• Journal of the Korea Institute of Building Construction
• /
• v.8 no.1
• /
• pp.71-76
• /
• 2008

Recently, the high-rise apartment housings have become a prototype of the urban residential dwelling in Korea and the numbers of one have steadily been increasing. According to this trend, the strength of the construction materials is also fortified to assure the stability and durability of the buildings. Specially, Re-bar of SD500 type is largely used at the construction sites of high-rise building. This study analyzes the current usage of SD500 high-strength re-bar at domestic construction sites. Through the result of this analysis, we develop Economic Evaluation Model that measure economic efficiency of lap splice and coupler splice, which are most commonly used in connection SD500. The evaluation method was applied to construction sites in Seoul in December 2006, and the result revealed that coupler splice is relatively superior in terms of cost efficiency when the re-bar diameter is longer and the concrete strength is lower.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10c
• /
• pp.105-110
• /
• 1998

The purpose of this was to examine the used of fly ash as a type of construction material. In this paper the results from a recent study on development of a cement composite utilizing relatively large amount of fly ash are presented. The flowable fly ash-cement sand composite was investigated for strength and flowability characteristics. The independent variable considered were: fly-ash content, sand content, and ratio of water to cementitious materials. Results of this study show that high volume fly-ash composite can be proportioned to obtain 10~15kg/$\textrm{cm}^2$ compressive strength at 28 days. For applications requiring strength between 10kg/$\textrm{cm}^2$ and 15kg/$\textrm{cm}^2$, the mixture with fly ash-cement ratio of 5.6 and sand-cement ratio of 28 with relatively high water content may be used. Slump was held at 25$\pm$1cm for all mixtures produced compressive strength at 28 days were found to range from 5kg/$\textrm{cm}^2$ to 13.7kg/$\textrm{cm}^2$.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.116-119
• /
• 2004

The use of higher strength materials frequently requires the change of design provisions. Following to the previous researches, high strength reinforcing bars have a weak point about the development and splice length. Based on the previous research about high relative rib area, bond strength between reinforcing bars and concrete can be improved by the control of rib height and spacing. But, the code provisions do not include these specific shape of reinforcing bars. So, the purpose of this paper is to determine the effect of relative rib area to the bond strength. This paper describes the experiment and analysis of 5 beam-spliced specimens containing D25 with relative rib areas ranging from 0.073 to 0.17. The test results are also analyzed to make a design formula about the calculation of splice length on the consideration of relative rib area.

• 연구논문집
• /
• s.34
• /
• pp.131-138
• /
• 2004

Porous silicon nitride ceramics were prepared by Self-propagating High Temperature Synthesis from silicon powder, silicon nitride powder and the pore-forming precursor. The microstructure, porosity and the flexural strength of the porous silicon nitride ceramics were varied according to the Si/$Si_3N_4$ ratio, size and amount of the pore-forming precursors. Some samples exhibited as high flexural strength as $162\pm24$ MPa. The high strength is considered to result from the fine pore size and the strong bonding among the silicon nitrid particles.

• Transactions of Materials Processing
• /
• v.26 no.6
• /
• pp.372-377
• /
• 2017

In this paper, an effective design procedure was proposed to design the rib of die structure for auto-body member with ultra-high strength steel (UHSS) having ultimate tensile strength (UTS) of 1.5 GPa. From analysis results of the die structure, structural safety of the die was evaluated with information such as displacement and von-Mises stress. It was concluded that the casting part could be designed in order to reduce tool deformation. A design guideline of the die structure was proposed, especially for the rib structure in the casting part with an optimization scheme and local reinforcement concept. Simulation result following the design guideline fully explained that stability of the tool structure could be obtained simultaneously with weight minimization.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1284-1285
• /
• 2006

We reported a P/M soft magnetic material with core loss value of $W_{10/1k}=68W/kg$, which is lower than that of 0.35mm-thick laminated material, by using high purity gas-atomized iron powder. Lack of mechanical strength and high cost of powder production are significant issues for industrial use. In order to achieve both low core loss and high strength by using inexpencive powder, the improvement of powder shape and surface morphology and binder strength was conducted. As the result, the material based on water-atomized powder with 80 MPa of TRS and 108 W/kg of core loss (W10/1k) was achieved.

