• Elastomers and Composites
• /
• 제25권3호
• /
• pp.195-202
• /
• 1990

Rubber-modified polyurethane resin which was prepolymer type terminated with NCO, was synthesized by reacting isocyanate groups[NCO] and hydroxyl groups[OH]. Polybutadiene rubbers which had OH groups in the side of rubber chains, were charged at ratio $0%{\sim}40%$ of solid component in reactants. For products, physical properties were investigated experimentally. The results abtained in experiment were as follows. 1. Liquid resin and dried film was good solubility and clearity at less than 25%, 20% of rubber without being related to sort. 2. G-1000 showed better properties than R-45HT in solubility, dring time and adhesive strength. 3. Dring time and adhesive strength were considerably influenced by molecular weigh and structure of rubber. 4. In using 25% of mixed rubber(G-1000/R-45HT=50/50), It represented best properties in dring time(10 minute) and adhesive strength($23Kg/cm^2$).

• 한국환경과학회지
• /
• 제23권11호
• /
• pp.1909-1918
• /
• 2014

In this experiment no solvent based polyurethane(PU) adhesives were prepared with the polyol, isocyanate, dioctyl phthalate(DOP), 2-hydroxyethylacrylate(2-HEA) and other acrylate monomers. The softenening point of the PU adhesives measured by Ring & Ball method were examined in the present study. And adhesion strength and mechanical properties such as tensile strength and 100% modulus of the PU adhesives were evaluated by Universal Test Machine. The experimental results showed that increase of both DPE-41, benzoylperoxide(BPO) and toluene diisocyanate(TDI) increased softenening point, adhesion strength, tensile strength and 100% modulus. However as DOP content increased sofenening point, adhesion strength decreased and tensile strength, 100% modulus also decreased.

• Korean Chemical Engineering Research
• /
• 제48권5호
• /
• pp.568-573
• /
• 2010

본 연구에서는 polyester 섬유표면에 활성기를 부여하기 위한 전처리제로 isocyanate를 이용하여 농도에 따른 접착력을 평가하였다. 이 후 HNBR compound와 polyester fabric의 접착 시 접착력이 우수한 RFL 용액용 latex 선정 및 F/R mole ratio, F/R resin/latex 무게 비에 따른 실험을 진행하였다. 그 결과 전처리제의 농도가 7 wt%인 경우 가장 높은 접착력을 나타내었으며, RFL 용액용 latex로는 HNBR 컴파운드와 상용성이 높은 NBR latex가 우수한 결과를 나타내었고 F/R mole ratio, FR resin/latex 무게비가 각각 1/1, 20%일 때 가장 높은 접착력을 나타내었다. 또한, peel test와 FTIR 분석을 이용해 RF resin의 열처리 온도에 따른 접착강도와 spectra의 peak 변화를 평가해 본 결과 최적의 열처리 온도는 $200^{\circ}C$이었다.

• 접착 및 계면
• /
• 제14권1호
• /
• pp.43-48
• /
• 2013

압력감응성 아크릴 점착제의 물성은 가교를 위한 관능성그룹을 가진 단량체를 이용하여 쉽게 물성을 조절할 수 있다. 본 연구에서는 두개의 다른 가교제, isocyanate 및 epoxy형 가교제에 따른 아크릴 점착제의 가교특성과 물성을 연구하였다. 2-Ethylhexyl acrylate, acrylic acid (AA)와 2-hydroxyethyl methacrylate를 주 단량체로 하여 이소시아네이트 또는 에폭시형 가교제로 가교한 점착제의 박리점착 특성, 볼텍, 유지력 및 수축성을 고찰하였다. 점착특성은 AA함량 증가와 더불어 증가하였고 가교점이 많고 ether와 같은 유연한 결합을 생성하는 에폭시형 가교제에서 우수한 물성을 나타내었다.

• 한국염색가공학회지
• /
• 제30권2호
• /
• pp.90-97
• /
• 2018

Hydrophilic reactive hot-melt polyurethane adhesive(HRHA) using a hydrophilic polyol having different molecular weight and NCO index was synthesized. This HRHA was synthesized using Polyethylene glycol(PEG) as a hydrophilic polyol, Polypropylene glycol(PPG) and Polycaprolactone diol(PCL) as hydrophobic polyols, and Methylene diphenyl diisocyanate(MDI) as an isocyanate. The changes in IR spectrum, viscosity and thermal properties of HRHA with different PEG molecular weights and NCO index were investigated, and the tensile strength and elongation of the HRHA casting film and the peel strength, moisture permeability and water pressure of the HRHA coated fabric were confirmed. In this experiment, as the molecular weight of PEG and NCO index increased, the adhesive strength, tensile strength, elongation and moisture permeability was increased but viscosity and Tg was decreased.

• Elastomers and Composites
• /
• 제52권4호
• /
• pp.295-302
• /
• 2017

Polyurethane dispersion (PUD) polymers were synthesized by using polyether and polyester polyol. The effect of ionomeric centers, r(NCO / OH) values, chain extender process, and chain extender types on the adhesion properties was investigated. In the case of polyether-based PUD, the ionic center, r value, chain extension process and chain extender types were not adjusted even after adjustment. In the case of polyester-based PUD, when the ionic center content was more than 2.5%, the state of adhesive strength was $2.0kgf/cm^2$ or more. On the other hand, the initial adhesive strength was excellent at about $1kgf/cm^2$ when the ionic center content was over 3.5%. When the r value was 1.3 or more, it was found that the initial bonding strength and the state of bonding strength were excellent at about $1kgf/cm^2$ and $2.1kgf/cm^2$ or higher, respectively. An IR spectrum analysis of the synthesized PUD confirmed that PUD was composed of urethane based on the N-H characteristic peak at $3340cm^{-1}$ and the urethane characteristic peak at $1730cm^{-1}$. Moreover, the characteristic peaks of the isocyanate ($2260cm^{-1}$) used in the preparation of the prepolymer were not observed. As a result, the residual -NCO was not observed, and urethane was completely synthesized.

