• Journal of the Semiconductor & Display Technology
• /
• v.9 no.2
• /
• pp.73-78
• /
• 2010

This research is about the drying and curing characteristic of conductivity metallic ink on-line curing device in order to improve the curing time for productivity in RFID Gravure printing. The curing process is carried out to increase the electric conductivity after the metallic ink is printed on the substrate. The metal ink is composed of nano-sized silver or copper particles. In this research, the combined IR and Hot air curing system is used and its results is compared with those of oven, IR and Hot Air type respectively. Generally the curing time in the past is about 3 minutes. But the combined system (IR+Hot Air) in this research shows that curing time is less than 30 seconds. These results is much faster than those of other system. This study can be help to make Roll-to-Roll drying and curing process for mass and continuous production on-line.

• Proceedings of the SAREK Conference
• /
• 2009.06a
• /
• pp.183-188
• /
• 2009

RFID method is a non-contact automatic identification technology, which attaches microchips and antennas to an object in a tag form, to send and process information sent to the network using wireless frequency. Drying and curing process is extremely important which minimizes the resistivity of RFID antennas. This research is about the drying characteristic of conductivity ink, and analyzes and compares the hot-air drying process and infrared drying process. Also, the research was done for the improvement in drying performance by using combined process of hot-air and infrared mechanism. The experiment result shows that the hot-air or infrared drying system used alone cannot meet the required performance in drying printing method using conductivity ink. The combined drying system of hot-air and infrared ray showed resistance low enough in short drying and curing time, and this mechanism makes drying and curing process for mass and continuous production possible on-line.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.04a
• /
• pp.239-240
• /
• 2022

In winter, low outdoor temperature can casue reduction of concrete strength. Therefore, thermal protection is required when curing concrete in winter to maintain a certain level or higher surface temperature. Accordingly, in domestic construction sites, a curing method in which surrounds casting areas by tents and operates hot air blowers are widely applied. However, local low-temperature areas may occur due to airtightness of the curing tents. If additional heat is supplied to prevent occurrence of local low-temperature areas, energy consumption increases. Therefore in this study, a plan for improvement method of concrete curing was considered and the performance was evaluated through numerical analysis. A plan to improve the airtightness of the wall opening was applied, but the analysis showed that if only a part of the curing area is shielded, the temperature of the unshielded area decreases,making it inappropriate to improve curing performance.

• Journal of the Korean Society of Tobacco Science
• /
• v.23 no.1
• /
• pp.12-18
• /
• 2001

This study was conducted to investigate the effect of tobacco curing on far infrared light on the quality of flue-cured tobacco leaves. Physicochemical characteristics such as alkaloid, total sugar, total nitrogen, starch, total phenolic compounds, browning degrees, and color differences, in cured tobacco leaves were compared between hot air and far infrared curing methods. There was no significant difference in sugar/nicotine ratio and nitrogen number between the curing methods, while the contents of ether extract and filling capacity were increase by far infrared curing. Therefore, it was expected that far infrared curing might be effective for high aroma and physical properties of the cured tobacco leaves.

• Proceedings of the SAREK Conference
• /
• 2009.06a
• /
• pp.1429-1434
• /
• 2009

Recently electronic circuit pattern printing technologies like antennas of RFID process are paid attention. oven drying system is being used since drying and curing time of RFID Tag Gravure printing normally takes from 5 minutes and up to 30 minutes long. In this case the parental material which is of a sheet shape is possible, however, for a massive and a continuous production drying and curing process must be done on-line. This research compared and analyzed the an oven type drying device and a traditional hot-air drying device. Considering the experiment result, the cell depth that shows low resistivity, which doesn't consider the pattern difference, is $31{\sim}33{\mu}m$. Also, oven drying system showed some resistivity after around 120 seconds of drying time, and showed much better performance in minimum resistivity compared to the hot-air drying system.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.281-286
• /
• 2002

To study of binder and fine aggregate a lot of replacement fly-ash concrete, initial characteristics, standard environment of curing temperature $20^{\circ}C$, hot-weather environment of curing temperature $35^{\circ}C$, . Flesh concrete tested slump. air contest and Hardening concrete valuated setting period of form, day of age 1, 3, 5. 7, 10, 28 compression strength in sealing curing. Purpose of study is consultation materials in field that variety of fly-ash replacement concrete mix proportion comparison and valuation. (1) Experiment result age 28day compression strength more higher plan concrete then standard environment in curing temperature $20^{\circ}C$, , most strength F43 is hot-weather environment in curing temperature $35^{\circ}C$, replacement binder 25%, fine aggregate 15%. (2) Hot-weather environment replacement a mount of fly-ash is a same of plan concrete setting period of form. Age 28day compression strength replacement a mount of fly-ash more hot-weather concrete then plan concrete.

