• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.217-222
• /
• 2003

The steel slag, a by-product which is produced during the manufacture of steel by refining pig iron, is mainly used as road materials after aging it. It is necessary to age steel slag for long time in air because the reaction with water and free-CaO in steel slag could make the expansion of volume. This problem prevents steel slag from being used as aggregate for concrete. But steel slag used in this study was controled by an air-jet method which rapidly cools substance melted at a high temperature. Rapid cooling prevents from generation of free-CaO in steel slag. In this study, properties of steel slag manufactured by air-jet method and mortar used it were investigated. As results of this study, free-CaO contents were controled under 1%. Mortar used this steel slag demanded to lower water contents, higher compressive strength and lower drying shrinkage than the basic mortar in the same condition.

• Advances in concrete construction
• /
• v.11 no.2
• /
• pp.99-109
• /
• 2021

Slag blended concrete is widely used as a mineral admixture in the modern concrete industry. This study shows an optimization process that determines the optimal mixture of air-entrained slag blended concrete considering carbonation durability, frost durability, CO2 emission, and materials cost. First, the aim of optimization is set as total cost, which equals material cost plus CO2 emission cost. The constraints of optimization consist of strength, workability, carbonation durability with climate change, frost durability, range of components and component ratio, and absolute volume. A genetic algorithm is used to determine optimal mixtures considering aim function and various constraints. Second, mixture design examples are shown considering four different cases, namely, mixtures without considering carbonation (Case 1), mixtures considering carbonation (Case 2), mixtures considering carbonation coupled with climate change (Case 3), and mixtures of high strength concrete (Case 4). The results show that the carbonization is the controlling factor of the mixture design of the concrete with ordinary strength (the designed strength is 30MPa). To meet the challenge of climate change, stronger concrete must be used. For high-strength slag blended concrete (design strength is 55MPa), strength is the control factor of mixture design.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.11a
• /
• pp.103-105
• /
• 2012

With blast-furnace slag is a by-product generated when pig iron is produced. It has been used as the concrete admixture due to high reactivity. However, It causes low strength development during early age. In order to make up for this drawback, in this study, we evaluated compressive strength of mortar replaced with high volume blast-furnace slag. Experimental results, Compressive strength of mortar based on blast-furnace slag is affected by cement type, substitution rate of blast-furnace slag and pH after mixing.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.2
• /
• pp.201-207
• /
• 2015

In this paper, a series of experiments was conducted to evaluate the resistibility of carbonation and freeze-thawing damage of the high-volume blast furnace slag concrete using expancel, the expandable microsphere, and ERCO, emulsified refine cooking oil. The concrete mixture of 0.45 water-to-binder ratio with 60% of blast furnace slag was evaluated for carbonation, freeze-thawing resistibility, SEM, and porosity. According to the previous research, replacing ERCO contributes on improving carbonation resistibility with capillary pore filling effect by soap foaming reaction of ERCO while significantly decreased freeze-thawing resistibility. To improve this decreased freeze-thawing resistibility, expancel was used, and thus freeze-thawing resistibility was improved as the replacement ratio of expancel was increased. It is considered that the selective volume shrunken effect of expancel due to the external pressure and decreased air void spacing factor due to expancel.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2019.05a
• /
• pp.103-104
• /
• 2019

The aim of the research is assessing the possibility of recovering the compressive strength of the mortar mixture replaced excessively high volume of blast furnace slag accidently. As a result of the experiment, in the case of compressive strength, painting sodium oxide showed higher compressive strength recovery effect than painting calcium oxide. As a curing temperature, 20℃ showed advanced result rather than 65℃. From the wet curing, the reaction was confirmed, deeper penetration depth was checked at 20℃ than 60℃ temperature. Therefore for the concrete mixture with excessively high volume of blast furnace slag, it is considered that painting sodium hydroxide and curing 20℃ can recover the compressive strength effectively.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.4
• /
• pp.393-400
• /
• 2012

