For the development of multi-functional materials which has water reducing power, air entraining power and waterproofing power as well as a blending additive in cement mortar the low grade fly ash was modified with asphalt-stearic acid or asphalt-boiled o

• Journal of the Korea Institute of Building Construction
• /
• v.1 no.2
• /
• pp.179-184
• /
• 2001

The most recent building trend is going large, high rise, high strength as overlarge project is developing in domestic construction business. Belite cement has properties like low heat, excellent long term strength, and durability without admixture(fly ash, silica fume). so, Beilte cement is suitable for mass structure which is needed high strength, high fluidity and low heat property. This study is to examine the possibility if site adoption microwave-use early strength estimation method. Based on the existed study related the portland cement, the interrelation between Belite cement and microwave-use early strength estimation method is required. In this study, interrelation between mortar and Evaluating strength estimation method is investigated before the concrete experiment.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.1077-1082
• /
• 2001

The most recent building trend is going large, high rise, high strength as overlarge project is developing in domestic construction business. Belite cement has properties like low heat, excellent long term strength, and durability without admixture(fly ash, silica fume). so, Belite cement is suitable for mass structure which is needed high strength, high fluidity and low heat property. This study is to examine the possibility of site adoption microwave-use early strength estimation method. Based on the existed study related the portland cement, the interrelation between Belite cement and microwave-use early strength estimation method is required. In this study, interrelation between mortar and Evaluating strength estimation method is investigated before the concrete experiment.

• Korean Journal of Agricultural Science
• /
• v.8 no.2
• /
• pp.185-194
• /
• 1981

This study was carried out to determine the effect of accelerated curing on the strength of standard sand mortar and briquette ash mortar. The standard sand mortars and the briquette ash mortars made by mixture of the standard sand:cement and the briquette ash:cement at the ratio of 2 : 1, 3: 1 and 4 : 1, respectively, were cured at 4 different temperature of $20^{\circ}C$, $60^{\circ}C$, $80^{\circ}C$ and $100^{\circ}C$. The compression and tensil strength of mortars were measured at ${\sigma}_3$, ${\sigma}_7$, ${\sigma}_28$. The results obtained are summarized as follows; 1. At each age of curing and each curing temperature, the compression and tensile strength of the mortars made by the mixture of cement and standard sand was significantly higher than that of the mortars made by the mixture of cement and briquette ash. But the increasing rate of strength in compression and tension was significantly higher at the mortars of cement and briquette ash than those of cement and standard sand. 2. The strength of mortars which showed lower strength than Korean Standard at ordinary curing temperature was significantly increased and showed higher value than Korean Standard by the accelerated curing at high temperature. The increasing rate of strength by the accelerated curing was higher at the mortars containing less amount of cement than those containing more cement. The hardening of the mortars containing less amount of cement was significantly promoted by the accelerated curing in high temperature. 3. When the briquette ash was substituted for the materials of cement mortar, decline of the mortar strength is. unavoidable. But the enhancement of the mortar strength is still expected by the experimental results that the strength of cement-briquette ash mortar showed an increase of 137.6% by the accelerated curing at $60^{\circ}C$, 164.1% at $80^{\circ}C$ C and 183.8% at $100^{\circ}C$, respectively, compared with the strength of mortar cured at $20^{\circ}C$ for 28 days. 4. As the strength of cement briquette mortar is lower than that of cement standard sand mortar, the cement briquette ash mortar is expected to be increased in strength by the accelerated curing at high temperature. The cement briquette mortar is expected to be utilized to the production of secondary mortar goods or the constructions which need low strength of mortar.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.27 no.1
• /
• pp.46-61
• /
• 1985

