• Smart Structures and Systems
• /
• v.25 no.3
• /
• pp.337-343
• /
• 2020

In this paper, we focused on the self-healing concrete using new nano-capsules. Three types of nano-capsules with respect to availability, high strength and temperature tolerance are used; type 1 is URF and polyethylene (PE) as shell and nano titanium oxide (TiO₂) as core, type 2 is URF and PE as shell and nano silica oxide (SiO₂) as core, type 3 is PE as shell and nano silica oxide (SiO₂) as core. The concrete samples mixed by nano-capsules with three percents of 0.5, 1 and 1.5. Based on experimental tests and the compressive strength of samples, the URF-PE-SiO₂ is selected for additional tests of compressive strength before and after recovery, ultrasonic test, ion chlorine and water penetration depths. After careful investigation, it is concluded that the optimum value of URF-PE-SiO₂ nano-capsules is 0.5% since leads to higher compressive strength, ultrasonic test, ion chlorine and water penetration depths.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.6
• /
• pp.16-23
• /
• 2018

In this study, Polydimethylsiloxane (PDMS) was applied to Strain Hardening Cement Composites (SHCC) for penetrating water repellency. The penetration depth of PDMS, strength of SHCC, and chloride ion penetration resistance of SHCC were investigated. As a result of measuring penetration depth of PDMS when applying different application method, it was confirmed that all methods satisfied the requirements of KS F 4930. Although the immersion method showed the largest penetration depth, the spray method was considered to be more appropriate considering the ease of field application. Compressive strength tests showed that the penetration depth of PDMS decreased as the compressive strength of SHCC increased. The compressive strength of M4-A and M4-B specimens with large PDMS penetration depths decreased by 9.6% and 8.0%, respectively, compared with those of M4 specimens produced without PDMS. Compressive strengths of the M1-A and M1-B specimens with small PDMS penetration depths were reduced by 4% and 2.2%, respectively, compared with the M1 specimen. As a result, it can be seen that the strength reduction rate of SHCC increases as the penetration depth of PDMS increases. The chlorine ion penetration tests showed that the chlorine ion penetration resistance increases with the penetration depth of PDMS.