The effect of ground granulated blast-furnace slag (GGBS) and alkaline activator on the properties of setting, compressive strength, drying shrinkage and resistance of carbonation was assessed to develop high volume slag concrete, the GGBS replacement rate of which was more than 80 percent. The changes in the concrete as the replacement rate of GGBS increases were as follows. Initial and final setting time was delayed by two and a half hours, and the compressive strength development properties of concrete in early and long term age were decreased. Drying shrinkage was satisfactory as below $6{\times}10^{-4}$ in every mixture, and yet showed a tangible trend by replacement rate. Carbonation was materially increased. Setting time and early strength development property, however, were extremely advanced by the addition of the alkaline activator. While drying shrinkage was improved by the alkaline activator, resistance to carbonation was not.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10a
• /
• pp.269-274
• /
• 1998

In this study, to increase fluidity and resistance of segregation of materials, the effect of each of the materials, which have effects on high performance concrete from investigating the properties of strength and drying shrinkage of high performance concrete made by the basic mix proportion used fly-ash and ground granulated blast-furnace slag after hardening, has been checked. According to the experimental results, fluidity on W/C = 34% was satisfied within slump-flow 65$\pm$ 5cm and U-type self-compactability difference 5cm. On the properties of strength, high performance concrete produced compressive strength over 400kg/$\textrm{cm}^2$ in 28days when powder was replaced by 40% of fly-ash and 60% of ground granulated blast-furnace slag. And compressive strength was taken over 600kg/$\textrm{cm}^2$ equal to non-replacement in 91days. Also, the length change of concrete with the addition of fly-ash was smaller than that without it. Therefore, it may be effective on the decrease of drying shrinkage volume.

• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.177-184
• /
• 2015

In order to use the high-volume slag cement as a construction materials, a proper activator which can improve the latent hydraulic reactivity is required. The dissolved aluminum silicon ions from ground granulated blast furnace slag (GGBFS) react with sulfate ions to form ettringite. The proper formation of ettringite can increase the early-age strength of high-volume GGBFS (80%) cement. The aim of this study is to investigate the hydration properties with sulfate activators (sodium sulfate, anhydrite). In this paper, the effects of $Na_2SO_4$ and $CaSO_4$ on setting, compressive strength, hydration, micro-structure were investigated in high-volume GGBFS cement and compared with those of without activator. Test results indicate that equivalent $SO_3$ content of 3~5% improve the early-age hydration properties such as compressive strength, heat evolution rate, micro-pore structure in high-volume GGBFS cement.

• Korea Journal of Geothermal Energy
• /
• v.9 no.1
• /
• pp.34-39
• /
• 2013

• Computers and Concrete
• /
• v.22 no.2
• /
• pp.183-196
• /
• 2018

The rheological behaviour of high strength self compacting concrete (HS-SCC) studied through an experimental investigation is presented in this paper. The effect of variation in supplementary cementitious materials (SCM) $vis-{\grave{a}}-vis$ four different types of processed crushed sand as fine aggregates is studied. Apart from the ordinary Portland cement (OPC), the SCMs such as fly ash (FA), ground granulated blast furnace slag (GGBS) ultrafine slag (UFS) and micro-silica (MS) are used in different percentages keeping the mix -paste volume and flow of concrete, constant. The combinations of rheology, strength and durability are equally important for selection of mixes in respect of high-rise building constructions. These combinations are referred to as the rheo-strength and rheo-durability which is scientifically linked to performance based rating. The findings show that the fineness of the sands and types of SCM affects the rheo-strength and rheo-durability performance of HS-SCC. The high amount of fines often seen in fine aggregates contributes to the higher yield stress. Further, the mixes with processed sand is found to offer better rheology as compared to that of mixes made using unwashed crushed sand, washed plaster sand, washed fine natural sand. The micro silica and ultra-fine slag conjunction with washed crushed sand can be a good solution for high rise construction in terms of rheo-strength and rheo-durability performance.