electrical characteristics were investigated according to the variations of frequency and load resistance. The voltage step-up ratio of multilayer piezoelectric transformer showed the maximum value at the vicinity of 75 kHz and increased according to the increase of load resistance. When the output impedance coincided with the load resistance, the multilayer piezoelectric transformer showed the temperature rise of less than $20^{\circ}C$ at the output power of 20 W. As the results, the multilayer piezoelectric transformer manufactured at low co-firing temperature of $940^{\circ}C$ using PMN-PNN-PZT ceramics could be stably driven as the step-down transformers.

• 한국세라믹학회지
• /
• 제34권3호
• /
• pp.289-295
• /
• 1997

저손실 Mn-Zn 페라이트의 제조공정과 첨가제가 코아의 미세구조와 전기적 특성에 미치는 영향을 조사하였다. C\ulcorner와 SiO2를 원료분체혼합시에 첨가하는 경우보다 하소분체의 재분쇄시에 첨가할 때가 작고 균일한 소결체를 얻을 수 있었다. 산소분압(Po2)이 높아짐에 따라 미세구조가 불균일해졌고 DF(disaccomodation fac-색)가 증가하였다. 또한 하소온도가 높고 분쇄시간이 짧은 소결체의 경우 치밀한 속도가 감소하여, 130$0^{\circ}C$까지 정상입성장거동을 보였고, 따라서 높은 소결온도에서도 비교적 저손실 Mn-Zn 페라이트를 얻을 수 있었다. 장시간 분쇄하거나 하소온도가 낮은 시편의 경우는 치밀화속도의 증가에 기인하여 120$0^{\circ}C$이하의 저온 소결시 미립자의 저손실 Mn-Zn 페라이트를 얻을 수 있었으나 소결온도 125$0^{\circ}C$이상에서는 비정상 입성장을 유발시켰다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2008년도 제39회 하계학술대회
• /
• pp.1250-1251
• /
• 2008

In this study, the dielectric ceramics with low loss were investigated for high frequency application. All sample of the $Ba_5M_4O_{15}$ (M=Ta, Nb) ceramics were prepared by the conventional mixed oxide method and sintered at $1325{\sim}1575^{\circ}C$. The bulk density and dielectric constant of the $Ba_5Ta_4O_{15}$ ceramics were increased continuously with increasing of sintering temperature. The quality factor was increased in the sintering temperature of $1375{\sim}1475^{\circ}C$ but decreased at the temperature above 1475$^{\circ}C$. In the case of $Ba_5Nb_4O_{15}$ ceramics, the bulk density, dielectric constant and quality factor were increased with sintering temperature but decreased above temperature of 1400$^{\circ}C$. The dielectric constant, quality factor and temperature coefficient of the resonant frequency (TCRF) of the $Ba_5Ta_4O_{15}$ and $Ba_5Nb_4O_{15}$ ceramics, sintered at 1475$^{\circ}C$ and 1400$^{\circ}C$, were 25.15, 53105 GHz, -3.06 ppm/$^{\circ}C$ and 39.55, 28052 GHz, 5.7 ppm/$^{\circ}C$, respectively.

• 한국전기전자재료학회논문지
• /
• 제25권4호
• /
• pp.282-285
• /
• 2012

It is well known that Zinc Oxide (ZnO) is an attractive material for its various applications. ZnO has been mostly used as a transparent conducting oxide in liquid crystal displays, solar cells due to its advantages of low cost, high productivity, and excellent electrical conductivity. Notably, flexible-dye-sensitized solar cells (DSSCs) based on polyethylene terephthalate (PET) substrates require low temperature sintering processing conditions. Therefore, low temperature processing conditions have been strongly required for transparent conducting film applications. In this paper, we prepared low temperature-sintered ZnO ceramics employing Li as a sintering aid.

• 한국전기전자재료학회논문지
• /
• 제29권10호
• /
• pp.608-612
• /
• 2016

In this study, in order to develop relaxor ferroelectric ceramics for refrigeration device application with large electrocaloric effect and low sintering temperature, PLZT(8/65/35) ceramics was fabricated using conventional solid-state method with the variation of sintering temperature ($1,050^{\circ}C$, $1,100^{\circ}C$, $1,200^{\circ}C$). The XRD pattern of all specimens indicated general perovskite structure with secondary phase. From the results of temperature dependence of dielectric constant, the $T_C$ (ferroelectric-paraelectric phase transition temperature) was shifted toward high temperature with increasing sintering temperature. When the specimen was sintered at $1,100^{\circ}C$, the optimal value of ${\Delta}T{\sim}0.349^{\circ}C$ in ambient temperature of $215^{\circ}C$ was appeared. It is considered that PLZT(8/65/35) ceramics possess the possibility of refrigeration device application.

