• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.5
• /
• pp.486-492
• /
• 1999

The purpose of this research was to find out what is the dominant factor determining the $H_{ex}$ and the $H_C$ of Mn-Ir/Ni-Fe multilayers with different buffer layers. Regardless of (111) texture of Mn-Ir layer, all samples showed over the $H_{ex}$ of 155 Oe. We found out the $H_{ex}$ and the $H_C$ of Mn-Ir/Ni-Fe multilayers depend on interface morphology and grain size of Mn-Ir layer at the interface between Mn-Ir and Ni-Fe layers. The dependence of magnetroesistance ratio and coupling field on the thickness of ferromagnetic layer, thickness of Cu layer and different buffer layers have been studied. Maximum magnetoresistance ratio appeared for the sample Ta(5 nm)/Mn-Ir(10 nm)/Ni-Fe(7.5 nm)/Cu(2 nm)/Ni-Fe(6 nm)/Ta(5 nm)/Si. Magnetoresistance ratio may be related to grain of ferromagnetic layer. Coupling field may be related to the roughness and the grain size of ferromagnetic layer in the spin-valve multilayers.

• Journal of Adhesion and Interface
• /
• v.9 no.1
• /
• pp.9-15
• /
• 2008

EVA foam was treated by oxygen plasma under a various treatment time for surface modification. The effect of plasma treatment on surface properties of EVA foam was investigated in terms of FT-IR ATR, XPS, contact angle, and SEM analysis and the adhesion characteristic of the EVA foam was studied in peel strength. As a results, EVA foam treated by plasma led to an elimination of organic compound, an increase of oxygen content, and an increase of surface roughness, resulting in improving the adhesion properties of the EVA foam. As the plasma treatment time increased, the hydrophilicity and physical change of surface of the EVA foam were increased and showed maximum value at 180 s and 420 s, respectively. The maximum adhesion strength appeared at plasma treatment time of 420 s and therefore, in this study the physical change was thought to be a major factor for improving the adhesion of the EVA foam.

• Journal of Surface Science and Engineering
• /
• v.37 no.5
• /
• pp.249-252
• /
• 2004

Effects of HA and TiN coating on the electrochemical characteristics of Ti-6AI-4V alloys for bone plates were investigated using various test methods. Ti-6AI-4V alloys were fabricated by using a vacuum induction furnace and bone plates were made by laser cutting and polishing. HA was made of extracted tooth sintered and then tooth ash was used as HA coating target. The TiN and HA film coating on the surface were carried on using electron-beam physical vapor deposition (EB-PVD) method. The corrosion behaviors of the samples were examined through potentiodynamic method in 0.9% NaCI solutions at $36.5\pm$$1^{\circ}C$ and corrosion surface was observed using SEM and XPS. The surface roughness of TiN coated bone plates was lower than that of tooth ash coated plates. The structure of TiN coated layer showed the columnar structure and tooth ash coated layer showed equiaxed and anisotrophic structure. The corrosion potential of the TiN coated specimen is comparatively high. The active current density of TiN and tooth ash coated alloy showed the range of about $1.0xl0^{-5}$ $A\textrm{cm}^2$, whereas that of the non-coated alloy was$ 1.0xl0^{-4}$ $A\textrm{cm}^2$. The active current densities of HA and TiN coated bone plates were smaller than that of non-coated bone plates in 0.9% NaCl solution. The pitting potential of TiN and HA coated alloy is more drastically increased than that of the non-coated alloy. The pit number and pit size of TiN and HA coated alloy decreased in compared with those of non-coated alloy. For the coated samples, corrosion resistance increased in the order of TiN coated, tooth ash coated, and non-coated alloy.

• Journal of Adhesion and Interface
• /
• v.4 no.4
• /
• pp.15-21
• /
• 2003

Polysulfone/organophilic layered silicate nanocomposites were prepared in the range of 0.25 to 9 wt% of organophilic-layered silicate by solution blend. Nano-hybridized films were cast from the blend solution. Exfoliation and intercalation of the polysulfone/organophiliclayered silicate nanocomposite films were confirmed by an X-ray diffractometer and a transmission electron microscope. Surface morphologies of polysulfone/organophilic layered silicate nanocomposite films were determined by a scanning electronic microscope and an atomic force microscope. When the organophilic layered silicate was added more than 1.5 wt%, the surface roughness (RMS) was rapidly increased because clusters of intercalated organophilic layered silicate particles existed on the polysulfone/organophilic-layered silicate film surface. Surface tension revealed an upward tendency over the contents of 1.5 wt% organophilic layered silicate in polysulfone/organophilic layered silicate nanocomposite. The change of surface morphology in polysulfone/organophilic layered silicate nanocomposite were affected by nano scale dispersed and intercalated organophilic layered silicate particles.

