• Title/Summary/Keyword: hydrophilic chain

Search Result 87, Processing Time 0.027 seconds

The Synthesis of One-step Type Hydrophilic Non-porous Polyurethane Resin and the Physical Property of its Coated Fabric for the Garment (One-step형 친수무공형 폴리우레탄 수지 합성과 코팅 처리한 의류용 직물의 물성)

  • Yang, Sung-Yong;Kim, Hyun-Ah;Kim, Seung-Jin
    • Textile Coloration and Finishing
    • /
    • v.23 no.2
    • /
    • pp.131-139
    • /
    • 2011
  • This study surveyed on the synthesis of one-step type hydrophilic non-porous PU resin and the physical property of the coated fabric for the garment. Three kinds of chain extender such as MEG, 1,4-BD and NPG were used for the preparation of one-step type hydrophilic non-porous PU resin in order to examine the effect of chain extender on the physical properties of PU-coated fabric. And the effects of isocyanate on the physical properties of PU coated fabric were surveyed by mixing with various TDI and MDI ratios. In addition, the physical properties of the coated fabric treated with one-step type hydrophilic non-porous PU resin were examined according to the pre-treatment conditions such as cire finishing. Finally, the washing durability of the coated fabrics was assessed. The coated fabrics treated with PU resin synthesized with PEG1000, MEG and TDI/MDI (6/4) showed the best physical properties. Considering the pre-treatment conditions, best performance of hydraulic pressure, water vapor permeability, and water repellency were obtained with top roller rotation ratio of 150% under 50 ton pressure at $170^{\circ}C$.

Synthesis of New Semisynthetic Analogs of Epi-xanthatin by Modification of the Side Chain and Their Cytotoxic Activity (Epi-xanthatin의 Side Chain 변환을 통한 새로운 반합성 유도체들의 합성 및 세포독성)

  • Baek Du-Jong;Ahn Jong-Woong;Lee Chongock
    • YAKHAK HOEJI
    • /
    • v.49 no.1
    • /
    • pp.68-73
    • /
    • 2005
  • Epi-xanthatin analogs containing hydrophilic substituents such as carboxylic acid, alcohol, morpholine, amino acid, and glucose derivatives were synthesized and their in vitro cytotoxicity and in vivo antitumor activity were evaluated. The target compounds were generally cytotoxic against tumor cell lines of human origin with $ED_{50}$ values of $0.1{\sim}30{\mu}g/ml$, except the highly hydrophilic analog 6 containing aspartic acid. Contrary to the potent cytotoxicity weakly hydrophilic analogs 2 and 8 were not active in vivo, or even toxic to the test animals. As a result, hydrophilic analog of epi-xanthatin did not show in vitro cytotoxicity and hydrophobic analogs did not show in vivo antitumor activity, thus it is presumed that amphiphilic analogs or those with medium hydrophilicity would exhibit the antitumor potency in vivo.

Dielectric Property of Hydrophilic Copolymer Thin Films (친수성 고분자 박막의 유전 특성)

  • Choi, Seung-Ryul;Im, Kyung-Jin;Kim, Jun-Young
    • Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
    • /
    • 2007.06a
    • /
    • pp.229-229
    • /
    • 2007
  • In this study, HEMA-based hydrophilic copolymers were synthesized and dielectric constant (K) of the polymer thin films were investigated by change hydroxyl group (-OH) ratio in the polymer chain. The different hydroxyl group ratios were characterized by FT-IR and its thin films were obtained by spin coating. As a result, due to the moisture absorption of the hydrophilic thin film, the dielectric constant has been increased as was expected. The highest dielectric constant (K=4.19, @1MHz) was observed at 40% hydroxyl group ratio among the several polymers.

  • PDF

The Organization of Nanoporous Structure Using Controlled Micelle Size from MPEG-b-PDLLA Block Copolymers

  • Chang, Jeong-Ho;Kim, Kyung-Ja;Shin, Young-Kook
    • Bulletin of the Korean Chemical Society
    • /
    • v.25 no.3
    • /
    • pp.351-356
    • /
    • 2004
  • Selected MPEG-b-PDLLA block copolymers have been synthesized by ring-opening polymerization with systematic variation of the chain lengths of the resident hydrophilic and hydrophobic blocks. The size and shape of the micelles that spontaneously form in solution are then controlled by the characteristics of the block copolymer template. All the materials prepared in this study showed the tunable pore size of 20-80 ${\AA}$ with the increase of hydrophobic chain lengths and up to 660 $m^2$/g of specific surface area. The formation mechanism of these nanoporous structures obtained by controlling the micelle size has been confirmed using both liquid and solid state $^{13}C\;and\;^{29}Si$ NMR techniques. This work verifies the formation mechanism of nanoporous structures in which the pore size and wall thickness are closely dependent on the size of hydrophobic cores and hydrophilic shells of the block copolymer templates.

