• Journal of the Korean Wood Science and Technology
• /
• v.28 no.4
• /
• pp.41-50
• /
• 2000

Cement-bonded particleboard is being used as outdoor siding material all over the world, because this composite particularly bears a light weight, high resistance against fire, decay, and crack by cyclic freezing and thawing, anti-shock property, and strength enhancement. Construction systems are currently changing into a frame-building style and wooden houses are being constructed with prefabrication type. Therefore, they require a more durability at outdoor-exposed sides. In this study, the cement hydration property for Korean pine particle, Japanese larch particle and face- and middle layer particles (designated as PB particle below) used in Korean particleboard-manufacturing company was investigated, and the rapid manufacturing characteristics of cement-bonded particleboard by supercritical $CO_2$ curing was evaluated. Korean pine flour showed a good hydration property, however, larch flour showed a bad one. PB particle had a better hydration property than larch flour. The addition of $Na_2SiO_3$ indicated a negative effect on hydration, however, $MgCl_2$ had a positive one. Curing by supercritical $CO_2$ fluid gave a conspicuous enhancement in the performances of cement-bonded particleboards compared to conventional curing. $MgCl_2$ 3%-added PB particle had the highest properties, and $MgCl_2$ 1%-added Korean pine particle had the second class with the conditions of cement/wood ratio of 2.7, a small fraction-screened particle and supercritical curing. On the contrary, the composition of non-hammermilled or large fraction-screened particle at cement/wood ratio of 2.2 was poorer. Also, the feasibility for actual use of 3%-added, small PB particle-screened fraction was greatest of all the conventional curing treatments. Relative superiority of supercritical curing vs. conventional curing at dimensional stability was not so apparent as in strength properties. Through the thermogravimetric analysis, it was ascertained that the peak of a component $CaCO_3$ was highest, and the two weak peaks of calcium silicate hydrate and ettringite and $Ca(OH)_2$ were present in supercritical treatment. Accordingly, it was inferred that the increased formation of carbonates in board contributes to strength enhancement.

• Journal of Korean Society of Forest Science
• /
• v.63 no.1
• /
• pp.12-20
• /
• 1984

This research was performed to estimate the properties of particleboard based on the press time and temperature which was made of chip of larch that grows in Korea. The results in this study were as follows: 1) Even though the chips, 1:1-35 ratio between length and thickness, are relatively bad condition, the surface smoothness that can easily spread the adhesive evenly and thoroughly and bonding ability of chips can give proper physical properties. 2) It shows more mechanical properties at the press time of 10 min. in MOR (Modulus of Rupture), MOE (Modulus of Elasticity) and SHA (Screw Holding Ability). 3) It is not significant according to the press time 20 min. in MOR, IBS (Internal Bonding Strength) and SHA, for the reciprocal actions between the accelerating aging effect of chip and the softening effect of adhesion are occured. 4) IBS is rising according to the increasing temp at the press time of 10 min. Because it needs to transfer the plate heat to make the proper hardening temp. In the layer. 5) The heat treatment effects have greatly influenced the stahility of dimension by falling the absorption, anisotropy and inhomegenity. As a result of these the values of thickness and linear expansion ratio were respectively dropped by the increase of press temp and the time and so did absorption.

• Journal of the Korean Wood Science and Technology
• /
• v.30 no.1
• /
• pp.25-33
• /
• 2002

Improvement of density profile and sound absorption capability of particleboard was attempted. Three types of hot pressing methods examined ; flat-platen pressing method (A-type pressing), hot pressing in forming box (B-type pressing), and hot pressing set up jagged caul in forming box (C-type pressing). The raw materials were larch(Larix leptolepis (S, et. Z.) Gorden) shavings, phenol formaldehyde resin, and the particleboard perforated with stair type. The physical and mechanical properties such as specific gravity, bending strength (MOR), internal bonding strength (IB) and sound absorption coefficients were examined. The results are summarized as follows : 1) The MOR and internal bonding strength of the board pressed in forming box were higher than those of flat-platen pressed board. 2) The minimum density to average density ratio in thickness direction which pressed in forming box showed about 923%, in the case of 35 mm commercial particleboard and 50 mm flat-platen pressed board, its values showed about 66.4% and 865% respectively. 3) Sound absorption coefficients of the particleboard perforated with stair type were higher than those of flat-plated pressed board and commercial particleboard.