• 대한금속재료학회지
• /
• 제46권8호
• /
• pp.516-523
• /
• 2008

The effect of glass-frit size on microstructural evolution and electrical resistance of conductive silver paste was investigated. Silver paste was prepared by mixing 70 wt% commercial silver powder with $1.6{\mu}m$, 3 wt% Bi based glass-frit and 27 wt% organic vehicle. Two different sizes of glass-frit were obtained by ball-milling of commercial glass-frit ($3{\mu}m$) for 3 and 5 days, which had an average particle size of 1.0 and $0.5{\mu}m$. The smaller glass-frit was melt at low sintered temperature and rapidly spread between the silver particles, which is induced the dense networking among silver particles and strong adhesiveness to $Al_2O_3$ substrate. The silver film with smaller glass-frit sintered at $500^{\circ}C$ showed the small pore size and low porosity resulting in low electrical resistivity of $4{\mu}{\Omega}cm$.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2004년도 Asia Display / IMID 04
• /
• pp.558-560
• /
• 2004

We report the effect of wet ball milling conditions on the transparency of glass frit. Generally, the particle size of glass frit decreased as the milling time increased. And the transparency of glass frit changed with the particle size variation. The transparency of glass frit A increased as the milling time increased. But, the transparency of glass frit B, containing high $B_2O_3$ decreased as the particle size decreased. It seems to be the result of chemical reaction with water and glass frit.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 춘계학술대회 초록집
• /
• pp.101.3-101.3
• /
• 2010

Glass frit은 실리콘 태양전지의 Ag/Si contact을 위해 필수적이다. 태양전지의 고효율 특성 구현 때문에, Contact resistance(Rc)가 우수한 Pb-frit의 사용이 불가피한 상황이다. 본 연구는 기존의 Pb계를 무연화함과 동시에 동등수준의 효율을 목표로 하였다. Ag 분말 size 및 glass frit의 열적 거동 특성이 SiNx 코팅층 침투와 Ag re-crystallites에 미치는 영향에 대해 평가하였다. 6 inch 다결정 실리콘 웨이퍼를 사용하였으며, softening temperture(Sp)별로 4종의 Bi계 glass frit을 제조 하였고, 분말 size가 다른 3종의 Ag powder를 선정하였다. Glass frit Sp가 $460^{\circ}C$ 이상의 경우에는 효율이 10% 미만이였으나 Sp $460^{\circ}C$ 이하에서는 16% 수준의 효율을 확인할 수 있었다.

• 한국세라믹학회지
• /
• 제37권6호
• /
• pp.545-551
• /
• 2000

Sintering behaviors of the glass-alumina composites for low firing temperature were investigated as a function of the particle size of glass frit. The system of glass frit was Pb-B-Si-Al-O. The median particle sizes of the glass frits were 2.72$\mu\textrm{m}$, 2.67$\mu\textrm{m}$ and 1.33$\mu\textrm{m}$, which were prepared with changing ball-milling times as 24 h, 48 h and 96 h. The glass-alumina composites showed maximum density at certain temperature, and further heating led to dedensification behaviors, so called over-firing. The sintering temperature, which showed maximum density, raised from 425$^{\circ}C$ to 475$^{\circ}C$ with increase of particle size of glass frit from 1.33$\mu\textrm{m}$ to 2.72$\mu\textrm{m}$. Especially, the over firing behaviors, which were occurred at high sintering temperatures, were greatly increased with decrease of particle size of glass frit.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2004년도 Asia Display / IMID 04
• /
• pp.555-557
• /
• 2004

We report the effect of the particle size (D50) and PSD (Particle Size Distribution) of glass frit on the transparency of transparent dielectric layer of PDP. The milling efficiency of wet milling with water was the best among the dry milling, wet milling with IPA and wet milling with water. The transparency increased with the reduction of particle size of glass frit as the milling time increased. Also the transparency changed by the PSD of glass frit. Glass frits of broad PSD showed high transparency compared with the glass frits of sharp PSD.

• 한국세라믹학회지
• /
• 제46권2호
• /
• pp.175-180
• /
• 2009

Multilayer ceramic capacitors (MLCCs) have continually been made smaller in size and larger in capacity in resent years. However, the end termination electrode is still thick in many MLCCs. In this study, we used small grain glass frit to embody thin film and highly densification in the end termination by improve sintering driving force with well-dispersion and rising surface energy. Pastes were fabricated using size changed glass frit, such as 0.1 ${\mu}m$, 0.5 ${\mu}m$, 1.0 ${\mu}m$, 4.0 ${\mu}m$. Fabricated pastes were applied 05A475KQ5 chip and fired various sintering temperatures to analyze sintering behavior of pastes. Consequently, small glass frit used pastes have many merits than larger, such as well-dispersion, improve cornercoverage and surface roughness, possibility of low temperature sintering. However, we confirmed that small glass frit used pastes have narrow sintering window by rapid completion of sintering densification.