• Elastomers and Composites
• /
• v.43 no.1
• /
• pp.1-7
• /
• 2008

Far-infrared vulcanization of ethylene-propylene-diene terpolymer(EPDM) compounds has been studied in comparison with hot air vulcanization. Vulcanization characteristics of EPDM compounds were measured by degree of curing and temperature of specimens in vulcanization process. As a result, degree of curing by far-infrared of EPDM compounds was shown to be higher value than that by hot air at the same vulcanization temperature. Especially, degree of curing by far-infrared on 3 mm thickness of EPDM compounds was increased by two times compared to that by hot air. While the increase of thermal conductivity of EPDM compounds highly improved degree of curing by far-infrared, that hardly improved degree of curing by hot air.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.109-110
• /
• 2020

In This study, we tried to review an efficient curing method in consideration of safety and constructability among the problems of winter construction. In other words, as a result of the mock-up test, the measured value of carbon monoxide was 0 ppm in the case of an electric hot air fan. Since there is no carbon monoxide, problems such as suffocation are expected to be solved. In terms of temperature characteristics, electric hot air fans exhibited high thermal efficiency performance with a slight difference in upper/lower temperatures compared to the existing ones. In the future, we plan to conduct thermal efficiency evaluation through actual site performance verification. We will propose an efficient curing method through applicability evaluation.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.34 no.5
• /
• pp.27-34
• /
• 2018

Concrete placed under hot weather condition suffers from larger slump loss, rapid moisture evaporation due to high air temperature. Proper measures for material, transportation and curing should be taken to prevent the quality deterioration of the concrete under hot weather condition. In Korea, Although the period of hot weather concrete in Korea occupies only 2 months, there are a lot of quality problems including plastic, drying shrinkage and cold joint. Therefore, the objective of this paper is to investigate and compare the temperature history and crack occurrence of the concrete, which was placed in the actual apartment house construction field under hot weather condition, in response to the application of surface covered curing blankets including PE film, single layer clear bubble sheet, white colored bubble sheet and aluminum metalized bubble sheet. Test results indicated that the application of white colored bubble sheet and aluminum metalized bubble sheet showed most favorable results in terms of reduction in temperature rise and crack occurrence as well as easiness in handling. But, due to light reflection by aluminum metalized bubble sheet, it is believed that white colored bubble sheet is preferable.

• Journal of Korean Society of Occupational and Environmental Hygiene
• /
• v.21 no.1
• /
• pp.1-10
• /
• 2011

Generally, the tire curing process is the process in which the sulfur is added and subsequently the tire is heated to give the tire elasticity. In this process, all kinds of the chemicals in the tire are emitted with a lot of heat. The chemical fume and heat aggravate the work environment. To solve this problem, 92 local exhaust ventilators and 8 gravity ventilators were used, but not satisfactory yet. Preliminary survey showed that the temperatures in the process were very high: 30.3, 32.9 and $37.2^{\circ}C$ at 2, 4 and 6m above the ground level, respectively in the winter (outside temperature was $2^{\circ}C$). It can be imagined that the process is severely hot in the summer time. The higher temperature distribution in the higher space tells us that the hot plume could not be removed with the existing ventilation systems. Therefore, in this study, some alternative ventilation systems were designed. The partitions were used to contain the hot plume to increase the capture efficiency. The gravity ventilators were newly designed to improve the extraction efficiency of hot fume. To satisfy the balance of pressure in the curing process, some supply air system was introduced by renewing the existing air conditioning system. Many alternative solutions were evaluated by using computational fluid dynamics modelling. The best and applicable solution was selected and the existing ventilation system was modified. After implementing the new ventilation system, the hot environment was much improved. The temperature reduction in the curing process was about $6.4^{\circ}C$.