• 한국주조공학회지
• /
• 제34권2호
• /
• pp.54-59
• /
• 2014

In this study, the extruded Al-6.3Zn-2.4Mg alloys were selected among the 7000 series aluminum alloys sensitive to hydrogen environment in order to examine the effects of both the aging conditions and the length of hydrogen charging period on the mechanical properties of the alloy. The specimens were aged for 24hours at $100^{\circ}C$ (under aging (UA)), $120^{\circ}C$ (peak aging (PA)), and $160^{\circ}C$ (over aging (OA)), respectively. Charging tests were performed at RT for 12, 24, 36 hours under potentiostatic conditions (-2000 mV vs (Ag/AgCl)) for 12, 24 and 36 hours in 1M $H_2SO_4$ and 0.1%$NH_4SCN$ solution. The fracture surface was examined by scanning electron microscopy (SEM). X-ray diffraction (XRD) pattern in peak aged sample was obtained before and after hydrogen charging from extruded Al-6.3Zn-2.4Mg alloys. The decreasing rate of tensile strength and elongation is represented in order of over aging < under aging < peak aging, and it is believed that the hydrogen recharge is more sensitive to elongation than tensile strength. The formation of $AlH_3$ in hydrogen charged Al-6.3Zn-2.4Mg alloys has been confirmed by X-ray diffraction studies.

• 한국해양공학회지
• /
• 제1권1호
• /
• pp.111-119
• /
• 1987

The corrosion fatigue crack propagation characteristics of SS41 steel in 3.5% NaCl solution have been evaluated for loading frequencies of 1Hz and 0.2Hz. A sine wave loading profile was used for fatigue testing. Each test was carried out at a constant stress ratio, R(0.1). The main results are summarized as follows; 1. Fatigue crack propagation rate was higher in 3.5% NaCl solution than in air, higher in the base metal than in the weld metal, and higher at f =0.2Hz than at f =1Hz. 2. The crack closure level of the base metal was not influenced by cyclic frequencies, but that of the weld metal was much influenced. 3. When the crack closure effect was eliminated in the evaluation of crack propagation characteristics by using $\Delta K_{eff}$, the envirommental influence was distinctly observed. At the base metal, crack propagation rate was enhanced by the hydrogen embrittlement, and the weld metal was reduced by the crac closure. 4. There was clearly observed hydrogen embrittlement and severely corroded aspect at fracture surface of lower frequency than that of higher frequency, and at that of base metal than that of the weld metal.

• 대한금속재료학회지
• /
• 제46권5호
• /
• pp.296-303
• /
• 2008

Hydrogen permeation through dense palladium-based membranes has attracted the attention of many scientists largely due to their unmatched potential as hydrogen-selective membranes for membrane reactor applications. Although it is well known that the permeation mechanism of hydrogen through Pd involves various processes such as dissociative adsorption, transitions to and from the bulk Pd, diffusion within Pd, and recombinative desorption, it is still unclear which process mainly limits hydrogen permeation at a given temperature and hydrogen partial pressure. In this study, we report an all-electron density-functional theory study of hydrogen permeation through Pd membrane (using VASP code). Especially, we focus on the variation of the energy barrier of the penetration process from the surface to the bulk with hydrogen coverage, which means the large reduction of the fracture stress in the brittle crack propagation considering Griffith's criterion. It is also found that the penetration energy barrier from the surface to the bulk largely decreases so that it almost vanishes at the coverage 1.25, which means that the penetration process cannot be the rate determining process.

• 에너지공학
• /
• 제18권1호
• /
• pp.56-62
• /
• 2009

본 연구에서는 X65강의 용접부에 전기화학적 방법으로 수소를 장입한 이후에, 소형펀치시험편을 사용하여 기계적 강도를 평가하고 파면을 분석하였다. 모재부의 경우와는 다르게 용접부에서는 수소장입정도에 따라 강도저하가 민감하게 나타나는 거동을 보였다. 수소장입시 전류밀도, 온도, 장입시간의 변화에 따라 강도 및 연신율 등의 기계적 성질이 민감하게 변화하였다. 특히, 전류밀도가 높고 장입시간이 길어짐에 따라서 강도의 저하가 크게 나타났으나, 상대적으로 전해질 온도의 영향은 비교적 작게 나타났다. 또한 주사전자현미경을 통해 관찰한 시험편의 파면에서 수소침투된 표면근처의 재료에서 취성파면이 발견되었으며, 이는 강도의 저하 거동과 일치되는 경향이다. 수소취화 거동 평가 연구를 위해 본 연구에서 채택한 시험시스템은 재현성이 높게 나타나고 있으며, 이 방법을 이용한 재료의 강도평가 결과 매우 높은 신뢰성을 보이고 있다. 따라서 소형펀치시험과 전기분극법을 이용함으로써 X65강 용접부의 수소취화에 의한 강도변화를 민감하게 평가할 수 있었다. 산출된 데이터의 통계적인 처리를 통해 강도변화값을 예측할 수 있었음도 보였다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.54-59
• /
• 2004

In this paper probabilistic fracture mechanics(PFM) approach is employed to evaluate the integrity of CANDU Zr-2.5Nb pressure tubes. Modified failure assessment diagram(Jr-FAD), plastic collapse, and critical crack length(CCL) approach are used for evaluating failure probability of the tubes. Jr-FAD was extended from the Kr-FAD because fracture of pressure tubes occurs in brittle manner due to hydrogen embrittlement of material by deuterium fluence. For developing the probabilistic integrity evaluation module, AECL procedures and fracture toughness parameters of EPRI were used.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.273-275
• /
• 2002

The effect of post-weld heat treatment (PWHT) of marine structures steel was investigated at electrochemical viewpoint. In addition, slow strain rate test (SSRT) was carried out to investigate both electrochemical and mechanical properties by PWHT effect during impressed current cathodic protection. The optimum cathodic protection potential by SSRT was -770 mV(SCE). At the applied cathodic protection potential of -770 mV -850 mV(SCE), the fracture morphology was dimple pattern with ductile fracture, while it was transgranular pattern (Q.C: quasi cleavage) under -875 mV(SCE).

