• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.1030-1033
• /
• 2003

This paper presents the deposition characterization of polycrystalline silicon films by the HWCVD(Hot-wire Chemical Vapor Deposition) method at low substrate($300^{\circ}C$). The filament temperature, pressure and $SiH_4$ concentration were determined to be a critical parameter for the deposition of poly-Si films. Series A was deposited under the conditions of $1380^{\circ}C$(Tf), 100 mTorr and $2{\sim}10%\{SiH_4/(SiH_4+H_2)\}$ for 60 min. Series B was deposited under the conditions of $1400{\sim}1450^{\circ}C$ (Tf), 30 mTorr and $2{\sim}12%$ for 60 min. The physical characteristics were measured by Raman and FTIR spectroscopy, dark and photoconductivity measurements under AM1.5 illumination.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.267-267
• /
• 2010

The structural and electrical properties of microcrystalline silicon films were investigated by hot wire chemical vapor deposition(HWCVD) often called catalytic chemical vapor deposition(Cat-CVD). The Si microcrystalline phase is easily controlled by changing the rate of the silane concentration of $SiH_4$ to $H_2$ during deposition. The Structural property was observed by Raman and SEM. Photo-conductivity and dark conductivity, and photo-sensitivity were observed by Sunsimulator (AM 1.5 illumination). The film color was changed by the variation of silane concentration. HWCVD is useful for the formation of Si thin films for solar cell and needs further commercialized development for mass production.

• Current Photovoltaic Research
• /
• v.2 no.1
• /
• pp.1-7
• /
• 2014

We developed a method of growing thin Si film at $600^{\circ}C$ by hot wire CVD using a very thin large-grained poly-Si seed layer for thin-film Si solar cells. The seed layer was prepared by crystallizing an amorphous Si film by vapor-induced crystallization using $AlCl_3$ vapor. The average grain size of the p-type epitaxial Si layer was about $20{\mu}m$ and crystallographic defects in the epitaxial layer were mainly low-angle grain boundaries and coincident-site lattice boundaries, which are special boundaries with less electrical activity. Moreover, with a decreasing in-situ boron doping time, the mis-orientation angle between grain boundaries and in-grain defects in epitaxial Si decreased. Due to fewer defects, the epitaxial Si film was high quality evidenced from Raman and TEM analysis. The highest mobility of $360cm^2/V{\cdot}s$ was achieved by decreasing the in-situ boron doping time. The performance of our preliminary thin-film solar cells with a single-side HIT structure and $CoSi_2$ back contact was poor. However, the result showed that the epitaxial Si film has considerable potential for improved performance with a reduced boron doping concentration.