• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회 논문집(II)
• /
• pp.939-944
• /
• 2000

This study examines both strength development and pore volume of high temperature curing mortar, using a blast-furnace slag powder (BFS). This study experiments with various pre-steaming period, differing curing temperature and the replacement of BFS. According to the results, the strength development of BFS mortar is stronger when higher curing temperature are used(as opposed to standard curing). Also, regardless of the curing method, pore volume decreases as the curing time increases. From these results we can identify the optimum conditions required pre-steaming period, differing curing temperature and the replacement to produce BFS mortar properties.

• 한국건축시공학회지
• /
• 제3권2호
• /
• pp.129-134
• /
• 2003

In this research, we used fly-ash and blast-furnace slag as substitute material of cement and fine aggregate, and we, through experiments, researched and analyzed the features of high-flowable concrete added high efficiency AE water reduction agent. The results are below. 1. Liquefaction generally presented high-slump flow value; on the other hand, partial segregation was observed in case of mixing proportion with 65 cm slump flow and above. This segregation was partially improved in accordance with mixing admixture. 2. Compressive strength according to mixing admixture and increasing mixing ratio of fly-ash were subject to be declined when it was initially cast-in, but its gap was improved when time was fully passed. 3. After mixing blast-furnace slag and fly-ash as substitute material, the result showed that the modulus of elasticity against freezing & melting was improved according to mixing blast-furnace slag and also increased in accordance with increasing pulverulent-body volume. 4. According to increasing the mixing volume of fly-ash, the durability factor was deteriorated because compressive strength became lower as well as air content was decreased when it was initially case-in. 5. The minimum air content to secure durability was 3.7%, for that reason, we had better secure admixture such as air entraining agent when cast-in high-flowable concrete.

• 한국건설순환자원학회논문집
• /
• 제1권2호
• /
• pp.93-100
• /
• 2013

최근 플라이애시 및 고로슬래그 미분말을 다량 치환하는 콘크리트에 대한 연구가 활발히 진행되고 있다. 혼화재 다량 치환 콘크리트를 실제 현장에서 골조용으로 적용하기 위해서는 적정 치환율을 도출하는 것이 중요하다. 이에 본 연구에서는 혼화재 다량 치환 콘크리트의 특성을 파악하기 위해 작업성을 동일하게 확보한 조건에서 플라이애시 및 고로슬래그 미분말의 치환율 및 양생온도에 따른 압축강도의 변화를 측정하였다. 검토 결과, 플라이애시의 치환율이 10% 증가할시 재령 3일 압축강도는 약 1.4MPa, 재령 28일 압축강도는 약 3.8MPa가 감소하는 것으로 나타났으며, 고로슬래그의 치환율이 10% 증가할시 재령 3일 압축강도는 약 1.0MPa, 재령 28일 압축강도는 약 0.9MPa가 감소하는 것으로 나타났다. 본 연구를 통해 향후 공동주택의 골조용 혼화재 다량 치환 콘크리트의 연구개발을 위한 기초자료를 확보할 수 있었다.

• Computers and Concrete
• /
• 제16권2호
• /
• pp.261-274
• /
• 2015

This study established the standard recommended values and expansion fracture threshold values for the content of steel slag in controlled low-strength materials (CLSM) to ensure the appropriate use of steel slag aggregates and the prevention of abnormal expansion. The steel slags used in this study included basic oxygen furnace (BOF) slag and desulfurization slag (DS), which replaced 5-50% of natural river sand by weight in cement mixtures. The steel slag mortars were tested by high-temperature ($100^{\circ}C$) curing for 96 h and autoclave expansion. The results showed that the effects of the steel slag content varied based on the free lime (f-CaO) content. No more than 30% of the natural river sand should be replaced with steel slag to avoid fracture failure. The expansion fracture threshold value was 0.10%, above which there was a risk of potential failure. Based on the scanning electron microscopy (SEM) analysis, the high-temperature catalysis resulted in the immediate extrusion of peripheral hydration products from the calcium hydroxide crystals, leading to a local stress concentration and, eventually, deformation and cracking.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2009년도 춘계 학술대회 제21권1호
• /
• pp.311-312
• /
• 2009

콘크리트 파일에 진동밀로 개질한 슬래그 시멘트를 적용하여 기존의 제품과 압축 강도 비교시 분체량이 적음에도 불구하고 더 높은 압축 강도가 측정되었다. 이는 SEM 이미지 관찰시 기공의 크기 및 개체수 감소와 시멘트 수화물이 치밀한 구조로 성장하여 강도가 증진되었다고 판단된다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2017년도 춘계 학술논문 발표대회
• /
• pp.208-209
• /
• 2017

