• 콘크리트학회논문집
• /
• 제11권3호
• /
• pp.101-111
• /
• 1999

Compared with the BF slag, the EAF slag has expansion due to the reaction with water and free CaO. Therefore it is specified in Concrete Specification that the FAP slag aggregated must not be used in concrete. Because of this reason it is unusual to use the EAF slag aggregate in concrete. The EAF slag aggregate treated with accelerated and water aging was comparatively satisfied with fundamental properties, which are specific gravity, unit weight, abrasion and immersion expansion ratio, as concrete aggregate. Therefore when we measured the compressive strength till 28 days, we found that the mortar and concrete replacing the natural aggregate with the EAF slag aggregate by 4 steps had better results than the concrete using the natural aggregate in a view of the compressive strength. But at 91 days, concrete using the EAF slag aggregate had no difference with it using the natural aggregate.

• Journal of the Korean Wood Science and Technology
• /
• 제34권5호
• /
• pp.52-58
• /
• 2006

Coffee chaff for manufacturing of the 6 mm thick cement-bonded boards was obtained from a coffee processing industry at Omuo-Ekiti, in Ekiti State, Nigeria. Boards were produced with three levels of cement to coffee chaff ratio of 1.5:1, 2.5:1 and 3.5:1; and at three levels of mixing curing reagent of 2.0%, 2.5% and 3.0%. Three dimensional properties of thickness swelling (TS), water absorption (WA) and linear expansion (LE) were investigated after 48 hours immersion in water. The mean values obtained for TS, WA and LE ranged from 0.46% to 1.47%, from 11.52% to 24.00%, from 0.19% to 0.35%, respectively. The most dimensionally stable boards were produced at the highest mixing levels of curing reagent and cement to coffee chaff ratio of 3.0% and 3.5:1, respectively. The coffee chaff is suitable as raw material for the manufacture of cement-bonded composites and it would be able to stimulate and activate the use of other agro-byproducts for the manufacture of value-added panels.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 봄 학술발표회 논문집
• /
• pp.613-618
• /
• 2002

Steel slag produced in steel making process is divided with electric arc furnace slag and converter slag. Compared with the blast furnace slag, converter slag has the expansibility due to the reaction with water and free CaO. Therefore it is specified in Standard Specification for Concrete in Korea that steel slag aggregate must not be used in concrete. In this study, we treat electric arc furnace slag aggregate(EAFSA) for concrete before and after several aging process to reduce expansibility. The fundamental properties are measured, which are specific gravity, unit weight, abrasion value and immersion expansion ratio, as concrete aggregate. To understand the suitability of EAFSA for concrete, we made the concrete with EAFSA and then determined the strength and the volume change in EAFSA concrete. From the results EAFSA treated with steam aging process has potentiality for concrete aggregate.

• 한국염색가공학회지
• /
• 제35권4호
• /
• pp.246-255
• /
• 2023

In this study, we investigated for natural rubber foam to replace petrochemical-based neoprene foam. Experiments were conducted on vulcanization system and 2-step foaming process of natural rubber. The vulcanization system were EV(Efficient Vulcanization Cure), Semi-EV(Semi-Efficient Vulcanization Cure) and CV(Conventional Vulcanization Cure). In the 2-step foaming process, first molding temperature was 140℃, times were 15, 20, 25, and 30minutes, and the second molding temperature was 160℃, the times 5, 10, 15, and 20minutes. The cure and viscosity characterization were evaluated by oscillating disc rheometer (ODR) and mooney viscosmeter. Various mechanical characteristics, including hardness, tensile strength, elongation at the point of rupture, and tear strength, were quantified. Subsequently, an assessment of alterations in these mechanical attributes was conducted post-immersion in a NaCl solution. In addition degree of volume change was measured after immersing the NR foam in NaCl solution and the low-temperature permanent compression set was evaluated at 4℃. And expansion ratio and shrinkage ratio of NR foam were evaluated for 28 days. As a result the EV vulcanization system showed the least change in physical properties before and after salt water immersion, and the lowest shrinkage ratio for 28 days. In addition it was confirmed that the 2-step foaming optimum condition differed depending on the appropriate vulcanization condition.

