• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.661-664
• /
• 2008

As architectures have recently become high-risers and megastructured, stable high strength products have been ensured. Accordingly, use of precast concrete accouplement has been increased in order to facilitate air compression and rationalize construction. Since not only external heating but also internal temperature rise caused by the accumulation of cement hydration heat in manufacturing process, precast concrete members with large cross-section used for high-rise mega-structure's columns and beams may exhibit different temperature history compared to the precast concrete members for wall and sub-floor with relatively small cross-sections. Therefore, this study aims to elucidate the characteristics of temperature history of mass concrete members cast with high-strength concrete for precast concrete application. In this study, large cross-sectional precast concrete mock-up, unit cement quantity, and temperature histories in manufacturing precast concrete member under different curing condition were inclusively investigated.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2001.11a
• /
• pp.76-81
• /
• 2001

Recently, the structure is higher and larger, so that the application of high-strength concrete is increased, And as the development of construction skills, it is possible to place during the winter. Concrete work during winter is indispensible to shorten time of completion and cut costs. When concrete work during winter is placed, it has anxiety that concrete freeze at low temperature. As repetition of concrete's freezing cause reduction of durability, it is necessary for mixing to pay attention to air content and W/C ratios. Accordingly, in this study, we estimate the frost resistance by air content and W/C ratios, and development of strength after early-frost damage in the high-strength concrete during the cold weather. In this study, it could be confirmed that factors which were air content, W/C ratios and early curing period, affected on the frost resistance.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.13-16
• /
• 2005

Nanoscale materials are of great interest due to their unique optical, electrical and magnetic properties. Due to the recent amazing achievements in nano technology, new materials were developed. But these nano technology is not apply to the construction part in spite of exellent properties of nano size material. The purpose of this study is to apply to nano technology into building materials. To develop the high performance concrete, nano cement particles is prepared by mechanical method. In the results of this study, the nano silica powder increase effect according to increase of the mixing amount, appeared that compressive strength increased but is limit in increment. For the production of high-strength concrete, nano silica powder was suitable the binder ratio from 20$\%$. And, the compressive strength of concrete are especially dependent on the curing temperature.

• Applied Chemistry for Engineering
• /
• v.8 no.6
• /
• pp.973-978
• /
• 1997

The toughness and morphology of epoxy resin based on diglycidyl ether of bisphenol A(DGEBA) cured with of tris (dimethylaminomethy]) phenol(DMP-30) and castor oil (CO) as a toughening modifier have been studied. Mixtures of CO and an epoxy resin showed a higher miscibility than the classical CTBN modified epoxy resin. The glass transition temperature($T_g$) was decreased with the CO content and the cure temperature. It is interpreted that the networks of epoxy matrix obtained at high temperature are apparently looser and more flexible due to the lower crosslinking density. The toughness was slightly increased with the CO content at $40^{\circ}C$ of curing temperature. The toughness increased with increasing the cure temperature and CO content.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.11
• /
• pp.115-120
• /
• 2021

In this study, cigarettes, which are an essential element in the production of tobacco, are generally not cylindrical. The main materials used for cigarettes are generally hemp and pulp. For the production of cylindrical cigarettes, the cigarettes or cylinders are mounted via gluing. This adhesive is a vinyl acetate emulsion, a high-temperature melt adhesive, and is adhered in a cylindrical shape immediately after being linearly applied to the inner surface of the paper roll or a local part. These adhesives are greatly affected by the atmospheric temperature of the manufacturing space in summer and winter. In the summer, even if the adhesive is temporarily adhered, the coagulation time of the adhesive is long, and problems such as deterioration of the adhesive state occur. in the winter, there is a problem that the temperature of the manufacturing space is low and the adhesive force of the adhesive is poor, resulting in defective adhesive products. In order to solve these problems, another heat transfer device is utilized to cure the remaining adhesive to ensure higher adhesiveness.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.3
• /
• pp.213-218
• /
• 2019

In this study, a high-temperature vulcanizing (HTV) method was used to achieve a shore a hardness of 70. The basic base was composed of 60% silicon gum (GUM) which is a high-viscosity polymer, 30% fumed silica (FS), and 5% of plasticizer. The GUM and FS were mixed well with less than 1% silane to improve rubber strength. Expanded vermiculite was added as a filler at 10%, 15%, and 20%. The curing conditions were $170^{\circ}C$ for 10 min and a molding method was applied. We report herein, the results of inorganic analysis and flame-retardant and tracking tests on the expanded vermiculite. The flame retardance and tracking test outcomes for a shore a hardness of 70 were found to be optimal when the expanded vermiculite content was 10%.