Synthesis and Microphase Separation of Biodegradable Poly($\varepsilon$-caprolactone)-Poly(ethylene glycol)-Poly($\varepsilon$-caprolactone) Multiblock Copolymer Films

  • You, Jae-Ho;Choi, Sung-Wook;Kim, Jung-Hyun;Kwak, Young-Tae
    • Macromolecular Research
    • /
    • v.16 no.7
    • /
    • pp.609-613
    • /
    • 2008
  • Poly($\varepsilon$-caprolactone)-poly(ethylene glycol)-poly($\varepsilon$-caprolactone) (PCL-PEG-PCL) multiblock copolymers at various hydrophobic-hydrophilic ratios were successfully synthesized by the chain extension of triblock copolymers through isocyanate (hexamethylene diisocyanate). Biodegradable films were prepared from the resulting multiblock copolymers using the casting method. The mechanical properties of the films were improved by chain extension of the triblock copolymers, whereas the films prepared by the triblock copolymers were weak and brittle. Atomic force microscopy (AFM) of the multiblock copolymer film showed that the hydrophilic PEG had segregated on the film surface. This is consistent with the observed contact angle of the films.

The effect of the structure of each component on the o/w microemulsion droplet size and stability

  • Changgui Han;You
    • Journal of the Society of Cosmetic Scientists of Korea
    • /
    • v.22 no.2
    • /
    • pp.20-40
    • /
    • 1996
  • The oil in water type ME of 4 component system was composed with POE monoalkyl ether and POE sorbitan monoalkyl ester as surfactant, saturated hydrocarbon, side chain structure and aromatic structure as oil, and glycerine as cosurfactant using high pressure homogenizer. The objective of this study was to examine the role of surfactant and oil structure on droplet size and stability. The experimental results showed that the droplet size was smaller with bigger polarity of oil, less hydrocarbon, longer hydrophilic chain of surfactant and higher concentration of glycerine. SQ and LP systems showed very stable but AB and ISB system unstable microemulsion.

  • PDF

The Synthesis and Evaluation of Pendant Oligosaccharide-Lipid Side Chain Copolymer

  • Nam, Hye-Sung;Kim, Hyun-Joo;Nam, Kwang-Woo;Chung, Dong-June
    • Macromolecular Research
    • /
    • v.11 no.2
    • /
    • pp.115-121
    • /
    • 2003
  • In this research, the in vitro anti-thrombogenecity of artificial materials was evaluated using hydrophilic/hydrophobic copolymers containing oiligosaccharide as hydrophilic moiety and phospholipid as hydrophobic moiety respectively. N-(p-vinylbenzyl)-[O-$\alpha$-D-glucopyranosyl-(1longrightarrow4)]$_{n-1}$-D-glucoamide(VM7A) was (VM7 A) was adopted as hydrophilic oligosaccharide and 2-acryloxybutyl-2-(triethylammonium)ethyl phosphoric acid (HBA-choline) was adopted as hydrophobic phospholipid. Copolymers having various monomer feeding molar ratios were synthesized through radical polymerization. The synthesized copolymers were identified using FT-IR, $^1$H-NMR, XPS, and DSC. The surface energy of the copolymers were evaluated by dynamic contact angle (DCA) method and checked different roles of VM7A as hydrophilic moiety and HBA-choline as hydrophobic moiety on surface. The surface morphological differences between hydrated and unhydrated surfaces of copolymers were observed and evaluated using Am. The platelets were separated from canine whole blood by centrifugation and adopted to the anti-thromobogenecity test of the copolymers. From the results, we find out that as VM7A ratio increases, so did anti-thrombogenecity. Such results show the possibility of using these copolymers as blood compatible materials in living body.y.

Hydrophilic surface formation of polumer treated by ion assisted reaction and its applications (이온빔보조 반응법을 이용한 고분자 표면의 친수성처리와 그 응용)

