• KEPCO Journal on Electric Power and Energy
• /
• v.6 no.2
• /
• pp.137-143
• /
• 2020

The CM247LC, a Ni-based superalloy material used for gas turbine hot gas path parts, is casted using directionally solidified technology to analyze the mechanical properties and microstructures through HIP (Hot Isostatic Pressing) and post-heat treatment, and to derive optimal HIP treatment conditions. The CM247LC material is being researched in various ways as an alternative material for prototyping gas turbine blades. In particular, the blade rotating part is exposed and operated in a high temperature and high-pressure environment, and when damaged, it may cause huge economic losses. Therefore, in order to use the CM247LC material as prototyping materials for gas turbine blades, the reliability of the microstructure and mechanical properties must be verified. In this study, after casting rod test specimens using CM247LC material by directionally solidified technology, after that the specimens were performed by HIP treatment and post-heat treatment to test two HIP conditions designed by KEPCO to derive the possibility of prototyping of CM247LC material and optimization of HIP treatment conditions. Additionally, the properties of CM247LC material were compared to the GTD111DS material using for 1,300℃ class gas turbine blades.

• Korean Journal of Materials Research
• /
• v.6 no.3
• /
• pp.318-323
• /
• 1996

원소 분말을 합성하여 Ti5SI3 화합물을 합성하는 방법을 연구하였다. 합성법으로서는 기본적으로 반응소결법을 사용하였으며, 치밀화를 위하여는 유사-열간 정수압 성형법(PHIP, pseude-hot isostatic pressing)을 사용하였다. 반응소결법에서는 분말의 입도, 반응온도 및 유지시간이 소결밀도에 영향을 주었으며, PHIP법에 의한 치밀화에서는 압력 및 유지 간이 주요 변수로 사용되었다. 이들 변수중 미세한 입도와 유지시간이 기공을 감소시켰다. 또한 Cu의 첨가 영향을 연구하였는데, 약 6wt%이내의 Cu 첨가는 밀도 향상에 좋은 영향을 미쳤다. 반응소결 및 PHIP를 통해 Ti5SI3 -Cu의 상대밀도를 약 99%까지 높일 수 있었으며, 이때 Cu의 효과는 감도지수 부합됨을 확인하였다.

• Journal of the Korean Ceramic Society
• /
• v.30 no.10
• /
• pp.785-790
• /
• 1993

Sialon ceramics are presently seen as promising materials with high hardness, strength, fracture toughness and corrosion resistance for friction and wear applications. The objective of present work is to improve of mechanical properties and wear resistance of $\alpha$-Sialon(x=0.4) by addition of SiC whisker. $\alpha$-sialon(x=0.4)/SiC whisker composites were obtained by hot-isostatic pressing at 173$0^{\circ}C$ for 1 hour under 1757Kg/$\textrm{cm}^2$ N2 pressure after pressureless sintering the mixture of Si3N4, Y2O3, AlN at 1780~180$0^{\circ}C$ for 3~5 hours in N2 atmosphere. As the amount of SiC whisker content increased, relative density and hardness were decreased, however fracture toughness, bending strength and tribological properties were improved. Tribological properties of $\alpha$-Sialon/15 vol% SiC whisker composite were improved in spite of its low mechanical properties.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.05a
• /
• pp.139-142
• /
• 2004

Nickel base superalloys are widely used for high temperature applications due to heat resisting capability and corrosion resistance at high temperatures. Superalloys with many strengthening alloying elements are frequently used in powder form to alleviate harmful effects of alloy segregation. HIP (hot isostatic pressing) and DB (diffusion bonding) as a form of solid-state bonding process is used to make turbine components, such as integrated turbine rotors. HIP/DB process requires many technical overcomes related to dimensional changes as well as microstructural control. In this research, HIP/DB process for nickel base superalloys, Udimet 720 and MM 247, were investigated with a view to control the dimensional change during the consolidation process. Simple disc-shaped cans were used to select the conceptual die design for the control of the dimensional change especially in radial direction. The change in the shape of consolidated shape was investigated using commercial FE code with constitutive equations fur low temperature plasticity deformation.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.10a
• /
• pp.35-38
• /
• 2004

