• Journal of Ceramic Processing Research
• /
• v.13 no.spc1
• /
• pp.37-41
• /
• 2012

A lithium ion conducting borosilicate glass was fabricated by a conventional melt quenching technique from a mixture of Li2CO3, B2O3 and SiO2 powders. The Li ion conductivity of the lithium borosilicate glasses was evaluated in terms of the SiO2/B2O3 ratio. In the Li2O-B2O3-SiO2 ternary glass, the glass forming region decreases with an increasing Li2O content. At the same Li2O, the crystallization tendency of the glass samples increases with the SiO2/B2O3 ratio, resulting in a reduced glass forming region in the Li2O-B2O3-SiO2 ternary glass. The electrical conductivity moderately depends on the SiO2/B2O3 ratio in the Li2O-B2O3-SiO2 ternary glass. The conductivity of the glasses slightly increases with the SiO2/B2O3 ratio. The observed phenomenon can be explained by the modification of the glass structure as a function of the SiO2 content.

• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.1
• /
• pp.57-63
• /
• 2003

The effects of glass addition on the low-temperature sintering and microwave dielectric properties of $BaO-Nd_2O_3-TiO_2$ dielectric ceramics were studied. When 10∼13 wt% of lithium borosilicate glass was added, the sintering temperature decreased from 130$0^{\circ}C$to 850-$900^{\circ}C$relative density of more than 97% was obtained. When the sample was sintered at $850^{\circ}C$ with 10 wt% of glass, the dielectric properties of $\epsilon_r{\ge}54$, $Q{\times}f_0{\ge}2300$, and $\tau_f{\ge}+8ppm/^{\circ}C$ were obtained.

• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.98-103
• /
• 2003

The effect of glass addition on the low-temperature sintering and microwave dielectric properties in $BaO-Nd_2O_3-TiO_2$ dielectric ceramics were studied. When 10~30 wt% of alkali lithium borosilicate glass was added, the sintering temperature decreases from $1300^{\circ}C$;to;1000^{\circ}C$ and the relative density more than 95% was obtained. When the added amount of glass increased above 10 wt%, the density as well as dielectric properties changed, which was attributed to the second phase formation. When the sample was sintered at 100$0^{\circ}C$ with l0wt% of glass, the dielectric properties of $Qxf_o{ge}2800,;{varepsilon}_r{ge}65;and;{ au_f=+55 ppm/^{\circ}C$ were obtained.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.415-415
• /
• 2012

ICP (RF) 열 플라즈마 분말 합성법은 초고온 열플라즈마(~10,000 K) 속으로 원료물질을 투입한 뒤, 용융, 기화 및 재합성의 과정을 거쳐 초미분(<1 ${\mu}s$)을 합성하는 방법으로 고출력 시스템의 경우 고온/고 엔탈피 열 유동을 통한 고융점 및 저융점 복합물질의 동시 기화에 의한 물질 조성이 제어된 나노 복합체의 대량 합성이 가능할 것으로 기대되고 있다. 본 연구에서는 전북대학교 고온플라즈마 응용연구센터의 60&200 kW의 고출력 ICP (RF) 열 플라즈마 시스템을 이용하여 LTO (Lithium Titanium Oxide)와 IZTO (Indium Zinc Tin Oxide), Barium Borosilicate Glass (K2O-BaO-B2O3-SiO2)의 다성분계 나노 복합체를 합성하였으며, FE-SEM, TEM, XRD, ICP-OES를 이용하여 그 특성을 분석하였다.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.3 no.4
• /
• pp.335-340
• /
• 2005

The forward dissolution rate of a borosilicate waste glass was determined as an interlaboratory study(ILS) testing program for the evaluation of precision in the measurement of the dissolution rate or a waste glass using a single-pass flow-through(SPFT) test, whose conducting practice has been written for standardization through American Society for Testing and Materials (ASTM). A simulated low-activity waste glass powder with a size of 100/200 mesh was dissolved by lithium buffer solution (pH=10) at 70? under Ar atmosphere. By plotting the dissolution rates as a function of silicon and boron concentration in eluate, the forward dissolution rate of the glass was obtained as about $2.7\times10^{-5}g{\cdot}m{\cdot}s^{-1}$ in our laboratory.

• Journal of the Korean Ceramic Society
• /
• v.42 no.2 s.273
• /
• pp.81-87
• /
• 2005

The compositions for LTCC embedded capacitors based on $BaTiO_3$ ceramics with $5\~15\;wt\%$ of lithium-borosilicate glass frits were studied. After the glass frits, which is chemically stable and has acceptable ability of low-temperature sintering, were added to the host dielectric materials, the sintering behavior and dielectric properties were evaluated. As for $BaTiO_3$, relative density of >$95\%$, permittivity 990, and dielectric loss $3.1\%$ were obtained when sintered at $925^{\circ}C$ with 5 wt$\%$ of glass frits. As for $(Ba,Ca)(Ti,Zr)O_3$ ceramics, relative density of >$95\%$, open porosity <$0.5\%$, permittivity 700, and dielectric loss $2\%$ were obtained when sintered at $875^{\circ}C$ with 10 wt$\%$ of glass frits.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.3 s.32
• /
• pp.17-22
• /
• 2004

The microwave dielectric properties of $CaZrO_3$ ceramics with addition of $CaTiO_3$ were studied. The effect of glass addition on the low-temperature sintering and microwave dielectric properties of $CaZrO_3-CaTiO_3$ ceramics were also evaluated to develop the materials for functional substrates of low-temperature co-fired ceramics. When $10-20 wt\%$ of lithium borosilicate glass was added, the sintering temperature of the $CaZrO_3-CaTiO_3$ ceramics decreased from $1450^{\circ}C$ to below $900^{\circ}C$. As the $T_f$ of glass frits and $CaZrO_3$ are slightly negative and that of $CaTiO_3$ is significantly positive, zero $T_f$ could be realized by mixing an appropriate amount of $CaTiO_3$ with $CaZrO_3$. The $CaZrO_3-CaTiO_3$ ceramics sintered at $875^{\circ}C$ with $15wt\%$ glass frits showed the relative density of $98\%$, permittivity of 23, quality factor of 2500 GHz, and temperature coefficient of resonant frequency of $ -3 ppm/^{\circ}C$.