• Transactions on Electrical and Electronic Materials
• /
• v.7 no.3
• /
• pp.118-122
• /
• 2006

Diamond-like carbon (DLC) films were prepared on silicon substrates by the RF PECVD (Plasma Enhanced Chemical Vapor Deposition) method using methane $(CH_4)$ and hydrogen $(H_2)$ gas. We examined the effects of the post annealing temperature on the tribological properties of the DLC films using friction force microscopy (FFM). The films were annealed at various temperatures ranging from 300 to $900^{\circ}C$ in steps of $200^{\circ}C$ using RTA equipment in nitrogen ambient. The thickness of the film was observed by scanning electron microscopy (SEM) and surface profile analysis. The surface morphology and surface energy of the films were examined using atomic force microscopy and contact angle measurement, respectively. The hardness of the DLC film was measured as a function of the post annealing temperature using a nano-indenter. The tribological characteristics were investigated by atomic force microscopy in FFM mode.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.25-27
• /
• 2007

$Eu^{2+}$-doped $Ca_2Si_5N_8$ was grown on Si(100) substrate using metal-organic deposition (MOD) method and post-annealed at $900^{\circ}C$ in various atmosphere. Luminescence properties of these thin films were investigated with variations of $Eu^{2+}$-doped concentrations and annealing atmosphere. Thin film was formed with clean surface and uniform thickness of about 72 nm. From the measurements of luminescence properties of thin films, film must be post-annealed in nitrogen or mixture of nitrogen and hydrogen atmosphere to emit a sufficient light. For $Ca_{1.5}Eu_{0.5}Si_5N_8$ thin film annealed at $900^{\circ}C$ in nitrogen atmosphere, excitation band from 380 to 420 nm was detected with the maximum intensity at 404 nm and two broad emission bands from 530 to 630 nm were observed. These broad excitation and emission bands must be attributed to the nitrogen incorporations into the films. From the results, $Ca_{2-x}Eu_xSi_5N_8$ thin film has probability for next generation thin film lighting applications such as light emitting diode (LED) or electro-luminescence (EL).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.1033-1036
• /
• 2004

Si nanocrystallites thin films on p-type (100) Si substrate have been fabricated by pulsed laser deposition using a Nd:YAG laser. After deposition, samples were annealed at the temperatures of 400 to $800^{\circ}C$. Hydrogen passivation was then performed in the forming gas (95% $N_2$ + 5% $H_2$) for 1 hr. Strong violet-indigo photoluminescence has been observed at room temperature from nitrogen ambient-annealed Si nanocrystallites. The variation of photoluminescence (PL) Properties of Si nanocrystallites thin films has been investigated depending on annealing temperatures with hydrogen passivation. From the results of PL, Fourier transform infrared (FTIR), and high-resolution transmission electron microscopy (HRTEM) measurements, it is observed that the origin of violet-indigo PL from the nanocrystalline silicon in the silicon oxide film is related to the quantum size effect of Si nanocrystallites and oxygen vacancies in the SiOx(x : 1.6-1.8) matrix affects the emission intensity.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.04a
• /
• pp.88-91
• /
• 2003

Si nanocrystallites thin films have been fabricated by pulsed laser deposition using a Nd:YAG laser. After deposition, samples were annealed at the temperature range of 400 to $800^{\circ}C$. Hydrogen passivation was then performed in the forming gas ($95%N_{2}+5%H_{2}$) at $500^{\circ}C$. Strong violet-indigo photoluminescence has been observed at room temperature on nitrogen ambient-annealed Si nanocrystallites. As a result of photoluminescence spectra and infrared absorption spectra, we conclude that the violet-indigo PL efficiency is related with oxygen vacancy in the $SiO_x$(x= 1.6-1.8) matrix.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.122-122
• /
• 2008

