An experimental investigation with 2.8kW Nd:YAG laser system was carried out to study the effects of different laser process parameters on the microstructure and hardness of STD11. The optical lens with the elliptical profile are designed to obtain a wide surface hardening area with uniform hardness. The Laser beam is allowed to scan on the surface of the work piece varying the power (1600, 1800 and 1900kW) and traverse speed (200, 400, 600, 800 and 1000mm/min) at three different F-numbers of lens. After laser surface treatment three zones, In the microstructure have been observed : melted zone(decarburization), heat affected zone(martensite), and the substrate.

• 열처리공학회지
• /
• 제9권4호
• /
• pp.271-280
• /
• 1996

This study has been performed to investigate into some effects of power density and traverse speed of laser beam on optical microstructure, hardness and wear characteristics of gray cast iron treated by laser surface hardening technique. Optical micrograph has shown that large martensite and a small amount of retained austenite appear in outermost surface layer with fine martensite in inside hardened zone. Hardness measurements have revealed that the range of maximun hardness value is $Hv=650{\pm}15$ and as the power density increases and the traverse speed decreses, the depth of hardened zone increases due to as increase in input power density. Wear test has exhibited that wear rasistance of laser surface hardened specimen is superier compared to that of untreated specimen under the condition of same load at a given sliding distance, showing that absorption results of an wxidized substance due to a heavy abrasion appear in untreated specimen. The amount of weight loss of laser surface hardened specimen with respect to sliding distance at a given load decreses with increasing traverse speed at a given power density and with increasing power density at a given traverse speed.

• 열처리공학회지
• /
• 제33권1호
• /
• pp.25-32
• /
• 2020

In this study, the tribology of laser patterned DLC thin film was studied. DLC thin films were coated by RF-PECVD to improve the durability of tungsten carbide (WC) materials. DLC thin films have high hardness and low friction characteristics. Dot and line patterning was processed on the surface of DLC thin film with femtosecond laser, and the coefficient of friction was improved. As a result of ball on disk abrasion test, the hardness and friction coefficient of DLC thin films were much better than that of WC material. The friction coefficient of DLC thin film with dot patterning and line patterning showed better results. The excellent performance of the laser patterned DLC coating is appeared to reduce the coefficient of friction due to the reduction of surface contact area.

• 열처리공학회지
• /
• 제8권1호
• /
• pp.32-43
• /
• 1995

Ti-6Al-4V alloy are widely used in chemical and aircraft industries for their good corrosion resistance and high strength to weight ratio. Surface alloying of Ti alloy by $CO_2$ laser is able to produce few hundred micrometers thick TiN surface-alloyed layer with high hardness on the substrate very simplely by injecting reaction gas($N_2$) into a laser-generated melt pool and adjust the hardness to the specific requirements of the individual application by changing of laser processing parameters. This research has been investigated the effect of such parameters on TiN surface-alloying of Ti-6Al-4V alloy by $CO_2$ laser. The maximum hardness of TiN surface-alloyed zone waw obtained by injecting 100% $N_2$ gas and it was decreased as the amount of $N_2$ gas in Ar and $N_2$ gas mixture was decreased. As scanning speed was increased, the hardness and depth of TiN surface-alloyed zone was decreased at constant laser power. The surface hardness after double scanning laser treatment is higher than that of single scanning. At constant laser power, the surface roughness is increased after the surface alloying if laser scanning speed is decreased.

• 한국분말재료학회지
• /
• 제28권2호
• /
• pp.134-142
• /
• 2021

In this study, AlSi10Mg powders with average diameters of 44 ㎛ are additively manufactured into bulk samples using a selective laser melting (SLM) process. Post-heat treatment to reduce residual stress in the as-synthesized sample is performed at different temperatures. From the results of a tensile test, as the heat-treatment temperature increases from 270 to 320℃, strength decreases while elongation significantly increases up to 13% at 320℃. The microstructures and tensile properties of the two heat-treated samples at 290 and 320℃, respectively, are characterized and compared to those of the as-synthesized samples. Interestingly, the Si-rich phases that network in the as-synthesized state are discontinuously separated, and the size of the particle-shaped Si phases becomes large and spherical as the heat-treatment temperature increases. Due to these morphological changes of Si-rich phases, the reduction in tensile strengths and increase in elongations, respectively, can be obtained by the post-heat treatment process. These results provide fundamental information for the practical applications of AlSi10Mg parts fabricated by SLM.

