• Journal of Adhesion and Interface
• /
• v.2 no.3
• /
• pp.9-15
• /
• 2001

To estimate the effect of the surface state of the EVA foam on an adhesion, the surface was treated with solvents having different values of a solubility parameter and a surface tension. The morphology and the contact angle were measured by SEM and contact angle tester, respectively. The value of the critical surface tension(${\gamma}_{c,0}$) of the EVA foam calculated by Zismann plot was 27.08 dyne/cm. The surface state and the ${\gamma}_c$ of the EVA foam were changed by solvent treatment. The swelling ratio of EVA foam was influenced by solubility parameter of a solvent, on the other hand the degree of change in the surface state was dependent on a surface tension of a solvent. When a surface tension of solvent. When a surface tension of solvent is lower than ${\gamma}_{c,0}$ of the EVA foam, the wettability of a solvent was good and the surface state was greatly changed. The adhesion strength of EVA foam was greatly improved to above 600% as compared to that of the untreated one. As the ${\gamma}_c$ of EVA was closed to the surface tension of the primer, the good adhesion strength was obtained.

• Korean Journal of Materials Research
• /
• v.8 no.3
• /
• pp.189-194
• /
• 1998

The redistribution behavior of boron during Co silicidation annealing in the Co/metal/Si system was investigated using SIMS. Ti, Nb and Hf films were used as epitaxy promoting metal layers. After annealing treatment the boron peak height was about 1 order lowered in Co/Ti/Si and Co/Nb/Si systems but the relative peak position from the surface did not change. The distribution of boron was very similar to those of Ti and Nb, because of the strong affinities of boron with them. Also, the position of the main boron peak in the Co/Hf/Si system was almost the same as that of Hf, but the distribution feature of the Co/Hf/Si system somewhat differed from those of Co/Ti/Si and Co/Nb/Si systems. This implies that the affinity between B and Hf is weaker than those of B-Ti and B-Nb. Boron tends to be depleted at the silicidelsi interface while it tends to be piled-up at the Co-metal/Co silicide interface during silicidation annealing.

• Journal of Adhesion and Interface
• /
• v.20 no.1
• /
• pp.1-8
• /
• 2019

Fabrication of monolayer is important method for enhancing physical and chemical characteristics such as light shielding and antireflection while maintaining thin film properties. In previous studies, monolayers were fabricated by various methods on small substrates, but processes were complicated and difficult to form monolayers with large area. We used rod coating equipment with a small amount of coating liquid to form a HCP (hexagonal closed packing) coating of PMMA beads on PET(poly(ethylene terephthalate)) substrate with $20cm{\times}20cm$ size. We observed that changes in morphologies of monolayers by using the solvents with different boiling points and vapor pressures, by adapting surfactants on particles and by applying plasma treatment on substrates. The coverage was increased by 20% by optimizing the coating conditions including meniscus of beads, control of the attraction - repulsion forces and surface energy. This result can potentially be applied to optical films and sensors because it is possible to make a uniform and large-scale monolayer in a simple and rapid manner when it is compared to the methods in previous studies.

• Journal of Adhesion and Interface
• /
• v.25 no.3
• /
• pp.82-87
• /
• 2024

There is a growing interest in eco-friendly materials to achieve carbon neutrality, and many studies have been published on the use of functional nanoparticles in natural fibers as smart composites. This study is about the optimization of manufacturing parameters for carbon nanotube (CNT) growth by chemical vapor deposition (CVD) on the surface of basalt fiber. Co-Cu-based metal catalysts were prepared by co-precipitation method for CNT growth on the surface of basalt fiber. The catalyst was fixed to basalt fibers through a spray process. The effect of heat treatment temperature conditions and fiber surface conditions on the growth of CNT was evaluated. The growth of CNT was investigated using transmission electron microscopy (TEM) and scanning electron microscopy (SEM) to observe changes in their shape and diameter. The tensile strength of the composites using CNT/basalt fiber fabrics and amine-based epoxy as the base material prepared at different heat treatment temperatures was compared and evaluated according to ASTM D3039. We have observed that stable CNT are manufactured at temperatures above 600℃, while carbon nanofibers (CNF) are fabricated at temperatures above 400℃. The sizing material present on the surface of the basalt fiber was a hindrance to CNT growth.

