• Journal of the Korean Society for Heat Treatment
• /
• v.17 no.1
• /
• pp.23-28
• /
• 2004

In this work, the effect of Sc and Mm(misch metal) on the high temperature behavior of Al-Mg alloys was observed. Hardness was increased due to appearance of fine $Al_3Sc$ precipitates. The elongation of Al-Mg-Sc alloy at high temperature was higher than that of Al-Mg-Sc-Mm alloy because Al-Mg-Sc alloy has finer grain sizes than Al-Mg-Sc-Mm alloy. The strain rate sensitivity factor, "m" of Al-Mg-Sc and Al-Mg-Sc-Mm at $475^{\circ}C$ and $1{\times}10^{-2}s^{-1}$ were 0.33 and 0.46, respectively. The activation energy of Al-Mg-Sc and Al-Mg-Sc-Mm alloy for superplastic deformation was 133KJ/mol and 103KJ/mol respectively. The elongation of Al-Mg-Sc alloy at high temperature was decreased by the addition of Mm, but the strength at high temperatures and low strain rate was improved.

• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.701-705
• /
• 2002

High temperature tensile test has been performed at $450^{\circ}C$ at different strain rate with various grain size due to different reduction rate of Al-4wt%Mg-0.4wt%Sc alloy which is known to be one of useful superplastic alloys. The grain size of Al-4wt%Mg-0.4wt%Sc alloy is $67~100\mu\textrm{m}$ which is courser than that of the alloy which is commonly used as the superplastic material. The total elongation of the Al-4wt%Mg-0.4wt%Sc alloy is strongly dependent on the average grain size, and is a linear function of the inverse average grain size for the present alloy.

• Korean Journal of Materials Research
• /
• v.13 no.12
• /
• pp.819-824
• /
• 2003

The Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc alloy exhibited excellent elongation by the new thermomechanical treatment (TMT) process; solution treatment and furnace cooling\longrightarrowhot and cold rolling and then annealing for short time. Tensile test at high temperature from 430 to $500^{\circ}C$ has been performed with various strain rates using for the Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc alloy obtained by the TMT process. The elongation of the Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc was 550% tensile tested at $470^{\circ}C$ temperature and 2.2 $\times$ $10^{-3}$ $s^{-1}$ strain rate. The m value of Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc alloy deformed 85% increased from 0.33 to 0.46 with increasing total elongation. This new TMT process was very simple and easy to make the sheets in the company.