• Journal of Advanced Marine Engineering and Technology
• /
• 제30권1호
• /
• pp.157-168
• /
• 2006

Recently, interest in using Al alloys in ship construction instead of fiber-reinforced plastic (FRP) has increased because of the advantages of A) alloy ships over FRP ships, including high speed, increased load capacity. and ease of recycling. This paper investigated the mechanical and electrochemical properties of Al alloys in a slow strain rate test under various potential conditions. These results will provide reference data for ship design by determining the optimum protection potential regarding hydrogen embrittlement and stress corrosion cracking. In general, Al and Al alloys do not corrode on formation of a film that has resistance to corrosion in neutral solutions. In seawater, however, $Cl^-$ ions lead to the formation and destruction of a Passive film. In a potentiostatic experiment. the current density after 1200 sec in the Potential range of $-0.68\~-1.5\;V$ was low. This low current density indicates the protection potential range. Elongation at an applied potential of 0 V was high in this SSRT. However, corrosion protection under these conditions is impossible because the mechanical properties are worse owing to decreased strength resulting from the active dissolution reaction in parallel parts of the specimen. A film composed of $CaCO_3\;and\;Mg(OH)_2$ confers corrosion resistance. However, at potentials below -1.6 V forms non-uniform electrodeposition coating, since there is too little time to form a coating. Therefore, we concluded that the mechanical properties are poor because the effect of hydrogen gas generation exceeds that of electrodeposition. Comparison of the maximum tensile strength, elongation, and time to fracture indicated that the optimum protection potential range was from -1.45 to -0.9 V (SSCE).

• 한국수소및신에너지학회논문집
• /
• 제31권3호
• /
• pp.284-292
• /
• 2020

In this study, hydrogen charging was conducted for API X70 steel by the electro-chemical hydrogen charging method. Right after hydrogen was diffused from the specimen surface to the inside of the X70, the small punch tests and hydrogen concentration analysis was conducted within 5 minutes. Hydrogen was analyzed by melting the whole specimen and detect the gas after melting. Mechanical properties were measured by the small punch (SP) testing. Fracture surface and specimen surface were observed using scanning electron microscope. Three tests were repeated for study sensitivity of the SP test results under a same charging condition. It was observed that the variation of the maximum load, SP displacement at failure, hydrogen concentration as the charging period was not much in the case of X70 as the other steel such as Inconel. It can be argued that X70 base metal may have high hydrogen damage resistance and hydrogen diffusion in the base metal would not cause much embrittlement. Limitations of the SP test with 0.5 mm thickness for hydrogen damage test for X70 were discussed.

• Journal of Welding and Joining
• /
• 제16권4호
• /
• pp.55-62
• /
• 1998

While excellent joint quality has been obtained using dry chamber underwater welding methods, the size limitations imposed by this process restrict its use for underwater construction work. The wet underwater shielded metal-arc welding eliminates this restriction but suffers from poor weld properties by the 1-pass bead-on-plate welding due to the excessive diffusible hydrogen. On the other hand, in the wet underwater welding, it is well known that the quantity of diffusible hydrogen in multi-pass welded parts reduce to less than that in 1-pass welded parts. Therefore, in this paper, welding experiments are made the 3-pass bead-on-plate welds by using TMCP and normalized steel plates and E4301 and cellulose coated electrode. After that, The amounts of the hydrogen absorbed into the 3-pass welded area were measured according to the JIS Z 3118 specification. The microstructural changes as well as the microhardness distribution after the underwater 3-pass welding were also investigated using Vickers microhardness tester and S.E.M and O.M. The results indicated that the quantity of diffusible hydrogen in 3-pass welded areas was reduced little less than a half of one of that in 1-pass welded areas at the specific welding condition. As a result, the cold cracking of 3-pass welded areas decreased by reduced effect of diffusible hydrogen. In the underwater 3-pass welding, the micrography of cold cracking fracture surface showed mainly the cleavage of hydrogen embrittlement.

• 한국표면공학회지
• /
• 제40권6호
• /
• pp.262-270
• /
• 2007

Recently, there has been a new appreciation of aluminum alloys as materials that are capable of reducing the environment load. This is because aluminum alloys are lightweight, easy to recycle, permit miniaturization, and have environmental friendly properties. In this study, we investigated the mechanical and electrochemical properties of 5083F aluminum alloys using slow strain rate test(SSRT) and potentiostatic tests under various potential conditions. In the potentiostatic tests, the current density in the potential range from -0.7 to -1.4V after 1,200 s was low. After considering the results of the potentiostatic tests, maximum tensile strength, yield strength, elongation, time-to-fracture, observation of fractured specimen and fractography analysis, the optimum protection potential range was between -1.3 and -0.7V(Ag/AgCl).