• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.48 no.2
• /
• pp.13-19
• /
• 2016

Moso Bamboo was investigated as the a raw material for pulp and paper industry. Soda-Anthraquinone (Soda-AQ) pulping, elemental chlorine free bleaching was applied. Yield of soda or soda-AQ pulp was 29.3-31.7% with Kappa number 33.0-22.8 with different cooking time or anthraquinone addition at 20% active alkali. In soda or soda-AQ pulping, 81-86% of xylan was removed, which was the main reason for lower pulp yield than hardwood species. Average fiber length of Moso Bamboo soda-AQ pulp was 1.36 mm with $15.5{\mu}m$ fiber width. Soda-AQ pulp from Moso Bamboo (P-3, lowest Kappa pulp) was bleached with 5.5-6.5% of chlorine dioxide charge as D0ED1 bleaching sequence. In 3-stages ECF bleaching, final brightness of 85.3% ISO was achieved with total chlorine dioxide 6.5%.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2003.11a
• /
• pp.148-153
• /
• 2003

The influence of sizing, fiber and pigment type on coating penetration, using commercial paper and two types of handsheets as the base paper which were prepared from thermomechanical pulp(TMP) and hardwood bleached kraft pulp(KP) sized internally with alkyl ketone dimmer(AKD), was studied in terms of characteristics of coating holdout. Laboratory rod draw down coater was used for surface sizing and coating application. Characterization of coating penetration was done by measuring the roughness of the backside of coating layer. The backside of the coating was exposed by dissolving the fibers in a solution of cupriethylenedimine(CED). Data show that internal sizing of base paper is effective and surface sizing is more effective to prevent coating penetration. Comparing between the two types of base papers, backside roughness of coating layer of TMP sheet is much larger and sizing is more effective to reduce coating penetration than those of KP sheet. With regard to pigment type, clay is more effective than calcium carbonate for better coating holdout.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.31 no.4
• /
• pp.93-97
• /
• 1999

Tobacco stalks are greatly produced as annual agricultural wastes. These residues are available approximately 70,000 tons per year. This study was performed to evaluate the potentials of tobacco stalks as a new resource for reconstituent tobacco sheet. Tobacco stalk was more lignified than cereal straws, and had similar chemical constituents to hardwood. Pulping yields by cooling at 170$^{\circ}C$ of dry and green tobacco stalks were 56.7% and 66.3% , respectively. Around 50$^{\circ}$SR freeness level of mixed pulp was adjusted by mixing more than 10% chemical pulp9CP) in the case of dry tobacco stalk and more than 15% CP with wet one. By immersing this handsheet in extracted cooking liquors, reconsitutent sheet contained about 0.28% of nicotines could be prepared. This sheet had enough strength properties for cigarette paper making . In conclusion, it was proved that tobacco stalk could be used to produce the reconstituent tobacco sheet.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.31 no.2
• /
• pp.34-41
• /
• 1999

Adsorption of cationic polyacrylamide dry strength resins onto the surface of papermaking fibers and fines is critical for their effective utilization. Since dry strength resins are frequently employed when recycled fibers containing a great deal of fines are used as a raw material, their adsorption characteristic onto the recycled fiber fines is of great importance. In this study, effects of recycling on adsorption characteristics of cationic polyacrylamide onto primary and secondary fines were examined. Never dried bleached hardwood kraft pulp was beaten and dried for recycling. In each recycling step the adsorption characteristic of a cationic PAM onto primary and secondary fines was evaluated by kjeldahl nitrogen analysis method. The influence of recycling on water retention value and carboxyl content along with the sheet density and tensile strength was examined. Secondary fines of never dried pulp adsorbed twice as much of C-PAM as the primary fines, however, the adsorption capacity of the secondary fines decreased rapidly during the course of recycling and showed lower adsorption capacily than primary fines.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.19 no.1
• /
• pp.64-74
• /
• 2001

This study is to find the effect of the molecular weight distribution of components on the freeness and physical properties of paper by observing the change of properties according the modification of fibers by using production technology and process technology together to develop additives which can effectively control according to the purpose of paper-making process and by combining low molecular weight cellulase (below MW 20,000; CMC activity 400 unit) with different enzyme's molecular weight and activity and high molecular weight cellulase(MW 20,000∼80,000;CMC activity 90,000 unit) and then process them in Sw-BKP(Softwood Bleached Kraft Pulp) and Hw-BKP(Hardwood Bleached Kraft Pulp) and Cotton Linter Pulp and OCC(Old Corrugated Container) with different properties of pore of surface of fibers respectively, since it is judged that making the appropriate composition ratio of components is necessary in consideration of the properties of fibers and paper-making process.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2006.06b
• /
• pp.349-352
• /
• 2006

