• Composites Research
• /
• v.34 no.2
• /
• pp.88-95
• /
• 2021

VARTM (Vacuum-assisted resin transfer molding) process is a low-cost process technology and affiliated with OoA (Out of Autoclave). Besides, it has been widely used in various fields. However, because of its lower quality than the autoclave process, it isn't easy to apply the VARTM process to the aerospace industry, which requires high reliability. The main problem of the VARTM process is the loss of mechanical properties due to the low fiber volume fraction and high void content in comparison to the autoclave. Therefore, many researchers have studied to reduce void and increase fiber volume fraction. This study examines whether the method of controlling atmospheric pressure could increase the fiber volume fraction and reduce void during the resin impregnation process. Reliability evaluation was confirmed by compressive strength test, fiber volume fraction analysis, and optical microscopy. As a result, it was confirmed that increasing the atmospheric pressure step by step in the VARTM process of impregnating the preform with resin effectively increases the fiber volume fraction and reduces void.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.26 no.2A
• /
• pp.301-310
• /
• 2006

Carbon fiber reinforced polymer (CRFP) materials are well suited to the rehabilitation of civil engineering structures due to their corrosion resistance, high strength to weight ratio and high stiffness to weight ratio. Their application in the field of the rehabilitation of concrete structures is increased due to the vast number of bridges and buildings in need of strengthening. However, RC members, strengthened with externally bonded CFRP plates, happened to collapse before reaching the expected design failure load. Therefore, it is necessary to develop the new strengthening method to overcome the problems of previous bonded strengthening method. This problems can be solved by prestressing the CFRP plate before bonding to the concrete. In this study, a total of 21 specimens of 3.3 m length were tested by the four point bending method after strengthening them with externally bonded CFRP plates. The CFRP plates were bonded without prestress and with various prestress levels ranging from 0.4% to 0.8% of CFRP plate strain. All specimen with end anchorage failed by a plate fracture regardless of the prestress levels while the specimen without end anchorage failed by the separation of the plate from the beam due to premature debonding. The cracking loads was proportionally related to the prestress levels, but the maximum loads of specimens strengthened with prestressed CFRP plates were insignificantly affected by the prestress levels.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.29 no.5A
• /
• pp.519-529
• /
• 2009

Fiber reinforced composite materials have various advantages in mechanical and chemical aspects. Not only high fatigue and chemical resistance, but also high specific strength and stiffness are attained, and therefore, damping characteristics are beneficial to marine piles. Since piles used for marine structures are subjected to compression and bending as well, detailed research is necessary. Current study examine the mechanical behavior under flexural and/or compressive loads using concrete filled fiber reinforced plastic composite piles, which include large size diameter. 25 pile specimens which have various size of diameters and lengths were fabricated using hand lay-up or filament winding method to see the effect of fabrication method. The inner diameters of test specimens ranged from 165 mm to 600 mm, and the lengths of test specimens ranged from 1,350 mm to 8,000 mm. The strengths of the fill-in concrete were 27 and 40 MPa. Fiber volumes used in circumferential and axial directions are varied in order to see the difference. For some tubes, spiral inner grooves were fabricated to reduce shear deformation between concrete and tube. It was observed that the piles made using filament winding method showed higher flexural stiffness than those made using hand lay-up. The flexural stiffness of piles decreases from the early loading stage, and this phenomenon does not disappear even when the inner spiral grooves were introduced. It means that the relative shear deformation between the concrete and tube wasn't able to be removed.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.26 no.3
• /
• pp.223-242
• /
• 2024

Single-shell tunnels, introduced to South Korea in the early 2000s, have not been adopted for the main tunnels of roads or railways over the past two decades despite several attempts starting with the Gwangju City Bypass. This reluctance likely arises from concerns about the long-term performance of supporting materials and the absence of relevant criteria and specifications. However, recent progress, including the incorporation of high-strength shotcrete standards and corrosion-resistant rock bolt specifications, alongside equipment and technique enhancements, necessitates a reassessment of single-shell tunnels. While the single-shell tunnel method offers advantages in environmental impact, construction cost and period compared to the conventional NATM, it is crucial to address the challenges, such as limited design and construction experience, incomplete detailed standards, and insufficient construction specifications, through further research and pilot projects. This paper reviewed the basic principles of single-shell tunnel, current application and research status, technical development trends, criteria and specifications, and remaining challenges. It aims to reignite discussions on the feasibility of applying single-shell tunnels in South Korea.

