• Journal of the Korean Wood Science and Technology
• /
• v.43 no.2
• /
• pp.156-167
• /
• 2015

The aim of this study was to determine the physical and mechanical properties of glued laminated timber (glulam) manufactured from small-diameter logs of three wood species, Acacia mangium (mangium), Maesopsis eminii (manii), and Falcataria moluccana (sengon), with densities of 533, 392, and $271kg/m^3$, respectively. Glulam measuring 5 cm by 7 cm by 160 cm in thickness, width, and length, respectively, was made with three to five lamina, or layers, and isocyanate adhesive. The glulams contained either the same wood species for all layers or a combination of mangium face and back layers with a core layer of manii or sengon. Solid wood samples of the same size for all three species were included as a basis for comparison. Physical-mechanical properties and delamination tests of glulam referred to JAS 234:2003. The results showed that the properties of same species glulam did not differ from those of solid wood, with the exception of the shear strength of glulam being lower than that of solid wood. Wood species affected glulam properties, but three- and five-layer glulams were not different except for the modulus of elasticity. All glulams were resistant to delamination by immersion in both cold and boiling water. The glulams that successfully met the JAS standard were three- and five-layer mangium, five-layer manii, and five-layer mangium-manii glulams.

• Journal of the Korean Wood Science and Technology
• /
• v.47 no.3
• /
• pp.253-264
• /
• 2019

This study characterized the chemical compounds in tannin from mangium (Acacia mangium) bark extract and determined the physical-mechanical properties of glued laminated timber (glulam) made from sengon (Falcataria moluccana), jabon (Anthocephalus cadamba), and mangium wood. The adhesives used to prepare the glulam were based on mangium tannin and phenol resorcinol formaldehyde resin. Five-layer glulam beams measuring $5cm{\times}6cm{\times}120cm$ in thickness, width, and length, respectively, were made with a glue spread of $280g/m^2$ for each glue line, cold pressing at $10.5kgf/cm^2$ for 4 h and clamping for 20 h. Condensed mangium tannin consisted of 49.08% phenolic compounds with an average molecular weight of 4745. The degree of crystallinity was 14.8%. The Stiasny number was 47.22%. The density and the moisture content of the glulams differed from those of the corresponding solid woods with mangium having the lowest moisture content (9.58%) and the highest density ($0.66g/cm^3$). The modulus of rupture for all glulam beams met the JAS 234-2003 standard but the modulus of elasticity and the shear strength values did not. Glulam beams made with tannin had high delamination under dry and wet conditions, but glulam made from sengon and jabon wood met the standard's requirements. All glulam beams had low formaldehyde emissions and were classified as $F^{****}$ for formaldehyde emissions according to the JAS 234 (2003) standard.

• Journal of the Korean Wood Science and Technology
• /
• v.51 no.2
• /
• pp.81-97
• /
• 2023

The aim of this study were to evaluate tannin resorcinol formaldehyde (TRF) for the preparation of cross-laminated timbers (CLTs) made from fast-growing tree species and to analyze the physical and mechanical properties of CLTs. TRF copolymer resin was prepared by using the bark extracts of Swietenia mahagoni (L.) Jacq. It was observed that the TRF adhesive possessed less solid content (23.59%), high viscosity (11.35 poise), and high pH values (10.0) compared to the standard phenol resorcinol formaldehyde. The TRF adhesive was applied to produce CLTs with the addition of 15% tapioca and flour as an extender. The six-layered CLTs were produced from sengon (Falcataria moluccana Miq.), jabon [Anthocephalus cadamba (Roxb) Miq.], coconut (Cocos nucifera L.), and the combination of coconut-jabon and coconut-sengon wood. The analysis of variance revealed that the layer composition of CLT significantly affected the physical and mechanical properties of the beam. While the modulus of rupture met the standard, the moisture content and modulus of elasticity values did not fulfill JAS 1152-2007. All of the CLTs produced in this study demonstrated low formaldehyde emission, ranging from 0.001 mg/L to 0.003 mg/L, thereby satisfying the JAS 1152 for structural glue laminated timber.