This study was performed to obtain the basic data which can be applied to the use of foaming mortars. The data was based on the properties of foaming mortars depending upon various mixing ratios and addings to compare those of cement mortar. The foaming agents which was used at this experiment were pre-foamed type and mix-foaming type which is being used as mortar structures. The foaming mortar, mixing ratios of cement to fine aggregate were 1:1, 1: 2, 1 : 3 and 1 : 4. The addings of foaming agents were 0.0%, 0.5%, 1.0%, 1.5%, 2.0%, 2.5% and 3.0% of cement weight. The results obtained were summarized as follows; 1. At the mixing ratio of 1 : 1, the lowest water-cement ratios were showed by foaming mortars, respectively. But it gradually was increased in poorer mixing ratio and decreased in more addition of foaming agent. The water-cement ratios were decreased up to 1. 8~22. 0% by G, 2. 2~24. 1 % by U and 0. 7~53. 1% by J foaming mortar than cement mortar. 2, At the mixing ratio of 1 : 1, the highest bulk densities were showed by foaming mortars, respectively. But, it gradually was decreased in poorer mixing ratio and more addition of foaming agent. The bulk densities were decreased up to 1. 4~20. 7% by G, 2. 3~23. 7% by U and 26. 5~56. 5% by J foaming mortar than cement mortar. Therefore, foaming mortar could be utilized to the constructions which need low strengths. 3. At the mixing ratio of 1:1, the lowest absorption rates were showed by foaming mortars, respectively. But, it gradually was increased in poorer mixing ratio and more addition of foaming agent. Specially, according to the absorption rate when immersed in 72 hours, the absorption rates were showed up to 1. 01~1. 24 times by G, 1. 03~1. 58 times by U and 1. 10~5. 91 times by J foaming mortar than cement mortar. It was significantly higher at the early stage of immersed time than cement mortar. 4. At the mixing ratio of 1:1, the lowest air contents were showed by foaming mortars, respectively. But, it gradually was increased in poorer mixing ratio and more addition of foaming agent. Air contents were contented up to 4. 0~17. 2 times by G, 5. 2~23. 2 times by U and 23. 8~74. 5 times by J foaming mortar than cement mortar. 5. At the mixing ratio of 1 : 1, the lowest decreasing rates of strengths were showed by foaming mortars, respectively. But, it gradually was increased in poorer mixing ratio and more addition of foaming agent. Specially, the strengths of 28 days were decreased 0. 4~2. 2% than those of 7 days by foaming mortar, respectively. Also, the correlations between compressive and tensile strength, compressive and ending strength, tensile and bending strength were highly significant as a straight line shaped, respectively. 6. The correlations between absorption rate, air content, compressive strength and bulk density, absorption rate, compressive strength and air content were highly significant, respectively. The multiple regression equations of water-cement ratio, bulk density, absorption ate, air content, compressive strength, tensile strength and bending strength were computed depending on a function of mixing ratio and addition of foaming agent. It was highly significant, respectively. 7. At the mixing ratio of 1 : 1, the highest strengths were showed by cement mortar and foaming mortars, by chemical reagents. But, it gradually was decreased in poorer mixing ratio. The decreasing rates of strengths were in order of H $_2$S0 $_4$, HNO$_3$ and HCI, J,U,G foaming mortar and cement mortar. Specially, at the each mixing ratio, each chemical reagent and 3.0% of foaming agent, J foaming mortar was collapsed obviously. Therefore, for the structures requiring acid resistence, adding of foaming agent should be lower than 3.0%.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.3
• /
• pp.247-252
• /
• 2017

The aim of this research is the feasibility analysis of the reject ash premixed cement mortar with combined aggregate. Namely, for the combined aggregate with two different qualities of aggregates, a fundamental properties of cement mortar was evaluated depending on various replacing ratios of reject ash(Ri). According to the experimental results, the combined aggregate consisted with low-quality aggregate and sea sand did not change the flow value depending on the reject ash while the combined aggregates consisted with low quality aggregate and sea sand; and consisted exploded debris sand and sea sand the increasing reject ash increased the air content with increased replacing ratio of reject ash. In the case of compressive strength, as the replacing ratio of reject ash was increased, the compressive strength was increased. It is considered that when 5% of reject ash replacing ratio made similar quality of cement mortar with favorable quality aggregate, hence, it can be suggested that 5% replacement of reject ash for desirable fluidity and compressive strength of concrete.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.40 no.5
• /
• pp.52-58
• /
• 1998