• Journal of the Korea Institute of Building Construction
• /
• v.9 no.5
• /
• pp.79-86
• /
• 2009

In a steel structure, spray-applied fire resistive materials are crucial in preventing structural strength from being weakened in the event of a fire. The quality control of such materials, however, is difficult for manual workers, who can frequently be in short supply. These skilled workers are also very likely to be exposed to environmental hazards. Problems with construction work such as this, which are specifically the difficulty of achieving quality control and the dangerous nature of the work itself, can be solved to some degree by the introduction of automated equipment. It is, however, very difficult to automate the work process, from operation to the selection of a location for the equipment, as the environment of a construction site has not yet been structured to accommodate automation. This is a fundamental study on the possibility of the automation of spray-applied fire resistive coating work. In this study, the linkability of the cutting-edge RTLS to an automation system is reviewed, and a scenario for the automation of spray-applied fire resistive coating work and system composition is presented. The system suggested in this study is still in a conceptual stage, and as such, there are many restrictions still to be resolved. Despite this fact, automation is expected to have good effectiveness in terms of preventing fire from spreading by maintaining a certain level of strength at a high temperature when a fire occurs, as it maintains the thickness of the fire-resistive coating at a specified level, and secures the integrity of the coating with the steel structure, thereby enhancing the fire-resistive performance. It also expected that if future research is conducted in this area in relation to a cutting-edge monitoring TRS, such as the ubiquitous sensor network (USN) and/or building information model (BIM), it will contribute to raising the level of construction automation in Korea, reducing costs through the systematic and efficient management of construction resources, shortening construction periods, and implementing more precise construction

• Journal of Food Hygiene and Safety
• /
• v.32 no.5
• /
• pp.434-442
• /
• 2017

The UV light in sunlight breaks down the chemical bonds in a polyolefin polymer through a process called photodegradation, ultimately causing cracking, chalking, colour changes, and loss of physical properties such as impact strength, tensile strength, elongation, and others. UV absorbers are used to prevent or terminate the oxidation of plastics by UV light. They are receptive to UV radiation and dissipate the energy harmlessly as heat. Benzotriazoles and benzophenones are used mainly in polyolefins such as polyethylene and polypropylene. In this study, we have developed a method for the analysis of 12 UV absorbers, which are Uvinul 3000, Cyasorb UV 24, Uvinul 3040, Tinuvin 312 and P, Seesorb 202, Chimassorb 81, Tinuvin 329, 234, 326, 328 and 327, migrated from the food packaging materials into four food simulants for aqueous, acidic, alcoholic and fatty foods. The UV absorbers in food simulants were determined by reversed-phase high performance liquid chromatograph-ultraviolet detector with 310 nm after solid-phase extraction with a hydrophilic-lipophilic balance (HLB) cartridge or dilution with isopropanol. The analytical method showed a good linearity of coefficient ($R^2{\geq}0.99$), limits of detection (0.049~0.370 mg/L), and limits of quantification (0.149~1.120 mg/L). The recoveries of UV absorbers spiked to four food simulants ranged from 70.05% to 110.13%. The developed method would be used as a reliable tool to determine concentrations of the migrated UV absorbers.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.6
• /
• pp.263-271
• /
• 2015

