• Korean Journal of Materials Research
• /
• v.14 no.8
• /
• pp.547-551
• /
• 2004

The sulfidation behaviour of Fe-XAl-0.3Y(X=5, 10, 14, 25 $wt.\%$) alloys was investigated at 1123 K in $H_2/H_{2}S$ gas atmosphere for $1\sim24$ hrs using SEM/EDX, XRD and EPMA. The weight changes of Fe-XAl-0.3Y alloys followed the parabolic rate law, Sulfidation rates of iron aluminide alloys with high Al content were one-twentieth lower than that of 5Al alloys. This is due to the formation of protective $Al_{2}O_3$ oxides on the surface of 10Al, 14Al and 25Al alloys. By calculating partial pressure of impurity oxygen contained $H_2/H_{2}S$ gas, the $Al_{2}O_3$ oxides formation could be explained using Fe-Al-S-O thermodynamic stability diagram. The sulfidation product scales of the 5Al alloy showed that thick iron sulfide scale(FeS) containing porosities formed during early stages of sulfidation. With continued sulfidation, aluminum sulfide was formed at the alloy/scale interface.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.14 no.2
• /
• pp.25-30
• /
• 2015

This study involved the fabrication of precision machine tools using a polycrystalline diamond tip [sintered PCD and cemented carbide (WC-Co) tip] and WC-Co shanks via diffusion bonding with a paste-type nickel alloy filler metal. Diffusion bonding is a process whereby two materials are pressed together at high temperature and high pressure for a sufficient period of time to allow significant atomic diffusion to occur. For smooth progress, a filler metal of nickel alloy was used at the interface. Optical microscopy images were used to observe the copula of the bonded layer. It was confirmed that cracks occurred near the junction in all cases. The tensile strength of the bond was measured using a universal testing machine (UTM) with WC-Co proportional test specimens.

• Journal of the Korean Ceramic Society
• /
• v.49 no.3
• /
• pp.221-225
• /
• 2012

It is possible to enhance the color of the natural diamond with a high pressure high temperature(HPHT) process. We employed a pyrophyllite tube cell and cubic press apparatus for HPHT treatment on the brown colored Type II (5.6 GPa/ $1700^{\circ}C$/ 52 min), and Type I aB(5.6 GPa/ $1650^{\circ}C$/ 30 min) diamond samples. We investigated the microstructure, Types, fluorescence, properties of the diamonds with an optical microscopy, FT-IR, photoluminescence(PL) spectroscopy, Diamond-View, and micro-Raman spectroscopy. Two tinted brown diamonds changed into colorless just after the HPHT process. Optical microscopy showed that no crack and significant inclusion evolution occurred during the HPHT process except the small graphite spot appeared in Type I aB sample. FTIR spectrum confirmed that no Type, amber center, and platelet defect change with the HPHT treatment. Diamond-View could not distinguish the HPHT treated diamonds from the naturals. PL spectroscopy showed that N3 and H3 color centers remained even after HPHT process. Consequently, we successfully changed the color of diamonds into colorless by 5.6 GPa HPHT process.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.426-426
• /
• 2012

The CIGS absorber has outstanding advantages in the absorption coefficient and conversation efficiency. The CIGS thin film solar cells have been researched for commercialization and increasing the conversion efficiency. CIG precursors were deposited on the Mo coated glass substrate by magnetron sputtering with multilayer structure, which is CuIn/CuGa/CuIn/CuGa. Then, the metallic precursors were selenized under high Se pressure by RTP method which included. Se vapor was supplied using Se cracker cell instead of toxic hydrogen selenide gas. Se beam flux was controlled by variable reservoir zone (R-zone) temperature during selenization process. Cracked Se source reacted with CIG precursors in a small quantity of Se because of small size molecules with high activation energy. The CIGS thin films were studied by FESEM, EDX, and XRD. The CIGS solar cell was also developed by layering of CdS and ZnO layers. And the conversion efficiency of the CIGS solar cell was characterization. It was reached at 6.99% without AR layer.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.1 no.1
• /
• pp.40-49
• /
• 2001

We have developed a repeatable process of forming uniform, small-size and high-density self-assembled Si nano-crystals. The Si nano-crystals were fabricated in a conventional LPCVD (low pressure chemical vapor deposition) reactor at $620^{\circ}c$ for 15 sec. The nano-crystals were spherical shaped with about 4.5 nm in diameter and density of $5{\times}l0^{11}/$\textrm{cm}^2$. More uniform dots were fabricated on nitride film than on oxide film. To take advantage of the above-mentioned characteristics of nitride film while keeping the high interface quality between the tunneling dielectrics and the Si substrate, nitride-oxide tunneling dielectrics is proposed in n-channel device. For the first time, the single electron effect at room temperature, which shows a saturation of threshold voltage in a range of gate voltages with a periodicity of ${\Delta}Ｖ_{GS}\;{\approx}\;1.7{\;}V$, corresponding to single and multiple electron storage is reported. The feasibility of p-channel nano-crystal memory with thin oxide in direct tunneling regime is demonstrated. The programming mechanisms of p-channel nano-crystal memory were investigated by charge separation technique. For small gate programming voltage, hole tunneling component from inversion layer is dominant. However, valence band electron tunneling component from the valence band in the nano-crystal becomes dominant for large gate voltage. Finally, the comparison of retention between programmed holes and electrons shows that holes have longer retention time.