• Journal of Adhesion and Interface
• /
• v.22 no.1
• /
• pp.16-21
• /
• 2021

In the aircraft industry, anti- and de-icing are one of very important techniques for the safety. The anti-icing technique had not been studied while de-icing technique had been not only researched enough but applied to aircraft industry. In this work, surface roughness and energies of polyurethane (PU) topcoat were controlled with 3 different nanoparticles which was coated to PU topcoat. It was evaluated via static contact angle using distilled water. The adhesion property of 3 nanoparticles was evaluated directly using adhesion pull-off test. The color gamut of nanoparticle coated PU topcoat was also evaluated with 3 different nanoparticles. It was determined using RGB color degree variation between neat PU topcoat and coated nanoparticle. Finally, the optimized nanoparticle was determined to manufacture hydrophobic surface and to maintain color of neat PU topcoat for the aircraft.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05b
• /
• pp.90-93
• /
• 2002

In the surface pressure-area isotherms of mixed monolayers, mixtures containing as much as 30 mol% of AA form stable condensed monolayer while the monolayer without AA is in the expanded state because PVK take on 3D collapsed. All of the mixed monolayers with 0, 10, 20 and 30 mol% of AA could be readily transferred onto ITO substrate at 16, 17, 24 and 26 mN/m, respectively. The monolayer containing 30 mol% of AA, however, showed a roughness value of 28A and became homogeneous decreasing with the phase separation. We fabricated organic EL device of ITO/CuPc/MEL/BBOT/iLiF/Al using mixed monolayer of 13, 19 and 25 layer deposited by LB method as a emitting layer. In the voltage-current characteristics of EL device, current density was much smaller than that of the spin-coated devices. It may due to the large contact resistance existed at the interface of LB layer/organic layer inhibit carrier injection to the emitting layer. EL spectra of device showed peaks at 450. 470, 505, 555 and 650 nm and the white light emission indicate the CIE coordinate x=0.306, y=0.353.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.663-667
• /
• 2005

Surface modified carbon nanotubes were applied into the epoxy composites to investigate its tribological property. Carbon nanotubes reinforced epoxy composites were fabricated by casting. Effects to the tribological property of loading concentrations and types of surface modification of carbon nanotubes were investigated under sliding condition using linear reciprocal sliding wear tester. The results show that the small amount of carbon nanotubes into the epoxy exhibited lower weight loss than the pure epoxy. It is concluded that the effect of an enormous aspect ratio of carbon nanotubes surface area which wider than conventional fillers that react as interface for stress transfer. As increased the contents of carbon nanotubes, the weight loss from the wear test was reduced. And the surface modified carbon nanotubes show better tribological property than as produced carbon nanotubes. It is due that a surface modification of carbon nanotubes increases the interfacial bonding between carbon nanotubes and epoxy matrix through chemical bonding. Changes in worn surface morphology are also observed by optical microscope and SEM for investigating wear behaviors. Carbon nanotubes in the epoxy matrix near the surface are exposed, because it becomes the lubricating working film on the worn surface. It reduces the friction and results in the lower surface roughness morphology in the epoxy matrix as increasing the contents of the carbon nanotubes.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.3
• /
• pp.128-132
• /
• 2004

The perovskite ferroelectric materials of the PZT, SBT and BST series will attract much attention for application to ULSI devices. Among these materials, the BST ($Ba_0.6$$Sr_0.4$/$TiO_3$) is widely considered the most promising for use as an insulator in the capacitors of DRAMS beyond 1 Gbit and high density FRAMS. Especially, BST thin films have a good thermal-chemical stability, insulating effect and variety of Phases. However, BST thin films have problems of the aging effect and mismatch between the BST thin film and electrode. Also, due to the high defect density and surface roughness at grain boundarys and in the grains, which degrades the device performances. In order to overcome these weakness, we first applied the chemical mechanical polishing (CMP) process to the polishing of ferroelectric film in order to obtain a good planarity of electrode/ferroelectric film interface. BST ferroelectric film was fabricated by the sol-gel method. And then, we compared the surface characteristics before and after CMP process of BST films. We expect that our results will be useful promise of global planarization for FRAM application in the near future.

• Korean Journal of Materials Research
• /
• v.13 no.7
• /
• pp.460-464
• /
• 2003

Ni and Ti films were deposited by the thermal evaporator, and then annealed in the N$_2$ ambient at 300-80$0^{\circ}C$ in a RTA(rapid thermal annealing) system. Four point probe, AEM, FESEM, AES, and XPS were used to study the effects of Ti-capping layers on the thermal stability of NiSi thin films. The Ti-capped NiSi was stable up to $700^{\circ}C$ for 100 sec. RTA, while the uncapped NiSi layers showed high sheet resistance after $600^{\circ}C$. These results were due to that the Ni in-diffusion and Si out-diffusion were retarded by the capping layer, resulting in the suppression of the formation of NiSi$_2$and Si grains at the surface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.288-291
• /
• 2002

Application of metal silicides such as TiSi$_2$ and CoSi$_2$ as contacts and gate electrodes are being studied. However, TiSi$_2$ due to the linewidth-dependance, and CoSi$_2$ due to the excessive Si consumption during silicidation cannot be applied to the deep-submicron MOSFET device. NiSi shows no such problems and can be formed at the low temperature. But, NiSi shows thermal instability. In this investigation, NiSi was formed with a Ti-capping layer to improve the thermal stability. Ni and Ti films were deposited by the thermal evaporator. The samples were then annealed in the N$_2$ ambient at 300-800$^{\circ}C$ in a RTA (rapid thermal annealing) system. Four point probe, FESEM, and AES were used to study the thermal properties of Ti-capped NiSi layers. The Ti-capped NiSi was stable up to 700$^{\circ}C$ for 100 sec. RTA, while the uncapped NiSi layers showed high sheet resistance after 600$^{\circ}C$. The AES results revealed that the Ni diffusion further into the Si substrate was retarded by the capping layer, resulting in the suppression of agglomeration of NiSi films.