• Elastomers and Composites
• /
• v.41 no.1
• /
• pp.27-39
• /
• 2006

In this study, modified DA-MMT filled NR/DA-MMT nanocomposites were manufactured by a latex method and a compounding method. Cure characteristics and mechanical properties of the Cloisite 15A, carbon black, Na-MMT filled NR compounds and the DA-MMT filled NR compound by a latex method were also evaluated. The filler content of all compounds was 10phr except the carbon black filled compound. Degree of intercalation and dispersion was characterized by X-ray diffraction (XRD) and transmission electron microscope (TEM). According to the XRD diffraction pattern and TEM analysis, extensive intercalation and homogeneous dispersion of the clay were obtained after the two-roll milling. Although the layer distance was increased, some parts of DA-MMT showed the layer distance of Na-MMT after vulcanization. DA-MMT filled NR compounds showed the highest ODR torques, tensile strength, modulus, and tear energy. The NR/DA-MMT nanocomposite (by a latex method) compared with a NR/DA-MMT nanocomposite (by a compounding method) was found that the improvement of the mechanical properties was mainly due to the degree of dispersion of the clay.

• Journal of the Semiconductor & Display Technology
• /
• v.16 no.1
• /
• pp.52-58
• /
• 2017

Graphene oxide (GO)/carboxylated styrene-butadiene rubber (XSBR) nanocomposites with various contents of GO were prepared by a latex compounding method. It has been confirmed that the functional groups of GO and the hydrogen bonds between GO and XSBR are existed. It can be seen that the scorch time ($t_{s2}$), which is the measurement of incipient vulcanization of rubber, showed a delay after the addition of GO. Field emission scanning electron microscopy was employed to confirm the uniform dispersion of filler in the matrix. Indeed, with increasing fillers loading, the torque, tensile strength, thermal stability and crosslink density of obtained nanocomposites were improved. These results were correlated to the better dispersion of fillers through the rubber matrix.

• Elastomers and Composites
• /
• v.53 no.1
• /
• pp.6-12
• /
• 2018

Styrene-butadiene Rubber (SBR) Latex composites, incorporated with cellulose/starch-silica hybrids synthesized by gel-adsorption method, were filled into rubber by the latex compounding method. The structure morphology, mechanical properties, and thermodynamic properties of gel-silica hybrids were characterized. The states of hybrids which used as fillers were also characterized by SEM. As the fillers ratio increased, the difference for storage modulus of samples had been morphology by rubber process analyzer (RPA). Then, as more fillers ratio was filled into the matrix, the best tensile strength result, and the largest modulus value were also proved by UTM and RPA. As for thermal stability, increase in the ratio of fillers led to higher initial decomposition temperature, which was also proved by TGA. The swelling ratio of samples has also been characterized. From the results of all the tests, cellulose-silica hybrid showed the best results as a filler, and the best filling ratio of this hybrid is about 10 phr, which has the best storage modulus and great tensile strength.