Recently, Metal/Alumina/Silicon-Nitride/Silicon-Oxide/Silicon (MANOS) structures are one of the most attractive candidates to realize vertical scaling of high-density NAND flash memory [1]. However, as ANO layers are miniaturized, negative and positive bias temperature instability (NBTI/PBTI), such as the flat band voltage shift, ${\Delta}V_{FB}$, the interfacial trap density increase, ${\Delta}D_{it}$, the gate leakage current, ${\Delta}I_G$. and the retention characteristics, in MONOS capacitors, becomes an important issue in terms of reliability. It is well known that tunnel oxide degradation is a result of the oxide and interfacial traps generation during FN (Fowler-Nordheim) stress [2]. Because the bias temperature stress causes an increase of both interfacial-traps and fixed oxide charge could be a factor, witch can degrade device reliability during the program and erase operation. However, few studies on NBTI/PBTI have been conducted on improving the reliability of MONOS devices. In this work, we investigate the effect of post-annealing gas on bias temperature instability (BTI), such as the flat band voltage shift, ${\Delta}V_{FB}$, the interfacial trap density shift, ${\Delta}I_G$ retention characteristics, and the gate leakage current characteristics of MANOS capacitors. MANOS samples annealed at $950^{\circ}C$ for 30 s by a rapid thermal process were treated via additional annealing in a furnace, using annealing gases $N_2$ and $N_2-H_2$ (2 % hydrogen and 98 % nitrogen mixture gases) at $450^{\circ}C$ for 30 min. MANOS samples annealed in $N_2-H_2$ ambient had the lowest flat band voltage shift, ${\Delta}V_{FB}$ = 1.09/0.63 V at the program/erase state, and the good retention characteristics, 123/84 mV/decade at the program/erase state more than the sample annealed at $N_2$ ambient.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.430.1-430.1
• /
• 2016

We present the concept of reducible fugitive material that conformally surrounds core Cu nanowire (NW) to fabricate transparent conducting electrode (TCE). Reducing atmosphere can corrodes/erodes the underlying/surrounding layers and might cause undesirable reactions such impurity doing and contamination, so that hydrogen-/forming gas based annealing is impractical to make device. In this regards, we introduce novel reducible shell conformally surrounding indivial CuNW to provide a protection against the oxidation when exposed to both air and solvent. Uniform copper lactate shell formation is readily achievable by injecting lactic acid to the CuNW dispersion as the acid reacts with the surface oxide/hydroxide or pure copper. Cu lactate shell prevents the core CuNW from the oxidation during the storage and/or film formation, so that the core-shell CuNW maintains without signficant oxidation for long time. Upon simple thermal annealing under vacuum or in nitrogen atmosphere, the Cu lactate shell is easily decomposed to pure Cu, providing an effective way to produce pure CuNW network TCE with typically sheet resistance of $19.8{\Omega}/sq$ and optical transmittance of 85.5% at 550 nm. Our reducible copper lactate core-shell Cu nanowires have the great advantage in fabrication of device such as composite transparent electrodes or solar cells.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.1
• /
• pp.92-96
• /
• 2009

A new precursor [$Zr(acac)_{3}(H_{2}O)_{2}$] was synthesized by Sonochemical technique and used to deposit thin $ZrO_{2}$ film on quartz and ceramic substrate via ultrasonic aerosol assisted chemical vapour deposition (UAACVD) at 300 ${^{\circ}C}$ in oxygen environment followed by annealing of the sample for 2-3 minutes at 500 ${^{\circ}C}$ in nitrogen ambient. The molecular structure of the precursor determined by single crystal X-ray analysis revealed that the molecules are linked through intermolecular hydrogen bonds forming pseudo six and eight membered rings. DSC and TGA/FTIR techniques were used to determine thermal behavior and decomposition temperature of the precursor and nature of evolved gas products. The optical measurement of annealed $ZrO_{2}$ film with tetragonal phase shows optical energy band gap of 5.01 eV. The particle size, morphology, surface structure and composition of deposited films were investigated by XRD, SEM and EDX.

• Journal of the Korean Vacuum Society
• /
• v.19 no.1
• /
• pp.58-65
• /
• 2010

AlN thin films were deposited on sapphire substrates and ZnO templates by rf-magnetron sputtering. Powder-sintered AlN target was adopted for source material. Thickness of AlN layer was linearly dependent on plasma power from 50 to 110 W, and it decreased slightly when working pressure increased from 3 to 10 mTorr due to short mean free path of source material sputtered from AlN target by Ar working gas. When $N_2$ gas was mixed with Ar, the thickness of AlN layer decreased significantly because of low sputter yield of nitrogen. AlN layer was also deposited on ZnO template. However, it showed weak thermal stability that the interface between AlN and ZnO was deteriorated by rapid thermal annealing treatment above $700^{\circ}C$. In addition, ZnO layer was largely attacked by MOCVD ambient gas of hydrogen and ammonia around $700^{\circ}C$ through inferior AlN layer deposited by sputtering. And AlN layers were fully peeled off above $900^{\circ}C$.