• Journal of Sericultural and Entomological Science
• /
• v.27 no.2
• /
• pp.47-53
• /
• 1985

The studies on the reaction of Urea-Formaldehyde(UF) resin with silk fabric were studied, and the final results summarized as below; 1. The pH and UF molar ratio for preparing liquid resin was found at pH 4-5 and UF molar ration 1:2 and above. 2. The weight gains were increased with respect to increase in concentration of UF resin solution, while moisture regains were decreased. 3. The weight gains were significant high in case of wet pick up 70%. 4. The weight gains were increased with respect to increase in curing temperature and the amount of catalyst((NH4)2SO4) found was 2.5% on the weight of Dimethylol urea and Hydrochloric acid was 1%, Tartaric acid was 10%. 5. The effect of different catalyst on wash fastness of UF resin was good where as in case of acidic catalyst was significantly high. 6. The weight gains with different catalyst was high where as in case of potential acid catalyst was significantly high. 7. The crease recovery are increased with the increase of the weight gain of silk fabric and also stiffness are increased.

• Journal of Advanced Marine Engineering and Technology
• /
• v.22 no.2
• /
• pp.139-145
• /
• 1998

Filament winding method is widely used for composite fabrications using low viscosity liquid for-mation and processing asymmetrical structures of pressure vessel pipe rocket motor case etc. The filament winding method is affected by several parameters such as pot life of process time viscosi-ty of resin filament winding temperature and schedules curing condition and post curing condi-tion of resin. To develope high functional composite materials the rotation(5, 15, 20, 30rpm) of the winding machine was controlled by D.C motor. And the wiper to give proper tension was equipped between strand and resin bath. The resin is hooked by the design wiper. The adequate cure schedule was found by DSC. NOL ring test is carried out to investigate the basic physical properties such as design technology. The void contents in filament winding is generally higher than that of the prepreg laminated plate. These high contents of void can make a crack in resin in spite of low deformation. These problem was solved by giving tension in processing. To improve the characteristics of fiber volume fraction void contents resin/fiber bonding the winding speedc is changed under constant tension. It was found that resin impregnation was not different from in fiber contents void contents at the range of 0.5~1kg tension but it was found that resin was not impregnated at the above of 1.5kg tension. In burst test a pure PE liner was failed at a nozzle part under the $14kg/\textrm{cm}^2$ pressure but a pressure vessel of CNG was failed at a cylinder part under the $200kg/\textrm{cm}^2$ pressure.

• Journal of the Korean Applied Science and Technology
• /
• v.25 no.3
• /
• pp.322-331
• /
• 2008

In order to synthesize high-solid coatings, acrylic resins (HSAs) containing 90% solid content were first synthesized, then the synthesized HSAs were cured with a curing agent, isocyanate, at room temperature to obtain high-solid coatings. In the HSAs synthesis, conversion was in a range of $82{\sim}87%$, and viscosities and number-averaged molecular weight ($M_n$) of the HSAs were in a range of $4380{\sim}8010$ cP and $1540{\sim}1660$, respectively. From the correlation between $T_g$ value, viscosity and $M_n$, it was found that, with increasing $T_g$ value, viscosity increases rapidly and molecular weight increases slowly. From the visco-elasity measured by the pendulum method, it was found that the curing time decreased with increasing $T_g$ values. From the tests of physical properties of the coatings' film, $60^{\circ}$ specular gloss, impact resistance and heat resistance were proved to be good and pencil hardness, drying time and pot-life were proved to be poor.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10a
• /
• pp.571-574
• /
• 2000

When fresh concrete is exposed to low temperature, the concrete may suffer from the frost damage at early ages and the strength development may be delayed. To solve such problems of cold weather concreting admixtures called agent for enduring cold climate are developed to prevent the fresh concrete from being frozen at early ages. In this study, the experiments are carried out on several kinds of agent for enduring cold climate to present their performance. According to experimental results, most kinds of agent for enduring cold climate show the strength development in the range $-5^{\circ}C$ of curing temperature, it tends to be delayed at long term maturity without agents for enduring cold climate. while it gains high strength maturity when agents for enduring cold climate is applied.