• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.6 no.4
• /
• pp.80-88
• /
• 1997

An experimental investigation of the fatigue through crack growth behavior under simple stepped variable loading condition has been performed using Al7075-T651. Experiments were carried out by using cantilever bending type specimens, with chevron notches on a small electro-magnetic test machine. Tensile overloads have a retarding effect on the fatigue crack growth rates, therefore tensile overloads were used for the beneficial effect on the fatigue life. While in most cases compressive overloads have only a vanishing effect on crack growth rates, some experiments with single edge crack tension specimens reveal a marked growth retardation. The stress ratios used in this investigations varies from R=0.32 to 0.81, from R=0.04 to 0.76, from R=-0.15 to 0.73, and from R=-0.33 to 0.68 and the peak load for each case was not varied. The crack growth and crack closure were measured by Kikukawa's compliance method with a strain gauge mounted on the backside of each specimens. The results obtained are as follows. When the stepped variable load was applied, the smaller the stress ration was, the larger the delayed retardation of the crack growth rate was. The fatigue crack growh rate data obtained for through cracks were plotted well against the effective stress intensity factor range from 4.0 to 20.0MP{a^{SQRT}m}. It was found that the effective stress intensity factor range ratio was related well to the opening stress intensity factor, the maximum stress intensity factor, and crack length.

• Journal of Ocean Engineering and Technology
• /
• v.1 no.1
• /
• pp.104-110
• /
• 1987

Fatigue tests by axial loading (R = 0.05) were carried out to investigate fatigue crack growth characteristics of small surface cracks in 2 1/4 Cr-1 Mo steel at room temperature by using flat specimens with a small artificial pit. All the data of the fatigue crack growth rate obtained in the present test are determined as a function of the stress intensity factor range about a semi-elliptical crack, so that the application of linear fracture mechanics to the surface fatigue crack growth and to the fatigue crack growth into depth, and all the data obtained from tests were discussed in comparison with the data of Type 304 stainless steel and two type of mild steel under the same test conditions. The obtained results are as follows: 1)When the cycle ratios are same, surface fatigue crack length and its depth are almost same and fall within a narrow scatter band in spite of different stress levels. 2)Relations of the surface fatigue crack growth rate (da/dN) and fatigue crack growth rate into depth (db/dN) to its stress intensity factor range ($\Delta K_{Ia}, \Delta K_{Ib}$) can be plotted as a straight line at log-log diagram without dependence of stress level and coincide with the data of part-through crack in various steels.

• Journal of Ocean Engineering and Technology
• /
• v.14 no.1
• /
• pp.23-28
• /
• 2000

The fatigue crack growth behavior of the cold-rolled STS 304 steel developed for membrane material of LNG storage tank was examined experimentally at 293K, 153K and 111K. The fatigue crack growth rate(do/dN) tends to increase as the stress ratio (R) increases over the testing temperature when compared at the same stress intensity factor range($\Delta$K). The effect of R on do/dN is more explicit at low temperatures than at room temperature. The resistance of fatigue crack growth at low temperatures is higher compared with that at room temperature which is attributed to the extent of strain-induced martensitic transformation at the crack tip. The temperature dependence of fatigue crack growth resistance is gradually vanished with an increase in $\Delta$K which correlates with a decreasing fracture toughness with decreasing temperature. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and low temperature are mainly explained by the crack closure and the strengthening due to the martensitic transformation.

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.6
• /
• pp.185-188
• /
• 2009

The effects of the growth temperature on the properties of ZnO thin films were investigated by using X-ray diffraction, scanning electron microscopy, ultraviolet-visible spectrophotometry, and Hall measurements. The ZnO films were deposited by rf magnetron sputtering at various growth temperatures in the range of 100-$400{^{\circ}C}$. A strong c-axis preferred orientation is observed for all of the samples. As the growth temperature increases, the crystalline orientation of the ZnO (002) plane is not changed, but the full width at half maximum gets smaller. The dependence of the electron concentration, mobility, and resistivity on the growth temperature exhibits that the ZnO films have a higher electron concentration at higher temperatures, thus giving them a low resistivity. The optical transmittance and band gap energy, calculated from the spectra of optical absorbance, show a significant dependence on the growth temperature. As for the sample grown at $100{^{\circ}C}$, the average transmittance is about 90% in the visible wavelength range and the band gap is estimated to be 3.13 eV.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.13 no.4
• /
• pp.174-181
• /
• 2005