This study analyzed the fluidity and strength properties of mortar containing high volume blast furnace slag by replacement ratio of lightweight fine aggregate for reducing the unit weight of concrete structures.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2013년도 추계 학술논문 발표대회
• /
• pp.30-31
• /
• 2013

In this study, characteristics of the concrete replaced in large amount with blast furnace slag is analyzed by the microscopic analyses in the process of the mock-up testing to apply to the actual practice in the area of the general strength by activating a small amount of cement(25%) replaced in large amount of finely powered blast furnace slag.

• International Journal of Concrete Structures and Materials
• /
• 제8권1호
• /
• pp.69-81
• /
• 2014

In this study, portland cement (PC) has been partially replaced with a Class F fly ash (FA) at level of 70 % to produce high-volume FA (HVFA) concrete (F70). F70 was modified by replacing FA at levels of 10 and 20 % with silica fume (SF) and ground granulated blast-furnace slag (GGBS) and their equally combinations. All HVFA concrete types were compared to PC concrete. After curing for 7, 28, 90 and 180 days the specimens were tested in compression and abrasion. The various decomposition phases formed were identified using X-ray diffraction. The morphology of the formed hydrates was studied using scanning electron microscopy. The results indicated higher abrasion resistance of HVFA concrete blended with either SF or equally combinations of SF and GGBS, whilst lower abrasion resistance was noted in HVFA blended with GGBS.

• 한국건설순환자원학회논문집
• /
• 제3권1호
• /
• pp.1-6
• /
• 2015

최근 $CO_2$ 감축을 위해 고로슬래그 미분말과 같은 혼화재의 치환율을 높이기 위한 연구가 활발히 이루어지고 있다. 프리캐스트 콘크리트의 경우 증기양생을 실시하기 때문에 혼화재의 치환율을 높여도 초기 강도 확보에 유리한 것으로 알려져 있다. 하지만 다양한 증기양생이력에 따른 압축강도 특성에 대한 연구가 요구된다. 따라서 본 연구에서는 고로슬래그 다량치환(질량비 60%) 시멘트 콘크리트의 증기양생 이력에 따른 콘크리트 압축강도 특성을 규명하기 위해 물-결합재비(W/B) 32, 35%, 단위수량 135, $150,165kg/m^3$ 수준으로 콘크리트를 제조하였다. 그리고 공시체의 최고온도(50, $60^{\circ}C$) 및 최고온도유지시간(5, 6, 7hr)을 변수로 증기양생을 실시하였다. 실험결과, 증기양생을 통해 높은 초기강도를 얻을 수 있었지만 28일 압축강도에서 강도가 저하되는 현상을 확인할 수 있었다. 따라서 고로슬래그 다량치환 시멘트 콘크리트의 프리캐스트 콘크리트 부재에의 적용을 위해서는 탈형강도 및 요구강도를 확보할 수 있는 증기양생 이력에 대한 추가적인 연구가 필요하다.

• 한국건설순환자원학회논문집
• /
• 제3권3호
• /
• pp.261-267
• /
• 2015

본 연구에서는 고강도 고함량 고로슬래그 콘크리트의 개발을 위해 고로슬래그 미분말(GGBFS)을 65%까지 치환한 물-결합재비 23%의 고강도 콘크리트를 대상으로 압축강도 발현 특성과 내구성을 분석하였다. 연구 결과에 따르면 GGBFS를 65% 혼입한 고강도 콘크리트의 압축강도는 재령 3일까지는 보통 포틀랜드 시멘트(OPC)만을 사용한 콘크리트보다 낮지만 재령 7일 이후부터 더 높아지는 것으로 나타났으며, 강도의 증가와 함께 공극구조가 더 치밀해짐으로써 염소이온 투과 저항성이 커지고, 이로인해 별도의 공기연행 없이도 우수한 동결융해 저항성을 확보할 수 있으며, 수산화칼슘의 감소에도 불구하고 우수한 탄산화 저항성을 나타냈다. 반면 실리카퓸(SF)을 GGBFS와 함께 혼입하면 GGBFS만 혼입한 경우보다 강도는 낮아지고 염소이온 투과 저항성이 낮아지는 것으로 나타났다. 따라서 향후 고강도 고함량 고로슬래그 콘크리트에서의 SF의 반응에 대한 심층적인 연구가 요망된다.