• Journal of Surface Science and Engineering
• /
• v.50 no.3
• /
• pp.212-218
• /
• 2017

$Mg_xNi_yZn_{1-x-y}Fe_2O_4$ ferrite powders were prepared by self-propagating high temperature synthesis followed by classifying with an ultrasonic wet-magnetic separation unit to get high pure nano-sized particles. The $Mg_xNi_yZn_{1-x-y}Fe_2O_4$ ferrites were well formed by using several powders like iron, nickel oxide, zinc oxide and magnesium oxide at 0.1 MPa of oxygen pressure. The ultrasonic wet-magnetic separation of pre-mechanical milled ferrite powders resulted in producing the powders with average size of 800 nm. The addition of a surfactant during the wet-magnetic separation process improved productivity more than twice. The coercive force, maximum magnetization and residual magnetization of the $Mg_xNi_yZn_{1-x-y}Fe_2O_4$ nano-powders with 800 nm size were 3651 A/m, $53.92Am^2/kg$ and $4.0Am^2/kg$, respectively.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.4
• /
• pp.321-327
• /
• 2014

Structural light weight aggregate concrete are made with both coarse and fine light weight aggregates, but it is common with the high strength concrete to replace all or part with normal weight sand be called class 1 structural light weight aggregate concrete. Fire resistance of structural light weight aggregate concrete are determined by properties of high water content ratio and explosive spalling. Especially, structural light weight aggregate concrete is occurred serious fire performance deterioration by explosive spalling stem from thermal stress and water vapor pressure. This study is concerned with experimentally investigating fire resistance of class 1 structural light weight concrete. From the test result, class 1 structural light weight concrete is happened explosive spalling. The decrease of cross section caused by explosive spalling made sharp increasing gradient of inner temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.216-216
• /
• 2009

This paper describes a novel processing technique for the fabrication of polymer-derived SiCN (silicone carbonitride) microstructures for extreme microelectromechanical system (MEMS) applications. A polydimethylsiloxane (PDMS) mold was formed on an SU-8 pattern using a standard UV photolithographic process. Next, the liquid precursor, polysilazane, was injected into the PDMS mold to fabricate free-standing SiCN microstructures. Finally, the solid polymer SiCN microstructure was cross-linked using hot isostatic pressure at $400^{\circ}C$ and 205 bar. The optimal pyrolysis and annealing conditions to form a ceramic microstructure capable of withstanding temperatures over $1400^{\circ}C$ were determined. Using the optimal process conditions, the fabricated SiCN ceramic microstructure possessed excellent characteristics includingshear strength (15.2 N), insulation resistance ($2.163{\times}10^{14}\;{\Omega}$, and BDV (1.2 kV, minimum). Since the fabricated ceramic SiCN microstructure has improved electrical and physical characteristics compared to bulk Si wafers, it may be applied to harsh environments and high-power MEMS applications such as heat exchangers and combustion chambers.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.18 no.3
• /
• pp.307-314
• /
• 2009

Large area micro pattern replication has promising application potential in many areas. Rolling imprint process has been demonstrated as one of the most competitive processes for such micro pattern replication, because it has advantages in low cost, high throughput and high efficiency. In this paper, we developed a prototype of roll-to-flat(R2F) thermal imprint system for large area micro pattern replication process, which is one of the key processes in the fabrication of flexible displays. Experimental tests were conducted to evaluate the feasibility of system and the parameters' effect on the process, such as flat mold temperature, loading pressure and rolling speed. 100mm $\times$ 100mm stainless steel flat mold and commercially available polycarbonate sheets were used for the tests. The experimental results showed that the developed R2F system is suitable for fabrication of various micro devices with micro pattern over large area.

• Economic and Environmental Geology
• /
• v.33 no.1
• /
• pp.19-30
• /
• 2000

The Sannae-Eonyang granitic rocks are a large fossil hydrothermal system containing the Sannae Mo-W fissure-vein type and the Eonyang amethyst deposits in the southeastern Kyongsang Basin. They evolved through similar stages showing the similarities in chemical and mineralogical compositions, fractionation trends and early magmatic fluids. Major, trace and rare earth element(REE) variations can be accounted for fractional crystallization combined with variable degrees of metasomatism. Based on the aqueous fluids exsolved directly from the crystallizing melt, the Sannae-Eonyang granitic rocks were emplaced at similar depth or pressure conditions. High temperature fluid interaction with the granitic rocks affects the elements such as K, Na, Rb, Ba, Sr, Eu, and heavy REE (HREE) mostly through feldspar re-equilibration. Although hydrothermal fluids produced partly positive Eu anomalies and HREE depletion in the granitic rocks at the Sannae Mo-W mine, the chemical concentrations defining fractionnation trends have survived the effects of alteration. Aqueous fluids exsolved from the crystallizing melt appears to be widespread, whereas fluids of moderate to low salinity and low-density with relatively high homogenization temperatures and $Co_2$-rich fluids appear to be mainly restricted and responsible for Mo-W and amethyst mineralization, respectively. Hydrothermal system of the Sannae-Eonyang granitic rocks represents repeated fluid events; from exsolution of aqueous fluids from the crystallizing melt, through fluid immiscibility and meteoric convection to later mineralization.