• Applied Chemistry for Engineering
• /
• v.25 no.2
• /
• pp.204-208
• /
• 2014

This study investigated the effect of hydrogen permeance and selectivity, catalyst amount, $H_2O/CO$ ratio in a feed stream, and Ar sweep gas on the performance of a water gas shift reaction in a membrane reactor. It was observed that a minimum hydrogen selectivity of 100 was needed in a membrane reactor to obtain a hydrogen yield higher than the one at equilibrium and the hydrogen yield enhancement gradually decreased as the hydrogen permeance increased. The CO conversion in a membrane reactor initially increased with the catalyst amount and reached a plateau later for a membrane reactor with a low hydrogen permeance while the high CO conversion independent of a catalyst amount was observed for a membrane reactor with a high hydrogen permeance. For the $H_2O/CO$ ratio in a feed stream higher than 1.5, a hydrogen permeance had little effect on the CO conversion in a membrane reactor and it was found that a minimum Ar molar flow rate of $6.7{\times}10^{-6}mol\;s^{-1}$ was needed to achieve the CO conversion higher than the one at equilibrium in a membrane reactor.

• Membrane Journal
• /
• v.31 no.6
• /
• pp.456-470
• /
• 2021

In this study, polyetherimide-based hollow fiber membranes were manufactured using the NIPS (nonsolvent induced phase separation) method. THF, Ethanol, and LiNO₃ were used as additives to control the morphology of the PEI-hollow fiber membranes. Furthermore, for the development of a high hydrogen separation membrane, the spinning conditions were optimized through the characterization of SEM and gas permeance. As a result, as the content of THF increased, the hydrogen/carbon dioxide selectivity increased. However, the permeance decreased due to the trade-off relationship. When ethanol was added, a finger-like structure was shown, and when LiNO₃ was added, a sponge structure was shown. In particular, in the case of a hollow fiber membrane with an optimized PDMS coating layer, the permeance was 40 GPU and the hydrogen/carbon dioxide selectivity was 5.6.

• Clean Technology
• /
• v.20 no.4
• /
• pp.425-432
• /
• 2014

The effect of two important parameters of a catalytic membrane reactor (CMR), hydrogen selectivity and hydrogen permeance, coupled with an Ar sweep flow and an operating pressure on the performance of a water gas shift reaction in a CMR has been extensively studied using a one-dimensional reactor model and reaction kinetics. As an alternative pre-combustion $CO_2$ capture method, the feasibility of capturing a pressurized and concentrated $CO_2$ in a retentate (a shell side of a CMR) and separating a purified $H_2$ in a permeate (a tube side of a CMR) simultaneously in a CMR was examined and a guideline for a hydrogen permeance, a hydrogen selectivity, an Ar sweep flow rate, and an operating pressure to achieve a simultaneous capture of a concentrate $CO_2$ in a retentate and production of a purified $H_2$ in a permeate is presented. For example, with an operating pressure of 8 atm and Ar sweep gas for rate of $6.7{\times}10^{-4}mols^{-1}$, a concentrated $CO_2$ in a retentate (~90%) and a purified $H_2$ in a permeate (~100%) was simultaneously obtained in a CMR fitted with a membrane with hydrogen permeance of $1{\times}10^{-8}molm^{-2}s^{-1}Pa^{-1}$ and a hydrogen selectivity of 10000.

• Journal of Environmental Science International
• /
• v.7 no.5
• /
• pp.669-677
• /
• 1998

A porous $\alpha$-alumina tube of 2.5 mm O.D. and 1.9 mm I.D. was used as the support of an inorganic membrane. Macropores of the tube, about 150 nm in size, were plugged with silica formed by thermal decomposition of tetraethylorthosilicate at $600^{\circ}C$. The forced cross-flow CVD method that reactant was evacuated through the porous wall of the support was very effective in plugging macropores. The H$_2$ permeance of the prepared membrane was of the order of $10^{-8}/ molㆍs^{-1}/ㆍm^{-2}/. Pa{-1}$/, while the $N_2$ permeance was below $10^{-11}/ molㆍs^{-1}/ㆍm^{-2}/ㆍPa^{-1}$/ at $600^{\circ}C$. This was comparable to that of silica-modified Vycor glass whose size was 4 nm.