• Composites Research
• /
• v.33 no.5
• /
• pp.235-240
• /
• 2020

In this study, in order to improve the impact resistance of the B₄C tile-inserted B₄C_p/Al7075 hybrid composite, a control method of the B₄C/Al7075 interface was developed and the characteristics of the controlled interface were analyzed. B₂O₃, Ni, and Si were coated on the B₄C tile surface using additional thermal oxidation, electroless plating, and plasma spraying. The coated B₄C tile is inserted into the B₄C_p/Al7075 composite material using the liquid pressurization method. Interfacial energy, bonding strength, and impact resistance were measured to analyze the effect of the coating. All coatings enhanced interfacial energy, bonding strength, and impact resistance, and in particular, it was confirmed that the impact resistance increased by 86.8% when B₂O₃ coating was used. This study is significant in developing and analyzing a core surface treatment method that improves the performance of B₄C/Al series composites, which are attracting attention as next-generation lightweight amour and bulletproof materials.

• Restorative Dentistry and Endodontics
• /
• v.21 no.1
• /
• pp.321-338
• /
• 1996

The purpose of this study was to evaluate the effect of moistening and air-drying of acid conditioned dentin and enamel on the marginal microleakage. In this study, Class V cavity were prepared on both buccal and lingual surface of sixty extracted human premolars with cementum margin. These specimens were randomly devided into three groups and three dentin adhesives(Scotchbond Multi-Purpose, All bond 2, Prisma Universal Bond 3) were applied to each group. The specimens in each group were subdevided into four groups (Wet/primed, Dry/primed, Wet/not primed, Dry/not primed) and the etched dentin and enamel surface were treated these four surface treatments prior to the placement of a bonding agent or adhesive. Wet/primed group was simply blot-dried with a damp facial tissue before primer placement ; Dry/primed group was air dried for 30 seconds before the placement of a primer ; Wet/not primed group and Dry/not primed group were not primed after blot dried and air dried for 30 seconds each group. The bonding agent and composite resin were applied for each group. All specimens were exposed to 500 cycle of thermal stress. Specimens were placed in a silver nitrate solution and then sectioned buccolingually through the center of the restoration. The dye penetrations of the specimens were observed with a stereo microscope. The statistical test were applied to the results using a one way analysis variance (ANOVA) and Duncan's multiple range test. The aspects of silver ion penetration into the resin/dentin interface were examined under scanning electron microscopy. The results were as follows. 1. In all groups, the enamel margin showed significantly lower leakage value than the cementum margin (p<0.05). 2. Regardless of various surface treatment and dentin adhesives, there was no significant difference at the enamel margins (p>0.05). 3. At the dentin margins, the leakage values of Dry/not primed group showed significantly higher than that of the other groups (p<0.05). The leakage values of Wet/primed group showed significantly lower than that of the other groups, but, there was no significant difference between Wet group and Dry group. 4. There was no significantly difference between the dentin adhesives regarding the surface treatments in all groups(p>0.05). 5. On the backscatterd scanning electron microscopy observation, the penetration of the silver ion occured at the bonding resin/dentin interface. In the Wet/primed group, resindentin hybrid zone and resin penetration into the dentin was observed. The resin tags were compactively formed to a thickness of $3\sim4{\mu}m$ at the upper part of dentinal tubules. In the Dry/primed group, the thickness of the hybrid zone and the diameter, depth of the resin tags diminished. In the Non-primed groups, the hybrid zone was not identified and few resin tag was observed. There was the gap formation in the resin/dentin interface.

• Restorative Dentistry and Endodontics
• /
• v.25 no.2
• /
• pp.243-253
• /
• 2000

The purpose of this in vitro study was to evaluate dentin bonding by two different dentin bonding systems(DBS) using acetone based primer or adhesive [All Bond 2(AB2), One Step(OS)] when they were applied by wet or dry bonding technique. Morphology of resin-dentin interface and hybrid layer thickness(HLT) were investigated using Confocal Laser Scanning Microscope(CLSM) and compared to shear bond strength(SBS). 72 extracted sound human molars were randomly divided into 4 groups of 18 teeth each - Group 1.(AW); AB2 by wet bonding. Group 2(AD); AB2 by dry bonding. Group 3.(OW); OS by wet bonding, Group 4.(OD); OS by dry bonding. In 6 teeth of each group, notch-shaped class V cavities(depth 2mm) were prepared on buccal and lingual surface at the cementoenamel juction(12 cavities per group). To obtain color contrast in CLSM observation, bonding resins of each DBS were mixed with rhodamine B and primer of AB2 was mixed with sodium fluorescein. Prepared teeth of each group were treated with AB2, OS, respectively according to the manufacturer's instructions except for dentin surface moisture treatment after acid etching. In group 1 and 3, after acid etching, excess water was removed with wet tissue(Kimwipes), leaving consistently shiny, visibly hydrated dentin surface. In group 2 and 4, dentin surface was dried for 10 seconds at 1 inch distance. The treated teeth were then packed with composite resin(${\AE}$litefil) and light-cured. 12 microscopic samples($60{\sim}80{\mu}m$ thickness) of each group were obtained after longitudinal section and grinding(Exakt cutting and grinding system). Morphological investigation of resin-dentin interface and HLT measurement using CLSM were done. For measurement of SBS, remaining 12 teeth of each group were flattened occlusally to remove all enamel and grinded to 500 grit SiC(Pedemet Specimen Preparation Equipment). After applying DBS on the exposed dentin surface, composite resin was applied in the shape of cylinder, which has 5mm diameter, 1.5mm thickness, and light cured. SBS was measured using Instron with a crosshead speed of 0.5mm/min. It was concluded as follows, 1. HLT of AW(mean: $2.59{\mu}m$) was thicker than any other group, and followed by AD, OW, OD in descending order(mean; 2.37, 2.28, $1.92{\mu}m$). Only OD had statistically significant differences(p<0.05) to AW and AD. 2. There were intimate contact of resin and dentin at the interface in wet bonding groups, but gaps or irregular interfaces were observed in dry bonding groups. 3. The length, diameter, density of resin tags were various even in the same group without significant differences between groups and lots of adhesive lateral branches were observed. 4. There were no statistically significant difference of SBS between AB2 and OS, but SBS of wet bonding groups were significantly higher(p<0.05) than dry bonding groups. 5. There were no consistent relationships between HLT and SBS.

