• 한국수소및신에너지학회논문집
• /
• 제13권3호
• /
• pp.224-232
• /
• 2002

CdS-$TiO_2$ nano-composite sol was prepared by the sol-gel method in organic solvents at room temperature and further hydrothermal treatment at various temperatures to control the physical properties of the primary particles. Again, CdS-$TiO_2$ composite particulate films were made by casting CdS-$TiO_2$ sols onto $F:SnO_2$ conducting glass and then heat-treatment at $400^{\circ}C$. Physical properties of these 61ms were further controlled by the surface treatment with $TiCl_4$, aqueous solution. The photo currents and hydrogen production rates measured under the experimental conditions varied according to the $CdS/[CdS+TiO_2]$ mole ratio and the mixed-sol preparation method. For $CdS-TiO_2$ composite sols prepared in IPA, CdS particles were homogeneously surrounded by $TiO_2$ particles. Also, the surface treatment with $TiCl_4$ aqueous solution caused a considerable improvement in the photocatalytic activity, probably as a result of close contacts between the primary particles by the etching effect of $TiCl_4$. It was found that the photoelectrochemical performance of these particulate films could be effectively enhanced by this approach.

• Korean Chemical Engineering Research
• /
• 제50권1호
• /
• pp.182-185
• /
• 2012

$TiCl_4$와 히드라진/암모니아수를 사용하여 졸겔 및 강알칼리 수열합성법의 신규 2단 합성법을 통해 N도핑된 $TiO_2$ 나노튜브를 제조하였다. 제조된 나노튜브는 튜브형상의 손상이 없이 10 nm 전후의 직경과 3 nm 이하의 벽두께를 가지며, 잘발달된 아나타제 결정상을 나타내었다. 또한 N이 도핑되어 일반 도핑되지 않은 $TiO_2$ 나노튜브와 아나타제상입자에 비해 각각 ~35 nm, ~25 nm 정도 적색편이 된 우수한 가시광 흡수능과 노란색 색상을 보여 주었다.

• Korean Chemical Engineering Research
• /
• 제48권6호
• /
• pp.684-689
• /
• 2010

본 연구에서는 다양한 구조 유도제로 합성된 SAPO촉매를 이용하여 자일로오스의 탈수화 반응을 진행하였다. 구조 유도제로는 테트라에틸암모늄수산화물(TEAOH), 디프로필아민(DPA), 디에틸아민(DEA), 몰포린(Morpholine) 그리고 디에탄올아민(DEtA)을 사용하였다. 촉매의 특성을 파악하기 위하여 질소 흡착-탈착 등온선, 암모니아 승온탈착($NH_3$-TPD), 그리고 승온산화분석(TPO)을 이용하였다. 구조 유도제로 몰포린(Morpholine)을 사용하여 제조한 SAPO-34를 촉매로 사용하였을 경우 사용한 촉매중에서 푸르푸랄 수율이 가장 높았다. 고체산 촉매의 외부 표면적과 산농도가 자일로오스의 탈수화 반응에 영향을 주는 것으로 나타났다.

• Korean Chemical Engineering Research
• /
• 제58권1호
• /
• pp.21-28
• /
• 2020

The stem extract from Pyrus serotina var has natural antioxidant ability, but the extraction method does not result in a soluble compound in cosmetic formulations. This study investigated the cosmetic efficacy of the Pyrus serotina var stem extract and its epidermis permeation ability when combined with polymer micelles and a cell penetrating peptide. The total concentration of polyphenol compounds was determined to be 103.1644 ± 1.38 mg/g in the ethanol extract and 78.97 ± 1.45 mg/g in the hydrothermal extract. The 2,2-diphenyl-1-picrylhydrazyl (DPPH) radical scavenging effects were 55.94 ± 0.22% in the ethanol extract at 1,000 mg/L. Superoxide dismutase (SOD) activity rates were 104.05 ± 3.28% in the ethanol extract at 62.5 mg/L. The elastase inhibition rate was 67.21 ± 2.72% in the ethanol extract at 1,000 mg/L. An antimicrobial effect was observed in the Propionibacterium acnes strain. In the epidermal permeability experiment, it was confirmed that formulation of the polymer micelle containing the Pyrus serotina var stem extract and cell penetrating peptide (R6, hexa-D-arginine) showed small particle size and much better skin permeability. The cumulative amount of total Pyrus serotina var stem extract that penetrated to the skin over time increased over 24 hours in three formulations. The three formulations showed 51.61 ㎍/㎠ (Formulation 0), 75.97 ㎍/㎠ (Formulation 1) and 95.23 ㎍/㎠ (Formulation 2) skin penetration, respectively. Therefore, it was confirmed that the ethanol extracts of Pyrus serotina var stem showed good cosmetic efficacy and excellent epidermis permeation ability when combined with a polymer micelle and cell penetrating peptide. Thus, this extract has the potential to be used as a safe and natural cosmetic material in the future.

