• Carbon letters
• /
• v.12 no.4
• /
• pp.229-235
• /
• 2011

Isotactic polyacrylonitrile (PAN) with triad isotacticity of 0.53, which was determined by $^{13}C$ NMR, using dialkylmagnesium as an initiator, was successfully synthesized. Isothermal treatment of iso-PAN was conducted in air at 200, 220, 250 and $280^{\circ}C$. Structural evolutions and chemical changes were studied with Fourier transformation infrared and wide-angle X-ray diffraction during stabilization. A new parameter $CNF={I_{2240cm}}^{-1}/ ({I_{1595cm}}^{-1}+f^*{I_{1595cm}}^{-1})$ was defined to evaluate residual nitrile groups. Crystallinity and crystal size were calculated with X-ray diffraction dates. The results indicated that the nitrile groups had partly converted into a ladder structure as stabilization proceeded. The rate of reaction increased with treatment temperature; crystallinity and crystal size decreased proportionally to pyrolysis temperature. The iso-conversional method coupled with the Kissinger and Flynn-Wall-Ozawa methods were used to determine kinetic parameters via differential scanning calorimetry analysis with different heating rates. The active energy of the reaction was 171.1 and 169.1 kJ/mol, calculated with the two methods respectively and implied the sensitivity of the reaction with temperature.

• Polymer(Korea)
• /
• v.24 no.5
• /
• pp.646-655
• /
• 2000

Polymerizations of higher $\alpha$-olefins were carried out in toluene by using highly isospecific catalyst, rac-(EBI)M(NMe$_2$)$_2$ (EBI=1,2-ethylenebis-(1-indenyl); M=Zr(rac-1); M=Hf(rac-2)) In the presence of Al(i-Bu)$_3$/[Ph$_3$C][B($C_{6}F_{5}$)$_4$]. The polymerization of high $\alpha$-olefin showed high activity and similar polymerization behavior. The polymerization activity was affected by both monomer size and lateral size of polymer chain. The conversion of monomer to polymer decreases with the increased lateral size in the order of 1-pentene>1-hexene>1-octene>1-decene. The same dependences of melting behavior and intrinsic viscosity of polyolefin on lateral size were observed according to the results obtained by differential scanning calorimetry and intrinsic viscosity. All poly($\alpha$-olefin)s showed very high isotacticity (triad) and the isotacticity increases in the order of poly(1-pentene)$^1H$ NMR and Raman spectra analysis showed that chain transfer to cocatalyst, which generates saturated methyl groups, Is a main chain termination. The $\beta$-hydride eliminations, which generate unsaturated vinylidene, tri-substituted, and vinylene end group. are found to be minor chain terminations.