• The korean journal of orthodontics
• /
• v.28 no.5 s.70
• /
• pp.681-688
• /
• 1998

The purpose of this study was to evaluate the effects of the surface treatments of resin bases in indirect bracket bonding technique by study of shear bond strengths and failure patterns. Ninety metal brackets were bonded to the stone models of specimens involving bovine lower incisor with light-cured adhesive(Light-Bond). After removal of brackets with the resin base from the stone models, the surfaces of resin bases in thirty brackets were treated with Plastic Conditioner and the surfaces of resin bases in another thirty brackets were treated with sandblaster and the remaining thirty brackets were served as controls. All brackets were transferred to the specimens and bonded using sealant. The shear bond strength was tested on universal testing machine, and failure pattern was assessed with the adhesive remnant index(ARI). The results were as follows: 1. Surface treatments of resin bases with Plastic Conditioner or sandblasting showed statistically higher shear bond strengths than no treatment group. 2. No significant difference in shear bond strength was found between Plastic Conditioner treatment and sandblasting treatment groups. 3. No significant difference in ARI scores was found among the three groups. 4. As the result of correlation analysis between shear bond strengths and hnl scores, failure at adhesive/bracket base interface tends to increase when the shear bond strength was high, but it was not significant statistically. The above results suggest that improvement of bond strength can be obtained by surface treatment of resin base in the indirect bonding technique.

• Journal of the Korea Concrete Institute
• /
• v.14 no.1
• /
• pp.126-135
• /
• 2002

Plate bonding technique has been widely used in strengthening of existing concrete structures, although it has often a serious problem of premature falure such as interface separation and rip-off. However, this premature failure problem has not been well explored yet especially in view of local failure mechanism around the interface of plate ends. The purpose of the present study is, therefore, to identify the local failure of strengthened plates and to derive a separation criterion at the interface of plates. To this end, a comprehensive experimental program has been set up. The double lap pull-out tests considering pure shear force and half beam tests considering combined flexure-shear force were performed. The main experimental parameters include plate thickness, adhesive thickness, and plate end arrangement. The strains along the longitudinal direction of steel plates have been measured and the shear stress were calculated from those measures strains. The effects of plate thickness, bonded length, and plate end treatment have been also clarified from the present test results. Nonlinear finite element analysis has been performed and compared with test results. The Interface properties are also modeled to present the separation failure behavior of strengthened members. The cracking patterns as well as maximum failure loads agree well with test data. The relation between maximum shear and normal stresses at the interface has been derived to propose a separation failure criterion of strengthened members. The present study allows more realistic analysis and design of externally strengthened flexural member with steel plates.

• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.4
• /
• pp.35-38
• /
• 2003

Polymer light emitting diode (PLED) with an ITO/MEH-PPV/Al structure were prepared by spin coating method on the ITO (indium tin oxide)/glass substrates, using poly(2-methoxy-5-(2-ethylhexoxy)-1,4-phenylenevinylene (MEH-PPV) as the light emitting material. The dependence of heat treatment on the electrical and optical properties for the prepared PLED samples were investigated. The luminance decreased greatly from 630 cd/$\m^2$ to 280 cd/$\m^2$ at 10V input voltage as the heating temperature increased from $65^{\circ}C$ to $170^{\circ}C$. In addition, the luminance efficiency was found to be about 2 lm/W for the sample heat treated at $65^{\circ}C$. These results may be related to the interface roughness and/or the formation of an insulation layer, which is caused by the reaction between electrode and MEH-PPV organic luminescent film layer.