• 한국재료학회지
• /
• 제20권8호
• /
• pp.418-422
• /
• 2010

As a starting material, BCP (biphasic calcium phosphate) nano powder was synthesized by a hydrothermal microwave-assisted process. A highly porous BCP scaffold was fabricated by the sponge replica method using 60 ppi (pore per inch) of polyurethane sponge. The BCP scaffold had interconnected pores ranging from $100\;{\mu}m$ to $1000\;{\mu}m$, which were similar to natural cancellous bone. To realize the antibacterial property, a microwave-assisted nano Ag spot coating process was used. The morphology and distribution of nano Ag particles were different depending on the coating conditions, such as concentration of the $AgNO_3$ solution, microwave irradiation times, etc. With an increased microwave irradiation time, the amount of coated nano Ag particles increased. The surface of the BCP scaffold was totally covered with nano Ag particles homogeneously at 20 seconds of microwave irradiation time when 0.6 g of $AgNO_3$ was used. With an increased amount of $AgNO_3$ and irradiation time, the size of the coated particles increased. Antibacterial activities of the solution extracted from the Ag-coated BCP scaffold were examined against gram-negative (Escherichia coli) and gram-positive bacteria (Staphylococcus aureus). When 0.6 g of $AgNO_3$ was used for coating the Ag-coated scaffold, it showed higher antibacterial activities than that of the Ag-coated scaffold using 0.8 g of $AgNO_3$.

• 한국축산식품학회지
• /
• 제39권6호
• /
• pp.903-917
• /
• 2019

This study aimed to extend the shelf-life of coffee-containing milk beverage by adding Theobroma cacao (cacao nibs) extract. To prepare the beverage sample containing cacao nibs extract, 0.8% cacao nibs hydrothermal extract was aseptically injected. Qualitative changes in the beverage samples, including antioxidant effect, peroxide value (POV), caffeine content, and sensory parameters were monitored regularly during storage at 10℃, 20℃, and 30℃ for 4 wk. The inclusion of cacao nibs extract produced higher antioxidant activity compared to the control. As the storage temperature increased, the POV of all samples increased. Samples with cacao nibs extract generally displayed lower POV than the control. The caffeine content of all samples tended to decrease during storage, with the decrease accentuated by higher storage temperatures. In the shelf-life prediction using the Arrhenius model, the kinetic regressions of the cacao nibs extract-added sample and control were Y_POV=1.2212X-2.1141 (r²=0.9713) and Y_POV=1.8075X-2.0189 (r²=0.9883), respectively. Finally, the predicted shelf-life of cacao nibs-added group and control to reach the quality limit (20 meq/kg POV) were approximately 18.11 and 12.18 wk, respectively. The results collectively indicate that the addition of cacao nibs extract extends the shelf-life of the coffee-containing milk beverage and heightened the antioxidant effect.

• 멤브레인
• /
• 제9권2호
• /
• pp.97-106
• /
• 1999

조성이 각각 1.9 ${SiO}_2$-1.5 $Na_2O-Al_2O_3-40$ $H_2O$인 반응물과 $SiO_2-0.13 Na_2O-52$ $H_2O$-0.12 TPAOH 인 반응물로부터 다공성 지지판에 성장된 A 형 및 ASM-5형 제올라이트 결정박막을 합성하여 X 선회절분석기와 주사전자현미경으로 마그이 특성을 검토하였다. 알루미나 지지상에 붙어 성장한 ZSM-5gtud 제올라이트 결정은 치밀하게 서로 붙은 상태였다. A형 제올라이트는 지지체상에 치밀한 결정막으로 성장시키기가 어려웠으며, 반응시간을 연장시키면 물의 분리가 어려운 P형의 제올라이트결정막으로 전환되었다. 반응물을 조제할 때, 물은 첨가하지 않은 채로 혼합하고 디스크형으로 가압성형하여 100$^{\cirt}C$에서; 결정화시키면 단시간에 lcalf하게 성장된 A형 제올라이트 결정막을 합성할 수 있었다. 제조한 다공성 무기막들이 물과 알코올의 혼합액으로부터 물을 투과증발시키는 특성을 각각 검토하였다. 막으로 결정화시킨 A형 제올라이트는 미세세공의 분자체기능을 통하여 물과 알코올의 혼합수용랙에서 물만을 선택적으로 투과시키는 것을 알 수 있었다.

