• 한국세라믹학회지
• /
• 제44권1호
• /
• pp.43-51
• /
• 2007

Fluidity, setting time, hydration heat, bond water ratio, compressive strength, SEM and BET of OPC were measured by adding 1.0 wt% KCl and replacing 20 wt% mineral admixture in order to examine effects of blast furnace slag (BFS), limestone powder (LSP), and fly ash (FA) on fluidity and strength development of the cement contained much chloride. In general, the cement contained much chloride was high in heat of hydration, short in its setting time, low in its fluidity and low in its strength at 28 days due to the rapid hydration in its initial stage. As a result of the experiment, it has been demonstrated that fluidity became improved but the compressive strength at 28 days was decreased as replaced LSP to the cement contained much chloride. the fluidity and compressive strength at 28 days was improved as replaced BFS, the initial compressive strength development was improved due to the activation of initial reaction by KCl. Fluidity, initial compressive strength and late compressive strength at 28 days of cement contained much chloride replaced 5 wt% LSP and 15 wt% BFS concurrently was better than OPC, but the hydration heat was lower.

• Advances in concrete construction
• /
• 제2권1호
• /
• pp.13-27
• /
• 2014

The principal objective of this study is to deepen the characterization studies already led on sand concretes in previous works. Indeed, it consists in studying the effect of the sand type on the main properties of sand concrete: fracture and mechanical properties. We particularly insist on the determination of the fracture characteristics of this material which apparently have not been studied. To carry out this study, four different types of sand have been used: dune sand (DS), river sand (RS), crushed sand (CS) and river-dune sand (RDS). These sands differ in mineralogical nature, grain shape, angularity, particle size, proportion of fine elements, etc. The obtained results show that the particle size distribution of sand has marked its influence in all the studied properties of sand concrete since the sand having the highest diameter and the best particle size distribution has given the best fracture and mechanical properties. The grain shape, the angularity and the nature of sand have also marked their influence: thanks to its angularity and its limestone nature, crushed sand yielded good results compared to river and dune sands which are characterized by rounded shape and siliceous nature. Finally, it should further be noted that the sand concrete presents values of fracture and mechanical properties slightly lower than those of ordinary concrete. Compared to mortar, although the mechanical strength is lower, the fracture parameters are almost comparable. In all cases, the sand grains are debonded from the paste cement during the fracture which means that the crack goes through the paste-aggregate interface.

• 한국세라믹학회지
• /
• 제40권8호
• /
• pp.804-810
• /
• 2003

건설폐기물 중 폐콘크리트를 40$0^{\circ}C$로 가열한 후 ball mill로 분쇄하여 재생골재를 생산할 때 발생된 미분말을 보통 포틀랜드 시멘트의 SiO$_2$, CaO, A1$_2$O$_3$원에 대한 대체원료물질로서 활용하고자 하였다. 클링커를 제조하기 위한 주원료는 석회석, shale, 전로슬래그, fly ash를 이용하였고, modulus는 LSF:91.0, SM:2.60, IM:1.60로 고정한 후 shale에 대해 미분말을 25, 50, 15, 100%까지 치환하여 클링커를 제조하였다. 클링커의 주요생성광물은 1,45$0^{\circ}C$에서 OPC와 같은 광물상인 $C_3$S, $\beta$-C$_2$S, $C_3$A, $C_4$AF 상으로 나타났다. 조합원료의 반응성을 비교하기 위해 시차열분석을 실시하고, 소성성지수를 구한 결과, 클링커의 광물상 생성온도는 plain과 유사했으며, 소성성지수는 48.6-51.4 정도로 나타났다.

• 한국건설순환자원학회논문집
• /
• 제5권4호
• /
• pp.353-358
• /
• 2017

본 연구의 목적은 고성능 시멘트계열 재료의 점성을 감소시키는 것에 대한 기초적인 정보를 제공하는 것이다. 레올로지적 측면에서 시멘트 계열 재료의 유동성을 결정하는 것은 항복응력과 소성점도이다. 물결합재비가 낮고 분체비율이 높은 고성능 시멘트계열 재료의 경우, 고성능 감수제로는 항복응력을 줄일 수는 있으나 점성을 낮추는 것이 어렵다. 따라서 이 연구에서는 시멘트계열 재료의 소성점도를 줄이기 위한 목적으로 두가지 방법, 즉, 분말상태의 적절한 조합 및 저점도형 고성능 감수제의 사용을 제시하였다. 첫째, 다양한 산업부산물을 치환하여 석탄재 원분과 폐석회석 분말이 점성저하에 효과가 있음을 밝혔으며 저점도형 고성능 감수제가 일반형 고성능 감수제에 비해 시멘트 페이스트의 점도를 낮추는 것을 확인하였다. 따라서 본 연구의 결과를 바탕으로 다양한 방법의 시멘트계열 재료의 점도를 낮추는 기초적인 방법을 제공할 것으로 기대한다.