Commercial AR(Alkali Resistant)-glass fiber has a good chemical resistant property, but also has a problem of difficulty in fiberizing process because of high viscosity in melted glass compare with E-glass fiber which is the most widely used for reinforced fiber of composite materials. In this study, we fabricated AR-glass fiber with low zirconia contents compare with commercial AR-glass fiber relatively, and measured properties against E-glass fiber. We obtained transparent clear glass with zirconia contents of 0.5~16 wt% by melting at $1600^{\circ}C$ for 2 hours. These AR-glass samples had high visible transmittance of 89~90 %, softening temperature of $703{\sim}887^{\circ}C$. And softening temperatures of them were increased according to the increasing zirconia contents. Compare with E-glass, AR-glass contains 4 wt% zirconia has different value of $-94^{\circ}C$ in softening temperature, $+68^{\circ}C$ at Log3 temperature and $-13^{\circ}C$ at Log5 temperature in viscosity. We could verify good alkali resistant property of the AR-glass fiber with SEM after dipping in alkali solution for 48~72 hours, and also high tensile strength, 1.7 times compare with E-glass fiber at 48 hours and 2.2 times at 72 hours. We conclude that this AR-glass fiber can be widely used as general alkali resistant glass fiber because of easy manufacturing condition and good properties even though it has low zirconia contents.

• Restorative Dentistry and Endodontics
• /
• v.14 no.1
• /
• pp.41-56
• /
• 1989

The purpose of this study was to examine the effect of temperature dependence of the behavior on the physical properties of posterior composite resins. Three light cure posterior composite resins (Heliomolar, Litefil-P, and P-50) and one chemical cure posterior composite resin (Bisfil-II) were used as experimental materials. Composite resin was placed in a cylindrical brass mold (2.5 mm high and 6.5 mm inside diameter) that was rested on a glass plate. Another flat glass was placed on top of the mold, and the plate was tightly clamped together. After the mold had been filled with the light cure composite material, the top surface was cured for 30 seconds with a light source. Chemical cure resin specimens were made in the same manner as above. Three hundreds and twenty composite resin specimens were constructed from the four composite materials. One hundred and sixty specimens of them were placed in a heater at $50^{\circ}C$, $75^{\circ}C$, $100^{\circ}C$, $125^{\circ}C$, $150^{\circ}C$, $175^{\circ}C$ and $200^{\circ}C$ for 5 minutes or 10 minutes respectively before compressive strengths were measured. Another one hundred and sixty specimens were tested for the diametral tensile strengths in the same way as above. They were randomly divided into eight groups according to the mode of heating methods as follows and stored in distilled water at $37^{\circ}C$ for 24 hours. Group $37^{\circ}C$ - specimens were stored at $37^{\circ}C$ in distilled water for 24 hours. Group $50^{\circ}C$ - specimens were heated at $50^{\circ}C$ after curing. Group $75^{\circ}C$ - specimens were heated at $75^{\circ}C$ after curing. Group $100^{\circ}C$ - specimens were heated at $100^{\circ}C$ after curing. Group $125^{\circ}C$ - specimens were heated at $125^{\circ}C$ after curing. Group $150^{\circ}C$ - specimens were heated at $150^{\circ}C$ after curing. Group $175^{\circ}C$ - specimens were heated at $175^{\circ}C$ after curing. Group $200^{\circ}C$ - specimens were heated at $200^{\circ}C$ after curing. Twenty specimens of each of four composite resins were respectively made by insertion of materials into same mold for examining the dimensional changes between before and after heating. The final eighty specimens were stored in distilled water at $37^{\circ}C$ for 24 hours before testing the dimensional changes. Compressive and diametral tensile strengths were measured crosshead speed 1mm/minute and 500Kg in full scale with a mechanical testing machine (DLC 500 Type, Shimadzu Co., Japan). Dimensional changes were determined by measuring the diametral changes of eighty specimens with micrometer (Mitutoyo Co., Japan). Results were as follows: 1. Diametral tensile strengths of specimens in all groups were increased with time heated compared with control group except for that in group $50^{\circ}C$ and the maximum diametral tensile strength was appeared in the specimen of Litefil-P heated for 10 minutes at $100^{\circ}C$. In heliomolar and P-50, it could be seen in the specimen heated for 10 minutes at $150^{\circ}C$, but in Bisfil-II, it could be found in the specimen heated for 5 minutes at $150^{\circ}C$. 2. Compressive strengths of specimens in all groups was tended to be also increased with time heated but that in group $50^{\circ}C$ and the maximum compressive strengths were showed in the same specimens conditioned as the diametral tensile strengths of four composite materials tested. 3. In Heliomolar, Litefil-P, and Bisfil-II, it was decreased in diameters of resin specimens between before heating and increased in diameters of resin specimens after storing in distilled water, but it was not in P-50. 4. There is little difference in diametral tensile strengths, compressive strengths, and dimensional changes followed by heating the resin specimens for 5 minutes and 10 minutes, but there is no statistical significances.