• 한국세라믹학회지
• /
• 제56권1호
• /
• pp.104-110
• /
• 2019

The low-temperature sintering behavior of AlN was investigated through a conventional method. $CaF_2$, CuO and Cu were selected as additives based on their low melting points. When sintered at $1600^{\circ}C$ for 8 h in $N_2$ atmosphere, a sample density > 98% was obtained. The X-ray data indicated that eutectic reactions below $1200^{\circ}C$ were found. Therefore, the current systems have lower liquid formation temperatures than other systems. The liquid phase showed high dihedral angles at triple grain junctions, indicating that the liquid had poor wettability on the grain surfaces. Eventually, the liquid was likely to vaporize due to the unfavorable wetting condition. As a result, a microstructure with clean grain boundaries was obtained, resulting in higher contiguity between grains. From EDS analysis, oxygen impurity seems to be well removed in AlN lattice. Therefore, it is believed that the current systems are beneficial for reducing sintering temperature and improving oxygen removal.

• 대한건축학회논문집:구조계
• /
• 제35권12호
• /
• pp.149-156
• /
• 2019

Recently, skyscraper building and apartment fires, which were rapidly spread out from a low floor to a rooftop, have become a frequent occurrence in mass media. This fire problems have a fatal disadvantage that the exterior wall finish of the building emits toxic gas in case of fire by using dry bit method or organic insulating material. Therefore, in order to remedy these problems, many exterior wall finishing construction methods have been proposed, but the current trend is to use existing construction methods due to problems such as economy, weight, and durability. On the other hand, in countries such as Germany and Japan, ceramic sidings are used as exterior finishing material for buildings, which is environmentally friendly, excellent natural beauty, long life, easy maintenance and high-quality exterior materials. However, those ceramic sidings have still the problems such as manufacturing cost and weight problem because of boosting the sintering temperature up to 1,350℃ or more. Also, conventional CRC, MgO, FRP sidings which are composed of pulp, glass fiber and organic materials, have been reports of deformation due to ultraviolet rays, discoloration, corrosion and scattering, surface rupture, lifting and peeling. Therefore, in this study as an alternative to solve this problem, halosite nano kaolin produced in Sancheong in Korea and frit flux were used to satisfy the required properties as ceramic siding using low temperature sintering (below 1,000℃) and lightweight materials such as pearlite. This study aims to design the optimal formulation and process of materials and to study the characteristics of nano-coated ceramic siding material development and to present relevant basic data. The findings show that ceramic siding for nanocoated building materials is excellent as a natural ceramic siding building material. The fire resistance of natural minerals and nano particle refining technology satisfy the bending strength of 80kgf / cm2, the volume ratio of 2.0 and the absorption rate of less than 10.0%.

• 한국세라믹학회지
• /
• 제25권1호
• /
• pp.54-58
• /
• 1988

In order to depress PbO vaporization during calcination and improve sinterability in low temperature, a method for preparing homogeous Lead-Zirconate-Titanate (PZT) powder from aqueous salt solution by precipitation is described. In this method, single phae PZT fine powders are formed at above 500$^{\circ}C$. PZT-ceramics using these powders have high sinterability, and good sintering characteristics relatively low temp. (-high apparent density, low porosity, low water adsorption etc.)

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2004년도 Asia Display / IMID 04
• /
• pp.1099-1102
• /
• 2004

For the development of Pb-free low temperature sintering glass frits, $BaO-B_2O_3-SiO_2$ system was examined. The content of BaO and $B_2O_3$ was changed when the content of $SiO_2$ was fixed to 10 mol%. When the content of BaO was more than 60 mol% devitrification was observed. In the sintering temperature range between 520${\sim}$620 $^{\circ}C$, the optimum sintering temperature decreased as the content of BaO increased. When BaO ${\geq}$45 mol%, the glasses were crystallized after sintering. Candidate compositions are suggested in $BaO-B_2O_3-SiO_2$ system, which can replace the PbO containing glass system.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.645-648
• /
• 1999

With the variation of the sintering temperature and the amounts of B$_2$O$_3$, Bi$_3$O$_3$ and V$_2$O$_{5}$ , the densification and the piezoelectric properties of the MnO$_2$-doped PMN-PZT were investigated. The additives decreased the sintering temperature of ceramics. In the case of 0.5wt% B$_2$O$_3$, the sintering density, the mechanical quality factor, the electromechanical coupling factor and the piezoelectric constant were 7.51 (g/㎤), 1397, 51.1% and 305 (X10$^{-12}$ C/N) respectivly at 105$0^{\circ}C$. And the addition of lwt% Bi$_2$O$_3$, they were 7.59 (g/㎤) ,833,49.8% and 308 (X10$^{-12}$ C/N) respectivly at 1000 $^{\circ}C$.