• Journal of the Korean Ceramic Society
• /
• v.16 no.3
• /
• pp.178-183
• /
• 1979

The carborundum abrasive specimens bonded with a soda-borosilicate glass were prepared. Samples fired at specified temperatures with various mixing ratio and forming pressure were examined in terms of the structure, bonding strength, and microscopic observations. Increasing the forming pressure up to 400kg/$\cm^2$, the structure became denser in proportion to the forming pressure. The bonding strength was generally increased with increasing the mixing ratio (Vb/Vg), but the bloating phenomena were observed when samples were fired above 95$0^{\circ}C$ with mixing ratio above 20%, consequently, the bonding strength was decreased. Samples fired at the temperature range 900~95$0^{\circ}C$ with mixing ratio 15~30% had the dense structure with various grades.

• Proceedings of the KSR Conference
• /
• 2010.06a
• /
• pp.557-563
• /
• 2010

Mode II interlaminar fracture toughness was measured and fractured surfaces were observed of carbon/epoxy and glass/epoxy woven fabric composites for carbody structure. Woven fabric carbon/epoxy and glass/epoxy composites that made with prepreg and epoxy resin(RS1222) are used in carbody structure of Korean tilting train(TTX) and low floor bus. ENF(End Notched Flexure) specimens having $120mm{\times}20m{\times}5mm$ shape and 35mm initial crack were made with each composites and three point bending tests according to ASTM D790 were conducted for these specimens. Crack lengths in tests were recorded using optical microscope and digital camcorder. NL(Non Linear), 5% offset and Max. load points in load -displacement curves were checked and mode II interlaminar fracture toughness of these points were calculated and compared. Fractured surfaces of specimens were observed using optical microscope and mode II delamination behavior of each composites was discussed.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.2
• /
• pp.128-132
• /
• 1998

2/65/35 PLZT stock solution prepared by Sol-Gel processing was spin-coated on ITO coated glass and annealed by RTA(Rapid Thermal Annealing). The crystal structure of films was reported based on the observation of crystallization process and microstructure of the film fabricated at different fabrication condition. Films were crystallized into rhombohedral structure by annealing at $750^{\circ}C$ for 5 min. As the annealing temperature increased, the size of rosette structure of the films was grown up from $2.4{\mu}m$ to $15{\mu}m$, dielectric constant was increased, coercive field was decreased 33.82 kV/cm, remnant polarization was increased to 39.84 ${\mu}C/cm^2$ and Optical transmittance was decreased.

• Journal of the Korean Ceramic Society
• /
• v.35 no.12
• /
• pp.1257-1265
• /
• 1998

Hertzian contact tests were used to investigate the evolution of fracturedamage in the coating layer as functions of contact load and coating thickness by studying crack patterns in porcelain on glass-infiltrated alumina bilayer system conceived to simulate the crown structure of a tooth. Cone cracks initiated at the coating top surface without delamination at interface and crack propagation to substrate. Preferentially the cracks made multi-cracks at the coating top surface rather than proceeding to interface. The cracks were highly stabilized with wide ranges between the loads to initiate first cracking and to cause final failure im-plying damage-tolerant capability. Finite element modelling was used to evaluate the stress distribution. Maximum tensile stress were responsible for the cracking at the coating layer and had a profound influence on the crack pattern and fracture damage in the layered structure materials.

• Journal of the Korean Geotechnical Society
• /
• v.27 no.11
• /
• pp.83-92
• /
• 2011

The random and heterogeneous pore structure is a significant factor that dominates physical and mechanical behaviors of soils such as fluid flow and geomechanical responses driven by loading. The characterization method using non-destructive testing such as micro X-ray CT technique which has a high resolution with micrometer unit allows to observe internal structure of soils. However, the application has been limited to qualitatively observe 2D and 3D CT images and to obtain the void ratio at macro-scale although the CT images contain enormous information of materials of interests. In this study, we constructed the 3D particle and pore structures based on sequentially taken 2D images of glass beads and quantitatively defined complex pore structure with void cell and void channel. This approach was enabled by implementing image processing techniques that include coordinate transformation, binarization, Delaunay Triangulation, and Euclidean Distance Transform. It was confirmed that the suggested algorithm allows to quantitatively evaluate the distribution of void cells and their connectivity of heterogeneous pore structures for glass beads.