The conventional pulping processes in Iran were reviewed in this paper. On account of forest resources restriction, a considerable extent of non-harvestable hardwood forests, the possibility of accessable non-wood resources and Poplar fast-growing species for using in pulp and paper industry was investigate. The cultivated area and abundance of each mentioned raw material (Wheat Straw, Sugarcane Bagasse, Poplars) were specified and the quality of their produced papers were compared in strength and opacity properties. Spruce species data was used for experiments comparisons. Regarding to environmental pollutions, low yield, inflexibility in wood and non-wood species resulted from the existent conventional processes of paper manufacturing, APMP is recommended due to high quality paper, desirable opacity properties, high yield and also the usage for all the raw materials.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.47 no.1
• /
• pp.93-101
• /
• 2015

The purpose of this study is to examine the reusability of the fluff pulp recycled from paper diaper. To do this, the physical and optical properties of each handsheet made from these fluff pulp sample as well as the properties of the fiber recycled from paper diaper were analyzed and compared with those of non-recycled diaper fluff pulp samples and conventional pulp samples. These comparisons show that the characteristics of fiber such as length, width, curl, kink of the pulp recycled from paper diaper were similar to those of non-recycled diaper fluff pulp as well as to those of commercial pulp. The fine content of recycled diaper fluff pulp was lower than that of other pulp samples, while the ash content of the former was higher than that of the latter. Furthermore, it was also found that the bulk of handsheets made from the recycled fluff pulp was higher than that of other pulp samples, while the formation of the former was worse than that of the latter. The mechanical properties of the handsheet sample made from the recycled diaper fluff pulp was higher than those of the unused diaper fluff pulp and was lower that those of commercial fluff pulp and softwood tissue pulp handsheet. But, it was higher than that of hardwood tissue pulp handsheet. The optical properties of recycled diaper fluff pulp handsheet was lower than those of each handsheet samples made from other pulps due to its low fine content.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.46 no.4
• /
• pp.69-75
• /
• 2014

Effects of alkali swelling of HwBKP (hardwood bleached kraft pulp) at a low concentration below 2 percent (based on the oven-dried weight of pulp) on handsheet properties were investigated. Swelling treatment of HwBKP was performed at various low NaOH concentrations with/without beating. Then, the changes in handsheet properties were evaluated in terms of bulk, optical and strength properties. It was found that bulk was slightly increased when the alkali concentration was increased. When the pulp was only swollen without beating, paper optical and strength properties was slightly decreased or not changed with alkali concentration. When the pulp was alkali-swollen after beating, paper strength and opacity showed almost no changes while brightness was increased. When the pulp was beaten after NaOH swelling, alkali concentration showed almost no effect on brightness and opacity of paper. Paper strength was slightly decreased with alkali concentration, suggesting that alkali pretreatment before refining could adversely affect refining efficiency.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.42 no.4
• /
• pp.64-70
• /
• 2010

In this study, hemicelluloses were pre-extracted from mixed hardwood chips using sodium hydroxide solution and then they were isolated from pre-extractives by using various solvents. Isolation was conducted by precipitating hemicelluloses with isopropanol, ethanol, 1,4-dioxane, dimethylsulfoxide (DMSO) and potassium hydroxide (KOH), respectively. The precipitate yield on alkali pre-extractives was the highest when hemicelluloses were isolated by DMSO and then precipitated with ethanol. Most precipitates were yellow colored. The efficiency of isolation was evaluated by analysing the characteristics of isolated hemicelluloses. Isolation using DMSO, KOH and 1,4-dioxane ($80^{\circ}C$) showed rather high efficiency. The highest total separation efficiency was about 77% when alkali pre-extractives were reacted with KOH and precipitated with ethanol. The quantity and purity of isolated hemicelluloses were affected by the solvent type.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.43 no.1
• /
• pp.57-64
• /
• 2011

The purpose of this research is to investigate the anatomical and chemical properties of arrowroots for the use of paper fibers. The cells consisting of arrowroots showed certain affinities with those in the fibers and vessels of hardwood. Its parenchyma cells showed different shapes with those of hardwood. It was observed that starch was filled in the multi-shape cells. The average width and length of arrowroot fibers were $15.2{\mu}m$ ($11.1-20.3{\mu}m$) and 1.9 mm (1.49 mm-2.31 mm), respectively. In the chemical characteristics of arrowroots, the contents of cold- and hot-water, alcohol-benzene, and alkali extractives were 12-17%, 15.6%, and 38.8%, respectively. Its chemical composition was 61.3% holocellulose, 15.5% lignin and 2.0% ash.