• Journal of the Korean Applied Science and Technology
• /
• v.30 no.4
• /
• pp.575-585
• /
• 2013

This research was performed to evaluate the recycling feasibility as a construction material of dredged harbor soil mixed with clay and glass frit. Concentration of heavy metals of the dredged soil from D harbor was severly high, showing Zn of 526.0~13,150.1 mg/kg. The dredged soil was maily composed of 48.30 wt% $SiO_2$, 16.60 wt% $Al_2O_3$, 10.10 wt% CaO, 7.75 wt% $Fe_2O_3$. The clay and the glass frit contained 70.82 wt% $SiO_2$ and $Al_2O_3$ 18.78 wt%, and 71.75 wt% $SiO_2$, 13.99 wt% CaO, 8.51 wt% $Na_2O$, respectively. After adding 10~40 wt% to the clay and sintering them at $1,000^{\circ}C$ or $1,100^{\circ}C$, the compressive strength of the sintered specimens showed $132.6{\sim}178.5kgf/cm^2$ or $581.2{\sim}793.7kgf/cm^2$, respectively. In case of SC46 with the addition 40 wt% of the dredged soil to the clay, the compressive strength ($793.7kgf/cm^2$) of specimen sintered at $1,100^{\circ}C$ was over 5 times higher than that at $1,000^{\circ}C$. The specimen mixed with 40 wt% of dredged soil, 60 wt% of clay and 1 wt% of glass frit satisfied the 1st grade standard for clay brick by KS L 4201. The results of all specimens by Korean Standard Leaching Test also satisfied the standard criteria.

• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.2
• /
• pp.95-101
• /
• 2019

Purpose: The aim of this study is to evaluate the effects of various primers on the microtensile bond strength (${\mu}TBS$) of resin cements to cobalt-chromium (Co-Cr) dental casting alloy. Materials and methods: Four adhesive primers (Universal primer, Metal primer II, Alloy primer, and Metal/Zirconia primer) and two resin cements (Panavia F2.0, G-CEM LinkAce) were tested. One hundred fifty Co-Cr beams were prepared from Co-Cr ingots via casting ($6mm\;ength{\times}1mm\;width{\times}1mm\;thick$). The metal beams were randomly divided into ten groups according to the adhesive primers and resin cements used; the no-primer groups served as the control (n = 15). After sandblasting with aluminum oxide ($125{\mu}m$ grain), the metal and resin cements were bonded together using a silicone mold. Prior to testing, all metal-resin beams were examined under stereomicroscope, and subjected to the ${\mu}TBS$ test. The mean value of each group was analyzed via one-way ANOVA with Tukey's test as post hoc (${\alpha}=.05$) using SPSS software. Results: The mean ${\mu}TBS$ of all groups was ranged from 20 to 28 MPa. There is no statistically significant difference between groups (P > .05). Mixed failure, which is the combination of adhesive and cohesive failures, is the most prevalent failure mode in both the Panavia F2.0 and G-Cem LinkAce groups. Conclusion: The ${\mu}TBS$ of all tested groups are relatively high; however, the primers used in this study result in no favorable effect in the ${\mu}TBS$ of Panavia F2.0 and G-Cem LinkAce resin cement to Co-Cr alloy.