• The Korean Journal of Ceramics
• /
• v.1 no.4
• /
• pp.214-218
• /
• 1995

Partially stabilized zironia with magnesia (Mg-PSZ) is known as one of the toughest monolithic ceramics. However, the very large grain sizes obtained after sintering at a high solution-heat treatment temperature in the cubic region of the phase diagram limit the strength of this material rather modest. In this study fine-grained Mg-PSZ materials were fabricated by adding TiC particles as a dispersed phase. Samples were hot-pressed at $1750^{\circ}C$ and then annealed at $1420^{\circ}C$ for various times. Grain growth was retarded severely by the TiC particles resulting in grain sizes smaller by more than one order of magnitude than those of PSZ without TiC. The fine-grained microstructure lead to doubly-increased fracture strength while maintaining the same level of high fracture toughness as that of conventional Mg-PSZ without TiC particles.

• Journal of the Korean Society for Heat Treatment
• /
• v.17 no.3
• /
• pp.146-150
• /
• 2004

Because of the social needs for energy saving and the rigid environmental regulation, the development of light materials and new economical manufacturing technologies have been actively investigated. Recently, the hydroforming of high strength aluminum tube has attracted great interest due to its good strength-to-weight ratio, which could play an important role in lightweighting of automobile. However, the limited formability of high strength aluminum alloys is considered to hinder the active application of the hydroforming process. In this paper, the hydroformability of aluminum tubes with different heat treatments was investigated as the basic research of the hydroforming process for the high strength aluminum tubes.

• Korean Journal of Materials Research
• /
• v.18 no.11
• /
• pp.604-609
• /
• 2008

The sintering behavior of zircon with silica was investigated. Zircon with 5 vol% of sedimentation $SiO_2$ resulted in the apparent density of $4.45\;g/cm^3$, the diametral tensile strength of $12.125\;kgf/cm^2$, and the micro Vickers hardness of 1283 HV. The dissociation temperature and mechanical characteristics of the $ZrSiO_4$ were changed with different kinds of $SiO_2$. $SiO_2$ addition prevented dissociation of $ZrSiO_4$. Zircon with 5 vol% of sedimentation $SiO_2$ and with 5 vol% of fused $SiO_2$ resulted in increased diametral tensile strength and increased micro Vickers hardness by suppression of $ZrSiO_4$ dissociation and low temperature liquid $SiO_2$ formation. Zircon with fumed $SiO_2$ and quartz $SiO_2$ resulted in decreased diametral tensile strength and decreased micro Vickers hardness because of cristobalite and quartz phase formation and high temperature liquid $SiO_2$ formation. Zircon with 10 vol% of $SiO_2$ resulted in decreased diametral tensile strength and decreased micro Vickers hardness because of weak particle coupling due to excess formation of liquid $SiO_2$.

• Korean Journal of Materials Research
• /
• v.32 no.10
• /
• pp.442-447
• /
• 2022

Sealing treatment is a post-surface treatment of the plasma spray coating process to improve the corrosion resistance of the coating material. In this study, the effect of the sealing on the corrosion resistance and adhesive strength of the plasma spray-coated alumina coatings was analyzed. For sealing, an epoxy resin was applied to the surface of the coated specimen using a brush. The coated specimen was subjected to a salt spray test for up to 48 hours and microstructural analysis revealed that corrosion in the coating layer/base material interface was suppressed due to the resin sealing. Measurement of the adhesive strength of the specimens subjected to the salt spray test indicated that the adhesive strength of the sealed specimens remained higher than that of the unsealed specimens. In conclusion, the resin sealing treatment for the plasma spray-coated alumina coatings is an effective method for suppressing corrosion in the coating layer/base material interface and maintaining high adhesive strength.