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.194-198
• /
• 2002

Various composition of $K_2O{\cdot}CaO{\cdot}P_2O_5$ glasses were studied by melting process to identify glass forming region. Thermal properties were observed by DSC and TG-DTA, structural properties were investigated by FT-IR and Raman Spectroscopy. The glass transition temperature (Tg) and softening temperature (Ts) were decreased with increasing $K_2O\;and\;P_2O_5$ contents. The basic structural unit of phosphate glasses is the $PO_2\;and\;PO_4^{3-}$ groups to make a cross-link and P-O-P group to form skeleton structure. As CaO content was increased, the P-O-P field strength in these glass was increased and intensity of $PO_2\;and\;PO_4^{3-}$ stretch was decreased.

• Analytical Science and Technology
• /
• v.25 no.1
• /
• pp.3-6
• /
• 2012

$xZrO_2-(1-x)SiO_2$ glass precursor with relatively high concentration of zirconium propoxide in metal alkoxide solution was obtained by sol-gel method and then heated at various temperature from 500 to $1,100^{\circ}C$ to investigate the effect of the thermal treatment on the crystalline structure of the glass precursor. Based on X-ray diffraction analysis, the crystalline peak was started to develop at temperature higher than $600^{\circ}C$, and the crystalline phase was considerably increased at $850^{\circ}C$ or higher. With increasing the thermal treatment temperature, the characteristic peaks, such as baddelyite, tetragonal-$ZrO_2$ and zircon, was shown at $35^{\circ}$, $50^{\circ}$ and $60^{\circ}$ of $2{\theta}$.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1514-1516
• /
• 1999

This paper covers our efforts to improve the low carrier mobility and light instability of hydrogenated amorphous silicon (a-Si:H) films with microcrystalline silicon $({\mu}c-Si)$ films. We successfully prepared ${\mu}c-Si$ films on $CaF_2$/glass substrate by decomposition of $SiH_4$ in RPCVD system. The $CaF_2$ films on glass served as a seed layer for ${\mu}c-Si$ film growth. The XRD analysis on $CaF_2$/glass illustrated a (111) preferred $CaF_2$ grains with the lattice mismatch less than 5 % of Si. We achieved ${\mu}c-Si$ films with a crystalline volume fraction of 61 %, (111) and (220) crystal orientations. grain size of $706\AA$, activation energy of 0.49 eV, and Photo/dark conductivity ratio of 124. By using a $CaF_2$/glass structure. we were able to achieve an improved ${\mu}c-Si$ films at a low substrate temperature of $300^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.21 no.4
• /
• pp.349-354
• /
• 1984

The purpose of present study is to find the structure crystallization mechanism and physical properties in $TiO_2$ containing lead zinc borosilicate glass system. The experiments such as differential thermal analysis infrared spectral analysis. X-ray diffraction analysis and thermal expansion measurements have been done. Differential thermal analysis of coarse and fine glass powder showed bulk nucleating mechanism for high $TiO_2$ containing glasses and surface nucleation mechanism for low $TiO_2$ containing glasses. The prepared glasses crystallized to crystalline mixture of PbO.2ZnO. $B_2O_3$ .4PbO.2ZnO.$5B_2O_3$and 2PbO.ZnO.$B_2O_3$ when heat-treated in the range of 480 and 51$0^{\circ}C$ and crystallized to PbTiO3 when heat-treated at $600^{\circ}C$. Obtained crystalline phase of $PbTiO_3$ in glass matrix strongly affects to thermal expansion coefficient and the value of crystallized glass varied 68.0 to $107.1{\times}10-7$/$^{\circ}C$ depending on the amount of $TiO_2$added. Infrared spectral analysis showed that [$BO_3$] triangle and [$BO_3$] tetrahedral units were coexisted in the glass with high content of PbO.

• The Journal of the Acoustical Society of Korea
• /
• v.16 no.5
• /
• pp.12-17
• /
• 1997

In this work, we developed a new type ultrasonic dehumidifier with piezoelectric ceramics, which and efficiently repel waterdrops on outdoor glass plates exposed to raindrops. Through finite element analysis of a certain type of glass plates to analyze its dynamic behavior, the structure of the ultrasonic device we determined to get the optimal performance. A supplemental metal plate was attached to the glass plate for uniform cleaning. Based on the theoretical results, experimental samples were fabricated and evaluated with various dimensions of the glass plate and the piezoceramic vibrator. Driving circuit for the dehumidifier made use of the frequency sweeping technique to keep track of the resonant frequency of the glass plate that was variant with environmental conditions.