• 한국광물학회지
• /
• 제4권2호
• /
• pp.129-140
• /
• 1991

Two illite polytypes, 2M1 and 1Md, have been identified from the sericite deposits of the Bobae mine, Kimhae, Kyungsangnam-do. Each polytype has characteristic grain size, chemical composition, and occurrence. 2M1 illite occurs predominantly in the sericitic alteration zone, while 1Md illite occurs predominantly in the propylitic alteration zone, implying that the former was formed in the higher temperature than the latter. Illites can be subdivided into two types based on their crystal sizes;(1) the $\mu\textrm{m}$-sized illite which is below 0.01mm(100$\mu\textrm{m}$) in size and consists of 2M1 and 1Md type, (2) the mm-sized illite which is above 0.01mm in size and consists only of 2M1 type. Especially illite below 1$\mu\textrm{m}$ is premominantly of 1Md type. Therefore, it seems likely that illite crystal size is to some extent related to the polytype. XRD data show that there is no interstratified layer in illites regardless of the crystal size and polytype. Activity of muscovite component of the $\mu\textrm{m}$-sized illite is 0.843 while that of the mm-sized illite is 0.790. However, the latter is more similar to muscovite in crystal structure than the former is. The mm-sized illite has less Al and more Kthan the $\mu\textrm{m}$-sized illite. In both illites, Si contents show a positive relation to octahedral Mg. Fluid inclusion study and mineral association show that the formation temperature of illite is $270-330^{\circ}C$. The major chemical processes leading to the formation of sericitic deposit as well as the alteration zones are the leaching of SiO2 from the country rock and the addition of Al2O3 and K2O into the sericitic ores.

• Journal of Industrial and Engineering Chemistry
• /
• 제68권
• /
• pp.14-23
• /
• 2018

$TiO_2-coated$ cubic ${\alpha}-Fe_2O_3$ with mostly exposed (012) and (101) facets (${\alpha}-Fe_2O_3@TiO_2$) was fabricated using a hydrothermal route for the photo-Fenton degradation of tetracycline under visible light irradiation. $TiO_2$ coating could greatly affect the photocatalytic activity of ${\alpha}-Fe_2O_3@TiO_2$. Compared with cubic ${\alpha}-Fe_2O_3$ alone for photodegradation of tetracycline, ${\alpha}-Fe_2O_3@TiO_2$ with $TiO_2$ shell of around 15 nm exhibited higher removal efficiency of tetracycline in photo-Fenton system, and its durability was slightly affected after five cycle times under same conditions. It is ascribed to the well-matched interface between cubic ${\alpha}-Fe_2O_3$ core and $TiO_2$ shell, leading to the broadened light-absorption and the efficient separation of photo-generated electon-hole pairs. The $^{\bullet}OH$ radicals were main responsible for the advanced photocatalytic performance of ${\alpha}-Fe_2O_3@TiO_2$ in visible-light driven degradation of tetracycline.

• Journal of Applied Biological Chemistry
• /
• 제62권3호
• /
• pp.305-313
• /
• 2019

남성의 클라이맥스 증후군, 남성갱년기, 또는 테스토스테론 결핍 증후군은 고령화시대 남성노인들의 건강에 새로운 문제 중 하나이다. 이 현상은 나이가 들수록 남성에게서 나타나는 자연현상으로 혈중 테스토스테론 수치의 감소와 신체적 및 정신적 활동의 현저한 감소를 특징으로 한다. 이 연구의 목적은 해면체내 일산화질소(NO)와 혈액 내 남성호르몬의 수준을 비교하여 포공영(Taraxacum coreanum) 열수 추출물의 효과를 조사하였다. 포공영 추출물은 생체외 및 생체내에서 NO 생산량을 용량 의존적으로 증가시켰다. 포고영 추출물을 4 주간 섭취 한 나이든 쥐(22주)에서 다이하이드로 테스토스테론과 17-하이드록시 스테로이드 탈수소효소의 수준과 신경 인산화 질소 합성효소와 cGMP의 양은 유의하게 증가했다. 그러나 프로스타글란딘$E_2$, 테스토스테론 및 성 호르몬 결합 글로불린 수치는 모든 군에서 차이가 없었다. 또한, 총 정자 수 및 운동성 정자 수 또한 유의한 차이가 없었다. 전반적으로, 이러한 결과는 NO, cGMP 및 유리 테스토스테론을 향상시키기 위한 안전하고 효과적인 천연물질로서 Taraxacum coreanum 추출물의 가능성을 시사한다.