• Elastomers and Composites
• /
• 제49권3호
• /
• pp.245-252
• /
• 2014

폴리올, 이소시아네이트, 2-HEMA 및 기타 아크릴레이트 단량체들로부터 제조된 폴리우레탄 접착제의 FT-IR측정과 물성을 검토하였다. 폴리우레탄 접착제의 연화점, 점도, 접착강도 및 기계적 물성들이 각각 링과볼법, Brookfield 점도계 및 만능시험기를 이용하여 검토되었다. 실험 결과에 의하면 PPG 함량 및 부틸아크릴레이트 함량이 증가함에 따라 연화점, 접착강도, 인장강도 및 100% modulus 값 등은 감소하는 것을 보여준다. 하지만 2-HEMA 및 MDI량이 증가할수록 인장강도 및 100% modulus값 등은 증가하였으며 점도와 NCO함량 등도 또한 증가하였다.

• Journal of the Korean Wood Science and Technology
• /
• 제47권2호
• /
• pp.239-248
• /
• 2019

This research presents an improvement of the physical and mechanical properties of composite board (com-ply) made of Oriented Strand Board (OSB) coated with wood veneer of Pine (Pinus merkusii), Avocado (Persea Americana) and Mahogany (Swietenia mahogany). 1.5 mm thick veneers of those three wood types were adhered to the surface of OSB using two adhesive types: epoxy and isocyanate. The adhesive with the glue spread of $250g\;m^{-2}$ applied using single glue line was spread and then cold pressed with the pressure of $15kg\;cm^{-2}$ for 3 hours. The research result showed an improving dimension stability of com-ply, but not found on all parameters of physical property test. The moisture content seemed to be influenced by the com-ply type, yet not related to its thickness swelling, water absorption and linear expansion. The exception took place in the parallel linear expansion when immersed for 2 hours. The highest to the lowest increases of MOE and MOR were consecutively found on OSB coated with wood veneer of Pine, Mahogany and Avocado. However, the increases were statistically insignificant. The highest increasing screw hold power was found at the com-ply type AE (avocado veneer and epoxy adhesive) that was by 28%.

• 공업화학
• /
• 제24권2호
• /
• pp.148-154
• /
• 2013

UV 경화형 아크릴 점착제는 세상에서 매우 다양한 형태로 이용되는데, 반도체 산업을 기반으로 하는 웨이퍼 제조공정에서도 이용되고 있다. 특히 반도체에 사용되는 웨이퍼가 더욱 얇아짐에 따라, UV 경화형 아크릴 점착제는 더욱 적절한 점착 성능을 요구 받고 있다. 본 연구는 2-EHA (2-ethyl hexyl acrylate), 2-EHMA (2-ethyl hexyl methacrylate), SM (styrene monomer), 2-HEA (2-hydroxy ethyl acrylate), acrylic acid 모노머를 이용하여 hydroxy기를 가진 아크릴 수지점착제를 합성한 후 MOI (methacryloyloxyethyl isocyanate)의 투입량 조절을 통한 경화 특성을 향상시킬 수 있는 부가반응을 시킨 이소시아네이트 변성 아크릴 수지 점착제를 제조하여, 적절한 접착 성능을 알아보고, 수산기 값의 정도와 UV 조사량의 차이에 따라 웨이퍼 제조의 최적화된 조건을 찾았다. 시험 결과 UV 경화형 점착제에서 수산기(Hydroxyl group, -OH)와 이소시아네이트기(isocyanate group, -NCO)의 1 : 1 당량비로 이소시아네이트 경화제를 사용할 경우 수산기값이 클수록, UV 조사 전 박리력이 감소하였다. UV 조사량이 증가할수록 높은 경화 특성 때문에 박리접착 강도는 낮아졌다.

• 한국산학기술학회논문지
• /
• 제12권3호
• /
• pp.1479-1487
• /
• 2011

모바일 IT기기 등의 전자부품 분야에서 다기능, 고용량 메모리를 가능하게 하는 패키지의 중요성이 점차 증대되고 있다. 이러한 목적으로 여러개의 칩을 하나의 패키지에 실장하여 다기능, 고용량을 구현하는 Multi Chip Package(MCP)가 활용되고 있다. 이러한 MCP에서 칩과 칩간 접합 혹은 칩과 지지부재(substrate)간 접합을 구현하기위해 에폭시계 필름형 접착제가 사용되고 있다. 에폭시, 아민, 머캡탄, 아이소시아네이트 등의 유기 반응기를 가진 실란커플링제를 적용하여 에폭시계 필름형 접착제에 대한 점착성과 신뢰성을 확인하였다. 결과로부터 에폭시계 반응기를 가진 실란커플링제를 적용한 시료의 점착성과 필특성이 가장 뛰어났으며, 내습 테스트에서 계면파괴가 억제되어 가장 좋은 신뢰성을 나타내었다.