• Textile Coloration and Finishing
• /
• v.28 no.4
• /
• pp.271-279
• /
• 2016

This study deals with antibacterial properties of nylon fiber treated with glycidyltrimethylammonium chloride(GTAC) and silver nanoparticles(AgNPs). Nylon fibers were soaked into GTAC(2-30%, v:v) solution for 20 min. After sample was pre-drying at $80^{\circ}C$ for 10min and cured at $180^{\circ}C$ for 5min. The AgNPs coating was accomplished by soaking in silver colloid solution at $45^{\circ}C$ for 90min. The coated nylon fibers were characterized by scanning electron microscopy-energy dispersive spectroscopy(SEM-EDS). EDS analysis indicated that AgNPs and GTAC was attached on nylon fibers. The treated nylon fibers showed antimicrobial properties against Escherichia coli(ATCC 43895), Pseudomonas aeruginosa(ATCC 13388) and Staphylococcus aureus(ATCCBAA-1707).

• Textile Coloration and Finishing
• /
• v.28 no.2
• /
• pp.70-76
• /
• 2016

Silver nanoparticles(AgNPs) were attached to wool fibers using glycidyltrimethylammonium chloride(GTAC), which is a type of quaternary ammonium salt. GTAC, which contains an epoxy functional group that, under high temperatures, generates a ring-opening reaction with wool fibers, which contain the amine group. Then, the AgNPs are attached to the surface of the GTAC-treated wool fibers by treatment with a silver colloidal solution. The process involves the following procedures: (1) The wool fibers are immersed in the GTAC solution, followed by pre-drying at $80^{\circ}C$ and curing at $180^{\circ}C$ to induce an alteration in the chemical structure; and (2) The wool fibers treated with GTAC are immersed in the silver colloid at $40^{\circ}C$ for 120 min to chemically induce a strong attachment of the AgNPs to the wool fibers. Scanning electron microscopy was used to analyze the influence of the concentrations of GTAC and the silver colloid, as well as the influence of the applied temperature of the silver colloid on the wool fibers, and the influence of the morphological changes in the wool fiber surfaces. As a result, the enhanced concentrations of GTAC and the silver colloid together with an elevated applied temperature of silver colloid have a tendency to increase in Ag atomic%.

• Textile Coloration and Finishing
• /
• v.9 no.1
• /
• pp.33-43
• /
• 1997

This study was carried out to investigate increasing the neutral substantivity of anionic dyes for cationic-modified cotton fabric treatied with cationic agent. In the present study 3-chloro-2-hydroxypropyltrimethyl ammonium chloride for reactive cationic agent was produced by reaction of epichlorohydrine with trimethylamine hydrochloride. 3-chloro-2-hydroxypropyltrimethylammonium chloride was converted in an aqueous solution of sodium hydroxide into glycidyltrimethylammonium chloride. By treating with this epoxy reagent the hydroxyl groups of cotton fabric was modified to trimethylammonium group through ether linkage. The introduction of new cationic sites into cotton fabric by pretreating with cationic agent improves the substantivity of anionic dyes with the cotton in dyebath. Dyeablity of the modified cotton fabric for direct and reactive dyes was much improved in a non-electrolytic or a little electrolytic dyebath and was proportional to the concentration of cationic agent.