• Membrane Journal
• /
• v.20 no.3
• /
• pp.210-216
• /
• 2010

The hydrogen permselective membrane were prepared by chemical vapor deposition (CVD) aiming at the applications to hydrogen iodide decomposition in the thermochemical IS process, and it was evaluated for the possibility as a separation membrane. An electron probe X-ray microanalyzer (EPMA) and SEM picture were used to analyze the morphology and structure of the prepared membranes. It was confirmed that Zr-Si-O layer exist in the surface of the prepared membrane using zirconia coated support. Single-component permeance to $H_2$ and $N_2$ were measured at $300{\sim}600^{\circ}C$. Hydrogen permeance through the Z-1 membrane at a permeation temperature of $600^{\circ}C$ was about $1{\times}10^{-7}\;mol{\cdot}Pa^{-1}{\cdot}m^{-2}{\cdot}s^{-1}$. The selectivities of $H_2/N_2$ at $600^{\circ}C$ were 5.0 and 5.75 for Z-1 and Z-2 membrane, respectively.

• Journal of the Korean institute of surface engineering
• /
• v.37 no.5
• /
• pp.243-248
• /
• 2004

A palladium-nikel(Pd-Ni) alloy composite membrane has been fabricated on microporous nickel support formed with nickel powder. Plasma surface treatment process is introduced as pre-treatment process instead of HCI activation. Pd coating layer was prepared by dc magnetron sputtering deposition after $H_2$ plasma surface treatment. Palladium-nickel alloy composite layer had a fairly uniform and dense surface morphology. The membrane was characterized by permeation experiments with hydrogen and nitrogen gases at temperature of 773 K and pressure of 2.2psi. The hydrogen permeance was 6 ml/minㆍ$\textrm{cm}^2$ㆍatm and the selectivity was 120 for hydrogen/nitrogen($H_2$/$N_2$) mixing gases at 773 K.

• Journal of the Korean institute of surface engineering
• /
• v.37 no.5
• /
• pp.289-295
• /
• 2004

A dense palladium-nikel (Pd-Ni) alloy composite membrane has been fabricated on microporous nickel support mixed with submicron/micron nickel powder instead of mesoporous stainless steel support. Plasma treatment process is introduced as pre-treatment process instead of HCI activation. Pd-Ni alloy composite membrane prepared by electro plating was fairly a uniform and dense surface morphology. The membrane was characterized by permeation experiments with hydrogen and nitrogen gases at temperature 773 K and pressure 2.2 psi. The results showed that hydrogen ($H_2$) permeance was 27 ml/$\textrm{cm}^2$ㆍatmㆍmin and hydrogen/ nitrogen ($_H2$$N_2$) selectivity was 8 at 773 K.

• Korean Chemical Engineering Research
• /
• v.43 no.1
• /
• pp.66-70
• /
• 2005

For the application in HI decomposition reaction of thermochemical water-splitting IS process, the carbonized membranes using the polymer material (polyimide) were prepared, and SiC membrane was also prepared by SiO treatment on those carbonized membranes. The weight change by the carbonation of polyimide was about 50%, and the weight decreased with an increase of carbonation temperature. The gas permeance ($H_2$ or $N_2$) of carbonized membrane decreased with an increase of carbonation temperature led to the pore closing. The gas permeance ($H_2$ or $N_2$) of SiC membrane increased with an increase of SiO treatment concentration, and the gas permeation mechanism was changed from the activiation energy flow to Knudsen flow.

• Journal of the Korean Ceramic Society
• /
• v.50 no.6
• /
• pp.451-453
• /
• 2013

Porous ceramic membranes consisting of $Ce_{1-x}Y_xO_{2-{\delta}}$ were developed for hydrogen permeation tests. Various amounts (x = 0, 0.05, 0.1, 0.2) of yttrium were doped to ceria to study the effect of yttrium doping on ceria membranes on various properties, including hydrogen permeability. $Ce_{1-x}Y_xO_{2-{\delta}}$ powder was synthesized by the sol-gel method. These membranes were fabricated by pressing and sintering at $1300^{\circ}C$ for 6 h. As the amount of yttrium increased, the grain size of the membrane decreased. Hydrogen permeability was improved as the yttrium content increased. Selective permeability of hydrogen compared to CO is explained by electric conductivity. As the temperature rose, both the hydrogen perm-selectivity and electric conductivity on $Ce_{0.8}Y_{0.2}O_{1.9}$ improved.

• Journal of the Korean Ceramic Society
• /
• v.50 no.6
• /
• pp.495-497
• /
• 2013

SiC-$Y_2O_3$ porous composites were fabricated using $Y_2O_3$ powders synthesized by sol-gel process to control physical and thermo-chemical properties. $Y_2O_3$ powders were mixed with SiC powders by co-pressing with HPCS (hydridopolycarbosilane) binder at moderate temperature. The properties of membranes were characterized by XRD, FE-SEM, and BET surface analysis. Hydrogen permeability was performed at various temperatures.