In order to investigate the behavior of fatigue crack growth of SiC-particulate- reinforced Al-Si alloy composites, fatigue tests using single edge notched tension(SENT) specimens were performed. Composite materials were manufactured by using both permanent die casting and extrusion processes with different volume fractions of $10\%\;and\;20\%$. $SiC_p-reinfurced$ Al-Si composites showed the increased levels of threshold stress intensity factor range, ${\Delta}K_{th}$, for the increased volume fractions of SiC particles, which implies the increased fatigue crack growth resistance at the threshold or low ${\Delta}K$ levels, compared to the unreinforced Al-Si alloy. In the Paris region, however, the composites showed the increased rate of crack growth resulting in the unfavorable effects on the fatigue crack growth resistance. Critical stress intensity factor range at unstable crack growth leading to final fracture decreased as the volume fraction of SiC particle increased, because of the reduced fracture toughness of the composites. Extruded materials showed higher threshold and critical values than the cast materials.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1997.10a
• /
• pp.120-126
• /
• 1997

This paper examines the crack growth behavior of 7075-T651 aluminum alloy under high-low block loading condition. The cantilever beam type specimen with a chevron notch is used in this study. The crack growth and closure are investgated by compliance method. The applied initial stress ratios are R=-0.5, R=0.0 and R=0.25 Crack length($\alpha$), effective stress intensity factor range(ΔKeff), ratio of effective stress intensity factor range(U) and crack growth rate(d$\alpha$/dN) etc. are inspected fracture mechanics estimate.

• Journal of the Korean Society of Safety
• /
• v.12 no.4
• /
• pp.15-20
• /
• 1997

This study is to investigate the behavior of fatigue crack growth with ATOS 55 steel which can be applied to the commercial car Dump Frame. It is to obtain the material coefficients after tensile and fatigue crack growth test with the variation of thickness or heat treatment. Also, that is proved the Pari's law by experiment. The summarized results are as follows ; 1) Increasing thickness, tensile and yield strength measured highly regardless to heat treatment and measured lowly as variation of heat treatment temperature. 2) Specimen of thickness 8.0㎜ measured the faster of crack growth rate than another thickness according to the results of experiment. It was the different of stress conditions in crack tip. 3) It was found that the experimental constant m was range of 2∼5 to the relationship between fatigue crack growth rate and stress intensity factor range. Also, it was to prove the Paris's law by the experiment.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.7 no.2
• /
• pp.54-61
• /
• 1998

This paper examines the crack growth behavior of 7075-T651 aluminum alloy for small tensile overload under high-low block loading condition. The cantilever beam type specimen with a chevron notch is used in this study. The crack growth and closure are investigated by compliance method. The applied initial stress ratios are R=-0.5 R=0.0 and R=0.25 Crack length, effective stress intensity factor range, ratio of effective stress intensity factor range and crack growth rate etc, are inspected with fracture mechanics estimate.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.04a
• /
• pp.219-222
• /
• 2004

The effects of short fiber and particle hybrid reinforcement on fatigue crack propagation behaviors in aluminum matrix composites have been investigated. Single and hybrid reinforced 6061 aluminum containing same 20 $Al_2O_3\;volume\%$ with four different constituent ratios of short fibers and particles were prepared by squeeze casting method and tested to check the near-threshold and stable crack growth behavior. The fatigue threshold of the composites increased with portion of particle contents and showed the improved crack resistance especially in low stress intensity range. Addition of particle instead of short fiber also increased fracture toughness due to increase of inter-reinforcement distance. These increase in both fatigue threshold and fracture toughness eventually affected the fatigue crack growth behavior such that the crack growth curve shift low to high stress intensity factor value. Overall experimental results were shown that particle reinforcement was enhanced the fatigue crack resistance over the whole stress intensity factor range.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2016.10a
• /
• pp.387-388
• /
• 2016

Among agricultural products, environmental temperature and humidity is an important factor that affects the growth of mushrooms. Mushrooms grow well in a certain temperature range, but if mushrooms deviate from the appropriate temperature range, mushrooms growth and development quality will become worse, and even stop growing. In this paper, the status of the mushroom bacteria, the growth of the mycelium, the occurrence of the fruiting bodies and the growth of the fungus were investigated, o as to provide reference for cultivation management technology of mushroom precise cultivation.