• 한국재료학회지
• /
• 제18권5호
• /
• pp.283-288
• /
• 2008

The effect of sintering aids and glass-frit on the densification and resistivity of silver paste was investigated in an effort to enhance the sintered density and electrical conductivity of the silver electrode. To prepare Pb-free silver paste for use at low sintering temperatures, two commercial silver powders ($0.8\;{\mu}m$ and $1.6\;{\mu}m$ in size) and 5wt.% lab-synthesized nanoparticles (30-50 nm in size) as a sintering aids were mixed with 3 wt.% or 6 wt.% of glass frit ($Bi_2O_3$-based) using a solvent and three roll mills. Thick films from the silver paste were prepared by means of screen printing on an alumina substrate followed by sintering at $450^{\circ}C$ to $550^{\circ}C$ for 15 min. Silver thick films from the paste with bimodal particles showed a high packing density, high densification during sintering and low resistivity compared to films created using monomodal particles. Silver nanoparticles as a sintering aid enhanced the densification of commercial silver powder at a low sintering temperature and induced low resistivity in the silver thick film. The glass frit also enhanced the densification of the films through liquid phase sintering; however, the optimum content of glass frit is necessary to ensure that a dense microstructure and low resistivity are obtained, as excessive glass-frit can provoke low conductivity due to the interconnection of the glass phase with the high resistivity between the silver particles.

• 대한치과기공학회지
• /
• 제31권4호
• /
• pp.25-30
• /
• 2009

Zirconia($ZrO_2$) has attracted much attention in science and technology because of its high refractive index, high melting temperature, hardness, low thermal conductivity and corrosion barrier properties. And it is widely used as the dental restoration material because of its esthetic appearance. In this research, we analyzed the particle size and composition of the imported dental porcelain for zirconia. And the glass frit was produced. To decrease the glass transition temperature and softening temperature of the glass frit, $Li_2O$ was added into it and the effect of $Li_2O$ on the firing temperature was researched. Then the glass which contains leucite crystal with a high coefficient of thermal expansion(CTE) was manufactured and it was mixed with the glass frit to control the CTE. The phase composition were analyzed using the X-ray diffraction. The morphologies of the samples were observed by the scanning electron microscope. The 4wt% $Li_2O$-added glass frit has the optimal glass transition temperature and softening temperature. And 6 wt% leucite crystal was mixed with the glass frit to control the CTE. From the experimental results of crystallization, the crystal phase was found only leucite crystal.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 춘계학술발표대회
• /
• pp.42.2-42.2
• /
• 2011

$TiO_2$ films were modified by adding a glass frit as a light scattering particle and applied to an anode electrode in dye-sensitized solar cells (DSSCs) to enhance the adhesion between $TiO_2$ and fluorine doped transparent oxide (FTO). Low melting point glass frits at contents of (3 to 7wt%) were added to the nano crystalline $TiO_2$ films. The light scattering properties, photovoltaic properties and microstructures of the photo electrodes were examined to determine the role of the low glass transition temperature ($T_g$) glass frit. Electrochemical impedance spectroscopy, Brunauer-Emmett-Teller method and scratch test were conducted to support the results. The DSSC with the $TiO_2$ film containing 3wt% low Tg glass frit showed optimal performance (5.1%, energy conversion efficiency) compared to the $TiO_2$-based one. The photocurrent density slightly decreased by adding 3wt% of the frit due to its large size and non conductivity. However, the decrease of current density followed by the decrease of electron transfer due to the large frit in $TiO_2$ electrode was compensated by the scattering effect, high surface area and reduced the electron transfer impedance at the electrolyte-dye-$TiO_2$ interface. The stability of the photo electrodes was improved by the frit, which chemically promoted the sintering of $TiO_2$ at relatively low temperature ($450^{\circ}C$).

• 한국재료학회지
• /
• 제34권6호
• /
• pp.303-308
• /
• 2024

The semiconductor and display industries require the development of plasma resistant materials for use in high density plasma etching process equipment. Yttria (Y₂O₃) is a ceramic material mainly used to ensure good plasma resistance properties, which requires a dense microstructure. In commercial production, a sintering process is applied to reduce the sintering temperature of Y₂O₃. In this study, the effect of the addition of glass frit to the sintered specimen was examined when manufacturing yttria sintered specimens for semiconductor process equipment parts. The Y₂O₃ specimen was shaped into a Ø50 mm size and then sintered at 1,600 ℃ for 1~8 h. The characteristics, X-ray diffraction pattern, densities, contraction rate of the specimen, and swelling of the surface of the Y₂O₃ specimens were investigated as a function of the sintering time and glass frit addition. The Y₂O₃ specimen exhibited a density of over 4.9 g/cm³ as the sintering time increased, and the swelling phenomenon characteristics were improved by glass frit, by controlling particle size.