• Carbon letters
• /
• 제14권2호
• /
• pp.110-116
• /
• 2013

This study investigated a developed process for producing a composite bipolar plate having excellent conductivity by using coal tar pitch and phenol resin as binders. We used a pressing method to prepare a compact of graphite powder mixed with binders. Resistivity of the impregnated compact was observed as heat treatment temperature was increased. It was observed that pore sizes of the GCTP samples increased as the heat treatment temperature increased. There was not a great difference between the flexural strengths of GCTP-IM and CPR-IM as the heat treatment temperature was increased. The resistivity of GPR700-IM, heat treated at $700^{\circ}C$ using phenolic resin as a binder, was $4829{\mu}{\Omega}{\cdot}cm$ which was best value in this study. In addition, it is expected that with the appropriate selection of carbon powder and further optimization of process we can produce a composite bipolar plate which has excellent properties.

• Carbon letters
• /
• 제13권3호
• /
• pp.151-156
• /
• 2012

This study considered the effect of the heat treatment temperature on the compressive strength of coal powder compacts affected by density, porosity, and crystallinity. Coal powder compacts were made by pressing of milled coal powder and were heat treated at 200, 400, 600, 800, and $1000^{\circ}C$. The density and porosity of the heat treated specimens at each temperature were measured using the Archimedes method and changes in crystallinity were analyzed using Raman spectroscopy. Increases in compressive strength at $600^{\circ}C$ or higher temperatures were proportionally related to increases in the density and the degree of crystallinity.

• 한국세라믹학회지
• /
• 제28권4호
• /
• pp.269-278
• /
• 1991

Fine AlN powder was synthesized by carbothermal reduction and nitridation of alumimun hydroxide prepared from Al-isopropoxide. AlN ceramics with Y2O3 and CaO were prepared by hot-pressing under the pressure of 30 MPa at 180$0^{\circ}C$ for 1 h in N2 atmosphere. Grain boundary behavior and purification mechanism of AlN lattice were examined by heat treatment of AlN ceramics at 185$0^{\circ}C$ for 1-6 h in N2 atmosphere. AlN ceramics without sintering additives showed poor sinterability. However, Y2O3-doped and CaO-doped AlN ceramics were fully densified nearly to theoretical density. As the heat treatment time increased, c-axis lattice parameter increased. This is attributed to the removal of Al2O3 in AlN lattice. This purification effect of AlN attice depended upon the quantity of secondary oxide phase in the inintial stage of heat treatment and the heat treatment time.

• 대한기계학회논문집A
• /
• 제30권3호
• /
• pp.349-355
• /
• 2006

The gas turbine components is used on high temperature conditions which under severely circumstance with start-up and stop several times. Therefore, it is used nickel-base superalloys like and GTD-111DS. Damaged buckets on the t긴ade tip during operating are repaired per 24,000 hr to three times according to repair specification of manufacture. It is applied pre-heat, HIP(hot isostatic pressing) and post-heat treatment to support welding repair on blade tip effectively. On this study, It is utilize of $WRAP^{TM}$ (welding repair advanced process) method to make tension test specimens for this study, And then, material strength and characteristic for GTD-111DS was analyzed.

• 열처리공학회지
• /
• 제22권4호
• /
• pp.217-222
• /
• 2009

The effects of severe plastic deformation by equal channel angular pressing (ECAP) and subsequent heat treatment on the low cycle fatigue behaviors of Al-Mg-Si alloy were investigated. The specimens which were peak aged at $175^{\circ}C$ after solution treatment showed cyclic hardening at all strain amplitudes, while the specimens ECAPed after solution treatment showed cyclic softening at all strain amplitudes during fatigue. The specimens aged at $100^{\circ}C$ after ECAP showed slight cyclic hardening. Various changes of cyclic fatigue behavior after severe plastic deformation and/or heat treatment were discussed in terms of the microstructural changes and precipitation conditions.