The objective of this study was to develop a polymer mortar protection block with high strength and durability using unsaturated polyester resin to complement defects of conventional cement mortar protection block. Physical and mechanical properties of the polymer mortar protection block were also investigated. Low absorptivity, high impact strength, and great bending strength of the polymer mortar protection block was compared with those of the conventional cement protection block. In conclusion, the polymer mortar protection block is excellent and useful as industrial products for erosion control works.

• Advances in concrete construction
• /
• v.13 no.4
• /
• pp.315-325
• /
• 2022

Reinforced concrete structures are exposed throughout their lifetime to the phenomenon of carbonation, which considerably influences their durability by causing corrosion of the reinforcements. The fight against this phenomenon is usually ensured by anti-carbonation coatings which have the possibility of limiting the permeability to carbon dioxide or with coatings which absorb the CO₂ present in the air. A coating with good crack-bridging (sealing) capacity will prevent water from entering through existing cracks in concrete. Despite the beneficial effect of these coatings, their durability decreases considerably over time with temperature and humidity. In order to use coatings made from local materials, not presenting any danger, available in abundance in our country, very economical and easy to operate is the main objective of this work. This paper aim is to contribute to the formulation of a corrected dune sand-based mortar as an anti-carbonation coating for concrete. The results obtained show that the cement mortar based on dune sand formulated has a very satisfactory compressive strength, a very low water porosity compared to ordinary cement mortar and that this mortar allows an improvement in the protection of the concrete against the carbonation of 60% compared to ordinary cement mortar based on alluvial sand. Moreover, the formulated cement mortars based on dune sand have good adhesion to the concrete support, their adhesion strengths are greater than 1.5MPa recommended by the standards.

• Advances in concrete construction
• /
• v.11 no.5
• /
• pp.419-428
• /
• 2021

The pH of cement-based materials (CBMs) is an important factor for their durability, sustainability, and long service life. Currently, the use of supplementary cementitious materials (SCMs) is becoming mandatory due to economic, environmental, and sustainable issues. There is a decreasing trend in pH of CBMs due to incorporation of SCMs. The determination of numerical values of pH is very important for various low and high volume SCMs blended cement mortars for the better understanding of different defects and durability issues during their service life. In addition, the effect of cement hydration and pozzolanic reaction of SCMs on the pH should be determined at initial and later ages. In this study, the effect of low and high-volume fly ash (FA) and ground granulated ballast furnace slag (GGBFS) cement mortars in different curing conditions on their pH values has been determined. Thermal gravimetric analysis (TGA) was carried out to support the findings from pH measurements. In addition, thermal conductivity (k-value) and strength activity indices of these cement mortars were discussed. The results showed that pH values of all blended cement mortars were less than ordinary Portland cement (OPC) mortar in all curing conditions used. There was a decreasing tendency in pH of all mortars with passage of time. In addition, the pH of cement mortars was not only dependent on the quantity of Ca(OH)₂. The effect of adding SCMs on the pH value of cement mortar should be monitored and measured for both short and long terms.

• Journal of the Korean Ceramic Society
• /
• v.43 no.9 s.292
• /
• pp.537-543
• /
• 2006

Length change, hydration heat, setting time and compressive strength of OPC were measured by adding KCl and replacing limestone powder so as to examine the influence of limestone powder on hydration of the OPC contained much chloride. In general, the chloride modified cement was high in heat of hydration, short in its setting time, low in its fluidity and low in its strength at 28 days due to the sudden hydration in its initial stage. As a result of the experiment, it has been demonstrated that heat of hydration, became low as one replaced limestone powder to the chloride modified cement, and the fluidity and shrinkage rate of mortar decreased without change in setting time; furthermore, the compressive strength at 28 days was improved.