Graphite nanofiber (GNF) and carbon nanotube (CNT) are novel fiber reinforcing materials which have outstanding physical and mechanical properties. Aluminum matrix composites reinforced graphite nanofiber were fabricated by conventional powder metallurgy (PM) method. The composites were prepared through ultrasonication, ball milling, and hot isostatic pressing. A uniform distribution of GNF in aluminum matrix could be obtained. To measure the mechanical properties of GNF-Al composites testings were done in indentation and compression. The compressive strength was enhanced according to reinforcing graphite nanofiber while the hardness was decreased. This study makes the high performance composites for future applications.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2006.10a
• /
• pp.627-628
• /
• 2006

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.30 no.3 s.246
• /
• pp.349-355
• /
• 2006

The gas turbine components is used on high temperature conditions which under severely circumstance with start-up and stop several times. Therefore, it is used nickel-base superalloys like and GTD-111DS. Damaged buckets on the t긴ade tip during operating are repaired per 24,000 hr to three times according to repair specification of manufacture. It is applied pre-heat, HIP(hot isostatic pressing) and post-heat treatment to support welding repair on blade tip effectively. On this study, It is utilize of $WRAP^{TM}$ (welding repair advanced process) method to make tension test specimens for this study, And then, material strength and characteristic for GTD-111DS was analyzed.

• Journal of Powder Materials
• /
• v.14 no.1 s.60
• /
• pp.32-37
• /
• 2007

Using spark plasma sintering process (SPS), Ti-6Al-4V alloy powders were successfully consolidated without any contamination happened due to reaction between the alloy powders and graphite mold. Variation of microstructure and mechanical properties were investigated as a function of SPS temperature and time. Compared with hot isostatic pressing (HIP), the sintering time and temperature could be lowered to be 10 min. and $900^{\circ}C$, respectively. At the SPS condition, UTS and elongation were about 890 MPa and 24%, respectively. Considering the density of 98.5% and elongation of 24%, further improving the tensile strength would obtain by increasing the SPS pressure.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.10a
• /
• pp.171-174
• /
• 2004

Superalloys with many strengthening alloying elements are frequently used in powder form to alleviate harmful effects of alloy segregation. HIP (hot isostatic pressing) and DB (diffusion bonding) as a form of solid-state bonding process is often used to make turbine components, such as integrated turbine rotors. HIP/DB process requires many technical overcomes related to dimensional changes as well as microstructural control. In this research, HIP/DB process for nickel base superalloys, Udimet 720, were investigated with a view to control the dimensional change during the consolidation process. Simple disc-shaped cans were used to select the conceptual die design for the control of the dimensional change especially in radial direction. The change in the shape of consolidated shape was investigated using commercial FE code with constitutive equations for low temperature plasticity and creep deformation.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.1027-1032
• /
• 1995

SiC had been widely applied for mechanical sealing as a sealing material. SiC sintering is commonly made of reaction sintering, presureless sintering, and hot isostatic pressing (HIP) sintering. In this investigation, however, clay bonded sintering was used to avoide any complications of the special sintering methods as mentioned above. In order to prevent harmful SiC oxidation in the clay bonded sintering, clay and frit were used to form the SiC oxidation protecting layer and graphite was added to provide high solid lubricity. As a result, the material with 6% clay (clay 5.4% and frit 0.6%) and 2~4% graphite (45 mesh) sintered at 140$0^{\circ}C$ for 3 hours, showed the following physical properties; porosity 6%, static friction coefficient 0.15, kinematic coefficient 0.1,. and specific wear rate 4.8$\times$10-8 $\textrm{mm}^2$kgf-1. On the other hand, the flexural strength was 900kgf/$\textrm{cm}^2$. This tribological characteristic properties were similar to those of the reaction sintered SiC except the flexural strength.