• 대한설비공학회:학술대회논문집
• /
• 대한설비공학회 2006년도 하계학술발표대회 논문집
• /
• pp.417-422
• /
• 2006

On trends of 'well-being', heat recovery ventilators(HRV) are recently installed in high rise buildings. HRV is not energy saving instrument but ventilating one. But many people have not been aware of the accurate fact. In this study, performances of HRV are tested under foreign and domestic standards. Especially air-tightness is measured three times by using gas concentration method and pressing equipment. Wet effective ventilating air volume is acquired by solving gas concentration equations. After research air-tightness and effective ventilating air volume must be more focused on than heat transfer efficiency to select the optimal HRV. Heat transfer efficiency must be adjusted by air-tightness results.

• 한국펄프종이공학회:학술대회논문집
• /
• 한국펄프종이공학회 2006년도 PAN PACIFIC CONFERENCE vol.2
• /
• pp.395-400
• /
• 2006

Polylactic acids polymer (PLA) was applied as an additive to improve the strength properties of handsheets prepared from three unbleached southern pine kraft pulps with different kappa number and an aspen bleached chemithermomechanical pulp (BCTMP). The results showed that PLA could greatly improve the tensile and burst strength of the pulp handsheets. Heat pressing effect was also important to enhance the strength properties. For unbleached kraft pulps, it was found that an appropriate amount of residual lignin in pulps had a positive effect on the handsheets strength improvement when adding PLA. The thickness of the handsheet did not change the PLA strengthening effect. In general, PLA effect on tear strength improvement could be neglected. However, it had a significant effect on the improvement of tear strength for the aspen BCTMP handsheets not containing sufficient amount of fines.

• 열처리공학회지
• /
• 제25권3호
• /
• pp.138-145
• /
• 2012

An ${\alpha}$-Ferrite (Fe) powder dispersed with 4 vol.% of $Al_2O_3$ was successfully produced by a simple miling at 210 K with a mixture of $Fe_2O_3$, Fe and Al ingredient powders, followed by 2 step high temperature consolidation: Hot Pressing (HP) at 1323 K and then Hot Isostatic Pressing at 1423 K. The microstructure of the consolidated material was characterized by standard metallographic techniques such as XRD (X-ray Diffraction), TEM and STEM-EDS. The results of STEM-EDS analysis showed that the HIPed materials comprised a mixture of pure Fe matrix with a grain size of ~20 nm and $Al_2O_3$ with a bimodal size distribution of extremely fine (~5 nm) and medium size dispersoids (~20 nm). The mechanical properties of the consolidated materials were characterized by compressive test and micro Vickers hardness test at room temperature. The results showed that the yield strength of the ODS (Oxide Dispersion Strengthened) Fe alloy are as much as $674{\pm}39$ MPa and the improvement of the yield strength is attributed to the presence of the fine $Al_2O_3$ dispersoid.

• 비파괴검사학회지
• /
• 제30권2호
• /
• pp.146-154
• /
• 2010

알루미늄 5052 합금의 탄성특성에 대한 ECAP 강소성변형과 어닐링효과를 연구하였다. 알루미늄 5052 합금은 용체화 처리 후 ECAP 가공하고 어닐링처리를 수행하였다. 탄성계수는 기존의 인장시험과 나노압입시험을 통해 측정하고 음향현미경의 음향재료신호를 이용하여 시료의 표변에서 탄성계수를 측정하였다. 기존의 시험법으로는 불가능한 소성변형과 열처리에 따른 탄성계수의 변화를 음향재료신호를 이용하여 성공적으로 측정하였고 개개의 결정립에서도 결정방위에 의존하는 탄성계수를 얻었다.

• 한국세라믹학회지
• /
• 제54권6호
• /
• pp.518-524
• /
• 2017

A flexible thermoelectric device using body heat has drawn attention as a power source for wearable devices. In this study, thermoelectric thick films were fabricated by cold pressing method using p-type antimony telluride and n-type bismuth telluride powders in accordance with specific loads. Thermoelectric thick films were denser and improved the electrical and thermoelectric properties while increasing the load of the cold pressing. The thickness of the specimen can be controlled by the amount of material; specimens were approximately 700 um in thickness. Flexible thermoelectric devices were manufactured by using the thermoelectric thick films on PI (Polyimide) substrate. The process is cheap, efficient, easy and scalable. Evaluation of power generation performance and flexibility on the fabricated flexible thermoelectric device was carried out. The flexible thermoelectric device has great flexibility and good performance and can be applied to wearable electronics as a power source.