  • Cho, J.;Choi, S. C.;Yun, K.H.;Koh, S. K.
    • Journal of the Korean Vacuum Society
    • /
    • v.8 no.3B
    • /
    • pp.262-268
    • /
    • 1999
  • Polycarbonate (PC) and Polymethylmethacrylate (PMMA) surface was modified by ion assisted reaction (IAR) technique to obtain the hydrophilic functional groups and improve the wettability. In conditions of ion assisted reaction, ion beam energy was changed from 500 to 1500eV, and ion dose and oxygen gas blown rate were fixed $1\times10^{16}$ ions/$\textrm{cm}^2$ and 4ml/min, respectively. Wetting angle of water on PC and PMMA surface modified by $Ar^+$ ion without blowing oxygen at 4ml/mon showed $5^{\circ}$ and $10^{\circ}$. Changes of wetting angle with oxygen gas and $Ar^+$ ion irradiation were explained by considering formation of hydrophilic group due to a reaction between irradiated polymer chain by energetic ion irradiation and blown oxygen gas. X-ray photoelectron spectroscopy analysis shows that hydrophilic groups such as -C-O, -(C=O)- and -(C=O)-O- are formed on the surface of polymer by chemical interaction. The polymer surface modification using ion assisted reaction only changed the surface physical properties and sept the bulk properties. In comparison with other modification methods, the surface modification by IAR treatment was chemically stable and enhanced the adhesion between metal and polymer surface. The applications of various kinds of polymer surface modification methods, metal and polymer surface. The applications of various kinds of polymer surface modification could be appled to the new materials about hydrophilic surface properties by IAR treatment. The adhesion between metal film and polymer measured by Scotch tape test whether the hydrophilic surfaces could improve the adhesion strength or not.

  • PDF

Fates of water and salts in non-aqueous solvents for directional solvent extraction desalination: Effects of chemical structures of the solvents

  • Choi, Ohkyung;Kim, Minsup;Cho, Art E.;Choi, Young Chul;Kim, Gyu Dong;Kim, Dooil;Lee, Jae Woo
    • Membrane and Water Treatment
    • /
    • v.10 no.3
    • /
    • pp.207-212
    • /
    • 2019
  • Non-aqueous solvents (NASs) are generally known to be barely miscible, and reactive with polar compounds, such as water. However, water can interact with some NASs, which can be used as a new means for water recovery from saline water. This study explored the fate of water and salt in NAS, when saline water is mixed with NAS. Three amine solvents were selected as NAS. They had the same molecular formula, but were differentiated by their molecular structures, as follows: 1) NAS 'A' having the hydrophilic group ($NH_2$) at the end of the straight carbon chain, 2) NAS 'B' with symmetrical structure and having the hydrophilic group (NH) at the middle of the straight carbon chain, 3) NAS 'C' having the hydrophilic group ($NH_2$) at the end of the straight carbon chain but possessing a hydrophobic ethyl branch in the middle of the structure. In batch experiments, 0.5 M NaCl water was blended with NASs, and then water and salt content in the NAS were individually measured. Water absorption efficiencies by NAS 'B' and 'C' were 3.8 and 10.7%, respectively. However, salt rejection efficiency was 98.9% and 58.2%, respectively. NAS 'A' exhibited a higher water absorption efficiency of 35.6%, despite a worse salt rejection efficiency of 24.7%. Molecular dynamic (MD) simulation showed the different interactions of water and salts with each NAS. NAS 'A' formed lattice structured clusters, with the hydrophilic group located outside, and captured a large numbers of water molecules, together with salt ions, inside the cluster pockets. NAS 'B' formed a planar-shaped cluster, where only some water molecules, but no salt ions, migrated to the NAS cluster. NAS 'C', with an ethyl group branch, formed a cluster shaped similarly to that of 'B'; however, the boundary surface of the cluster looked higher than that of 'C', due to the branch structure in solvent. The MD simulation was helpful for understanding the experimental results for water absorption and salt rejection, by demonstrating the various interactions between water molecules and the salts, with the different NAS types.

Solution Properties of Polyglycerol Alkyl Ether Nonionic Surfactant (폴리글리세롤을 친수성기로한 비이온성 계면활성제의 용액성)

  • Yun, Y.K.;Nam, K.D.;Kang, T.J.
    • Journal of the Korean Applied Science and Technology
    • /
    • v.9 no.2
    • /
    • pp.107-117
    • /
    • 1992
  • The synthesis and solution properties of polyglycerol alkyl ether($R_{12}Gn$) are described. The phase behavior, surface tension, cloud point and HLB value of polyglycerol dodecyl ether in aqueous solution and in mixed solution of surfactant /water /oil have been investigated and compared with values of polyoxyethylene dodecyl ether. The surface tension showed that $R_{12}Gn$ have sufficiently low values of surface tension and cmc to serve as useful polyoxyethylene alkyl ether. The mesophases appearing in the $R_{12}Gn$ systems were more stable in a high temperature range than the mesophases of polyoxyethylene alkyl ether systems. The cloud point and HLB data indicated that addition of one glycerol group was equivalent to the addition of three oxyethylene group units, as far as the hydrophilic property was concerned. The phase diagrams of the polyglycerol alkyl ether /dodecane /water systems showed that the solubilizing and emulsifying powers of $R_{12}Gn$ were greater than those of polyoxyethylene alkyl ether. It is concluded that the polyglycerol chain can be even more useful as hydrophilic group of nonionic surfactants than the polyoxyethylene chain.