• 한국생산제조학회지
• /
• 제20권5호
• /
• pp.646-652
• /
• 2011

Recently, lots of automobile part manufacturers try to increase glass fiber content of their plastic parts to improve strength and impact-resistance. For this reason, injection mold requires high hardness and wear-resistant. Laser surface treatment is used to improve characteristics of wear and to enhance the fatigue resistance for injection mold. In this paper, high carbon steel (HP4MA) for injection mold material was heat-treated to harden surface by using high power diode laser (HPDL). To find the process parameters for laser surface treatment of HP4MA, many experiments are carried out as changing the parameters of surface temperature and travel speed of laser. From the results of the experiments, it has been shown that the maximum average hardness is approximately 711~739 Hv when the temperature and the travel of laser are $1,050^{\circ}C$ and 2 mm/sec.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.59-64
• /
• 2002

Effects of the aging treatments on the microstructure and strength of heat affected zone(HAZ) in the welds of a age-hardened Al-Mg-Si alloy, 5N01-T5, were investigated. The base metal aging treatments before MIG welding were conducted at 423K to 473K for 28.8ks Post weld heat treatment(PWHT) to recover the HAZ strength was performed at 448K for 28.8ks. Microstructure observations, hardness measurements and tensile tests were conducted to study properties of the MIG weld joints. The position of the softest region in HAZ where the hardness insufficiently recovered after natural aging and PWHT was at a distance of approximately 15mm from the center of the fusion zone. Hardness of the softest regions after natural aging and PWHT decreased with increase in the base metal aging temperature. TEM observation clarified that strengthening ${\beta}$"(Mg$_2$Si) precipitates and coarse ${\beta}$′ precipitates affected the hardnes of HAZ. Incomplete recover of hardness in HAZ after PWHT was caused by the precipitating of non-hardening ${\beta}$′ phase during the weld thermal cycle. In order to examine the effects of weldheat input and welding speed, the laser weld joints were also investigated and compared with the MIG weld ones. Laser welding had the narrower width of the softened regions in HAZ compared with MIG welding. The hardness of the softest regions of the laser welds after PWHT was higher than that of the MIG welds. Quantitative relations between hardness of the softest region and base metal aging temperature were obtained for both welding processes. Accordingly, the equations to estimate the strength of the weld joints after PWHT with varying base metal temperatures were proposed for MIG welding and laser welding.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2000년도 특별강연 및 추계학술발표대회 개요집
• /
• pp.260-263
• /
• 2000

A methodology is developed and many used to evaluate the response sensitivity of the thermal systems to variations in their design parameters. Technique for computing the sensitivity of temperature distributions to changes in processing parameters needed for deciding the more effective laser input parameters for laser surface hardening treatment are considered. In this study, a state equation governing the heat flow in laser surface treatment is analyzed using a three-dimensional finite element method and sensitivity data of the processing parameter obtained using a direct differentiation method applied for sensitivity analysis. The interesting processing parameter is taken as the laser scan velocity and characteristic beam radius( $r_{b}$) of the sensitivity of the temperature T versus v and $r_{b}$ is analyzed. And these sensitivity results obtained in another parameters are fixed condition. To verifying the numerical analysis results, hardened layer dimensions (width and depth) of the numerical analysis compared with the results of an experimental data.ata.

• 열처리공학회지
• /
• 제20권4호
• /
• pp.203-208
• /
• 2007

고출력 다이오드레이저(High Power Diode Laser, HPDL)는 독일을 중심으로 한 유럽내의 여러 국가에서 적용분야를 점차 높여가고 있으며, 금속소재에 있어서의 높은 흡수율 및 발진장치의 높은 에너지 변환효율이 중요한 요인이라고 할 수 있다. 레이저소스로부터 출력되는 사각형 또는 라인형의 레이저-빔은 다이오드레이저를 이용한 금속의 열처리분야에 매우 적합하며, 이미 Body-in-White 차체(Car Body) 양산라인의 브레이징 공정에는 수 년 전부터 실제 적용되어왔다. 또한, 다양한 빔 형상, 균일한 에너지 밀도, 낮은 운전비용, 간단한 유지보수, 좁은 설치공간, 손쉽게 이동이 가능한 구조, 광케이블을 이용한 레이저-빔의 전송 등 여러 장점으로 인하여 보다 유연하고 효과적인 생산환경을 구축할 수 있다는 것 또한 다이오드레이저의 응용분야를 확대하는 요인이 되었다.

• 열처리공학회지
• /
• 제9권4호
• /
• pp.289-299
• /
• 1996

This study has been performed to investigate into some effects of power density and traverse speed of laser beam on the microstructure, hardness and residual stress of AISI 4140 treated by laser surface hardening technique. Optical micrograph has shown that large martensite and a small amount of retained austenite in outermost surface layer and fine lath martensite in inner surface hardened layer are formed under the condition of a given power density and traverse speed. Hardness measurements have revealed that as the power density increases at a given 2.0m/min of the traverse speed, the maximum hardness values of outermost surface hardened layer is increased from Hv=635 to Hv=670. X-ray analysis for residual stress has exhibited that low compressive residual stress values are obtained in center point of the cress section of surface hardened layer with in mid point between the edge and the center point, about 1.5mm from the center point, due simply to a difference in self-quenching rate. It has been shown that the higher the power density at a given traverse speed and the olwer the traverse speed at a given power density, the more the compressive residual stress values are increased due to an increase in the input heat of laser beam.