• 유기물자원화
• /
• 제12권4호
• /
• pp.95-104
• /
• 2004

본 연구에서는 가연성 건설폐기물 재활용의 일환으로, 폐발포폴리스티렌의 스티렌 용액에 가교제 및 개시제를 첨가하여 제조한 결합재와, 폐목재 칩을 이용하여, 폐목재-플라스틱 복합패널을 제조하였다. 전열 프레스를 이용하여 다양한 결합재량 및 충전재-결합재 비를 갖는 복합패널 공시체를 제조하였으며, 그 겉보기 밀도, 흡수율, 흡수에 의한 팽창률, 휨강도, 내수성 등에 관한 일련의 실험을 행하였다. 폐목재-플라스틱 복합패널의 겉보기밀도는 결합재량 및 충전재-결합재비의 증가에 따라 증대하며, 그 휨강도 및 습윤 휨강도는, 결합재량 35%, 충전재-결합재비 0.8에 있어서 최대치에 이른다. 흡수율 및 흡수에 의한 두께 팽창률은, 결합재량 및 충전재-결합재비의 증가에 따라 현저하게 감소한다. 결합재량 30%이상의 경우, 충전재-결합재비에 관계없이, 복합패널의 24h 상온 수중($20^{\circ}C$) 침지 및 2h 끓는 물중($100^{\circ}C$)＋1h상온 수중($20^{\circ}C$) 침지에 의한 휨강도의 감소는 거의 발생하지 않으며, 높은 내수성을 발현한다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제20권2호
• /
• pp.94-101
• /
• 2016

본 연구는 플라이애시 및 고로슬래그를 활용하여 알칼리 활성화 결합재로 제조된 모르타르 및 페이스트 샘플의 황산염 저항성을 평가하고 황산염 침투에 대한 고저항성 결합재를 제시하는 것이다. 이를 위하여 플라이애시 및 고로슬래그미분말 등의 광물질 혼화재를 결합재로 활용하여 고로슬래그미분말 치환율을 0, 30, 50 및 100%로 제작하였다. 규산나트륨 모듈 $Ms[SiO_2/Na_2O]$은 1.0, 1.5 및 2.0으로 조정하였으며, 초기 24시간 양생조건을 $23^{\circ}C$ 및 $70^{\circ}C$로 하고, 10% 황산나트륨 및 10% 황산마그네슘 용액에 각각 침지시키고, 황산염 저항성을 평가하기 위하여 압축강도, 질량변화율, 길이변화율 및 X선 회절분석을 측정하였다. 그 결과 고로슬래그미분말 치환량 및 Ms비가 증가할수록 재령 28일 압축강도 발현이 우수한 결과가 나타났다. 10% 황산나트륨에 침지한 경우에는 모든 시험조건에서 장기적인 강도발현과 질량 및 길이변화율이 작아 황산나트륨 침투에 대한 저항성이 우수한 것으로 나타났으나, 10% 황산마그네슘에 침지한 경우에는 장기적인 강도저하와 질량 및 길이변화가 크게 나타났으며, 그 경향은 고로슬래그미분말 치환량 및 Ms비가 증가할수록 현저하였다. 이것은 황산마그네슘의 경우 규산마그네슘수화물의 생성으로 인한 열화가 지배적으로 작용한 결과로 판단된다. 또한, X선 회절분석 결과 $MgSO_4$ 용액 침지에서의 알칼리 활성화 결합재의 팽창은 Gypsum($CaSO_4{\cdot}2H_2O$) 생성 반응에 의한 것으로 확인되었으며, 침지 6개월까지는 Gypsum의 생성이 지속적으로 증가되는 것을 알 수 있다.

• 한국수자원학회논문집
• /
• 제55권12호
• /
• pp.1065-1076
• /
• 2022

본 연구는 남강댐에서 대규모 선버들 군락의 확장과 고사가 수질에 미치는 영향을 파악하고자 하였다. 선버들 군락의 분포면적은 최초로 2003년에 0.12 km²였으나 2019년에는 3.58 km²로서 16 년 사이에 약 30 배로 급격하게 확장되었다. 그러나, 2013년에는 일부가 고탁도 장기 침수와 선버들 군락 내에서의 자기 솎음질(self-thining)에 의하여 분포면적이 0.17 km² 감소했다. 남강댐 저수지의 호소특성은 평균수심, 유역면적/호수 수면적 비, 체류시간, 회전율 및 성층화 등의 측면에서 호소형과 하천형이 복합적으로 나타났다. 호소수질에 대한 장기변동 특성을 분석한 결과, 대규모 선버들 군락지에서 COD, TP 및 엽록소 a 등이 남강댐 수역의 중앙부에 위치한 3 개 지점에 비하여 현저하게 크게 나타났다. 특히, 엽록소 a의 값이 남강댐 수질측정망 3 개 지점의 경향과 다르게 여름이 아닌 겨울에 최대값을 나타내는 것은 외부의 유입보다는 내부에서 발생된 것으로 사료된다. 이러한 남강댐 저수지에서 수질 악화의 한 가지 원인은 선버들 군락에서 낙엽, 가지 및 고사목 등 부산물의 분해과정에서 발생하는 막대한 양의 영양염류인 것으로 추정할 수 있다.