• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.363-364
• /
• 2005

LTCC(low temperature co-fired ceramics)용 glass/ceramic 복합체를 제조하기 위해 3종류 의 glass를 선정하고 filler로 $Al_2O_3$ 와 $TiO_2$를 사용하여 glass frit에 따른 소결 및 유전 특성에 대하여 조사하였다. Glass frit은 lead-borosilicate(PBS), zinc-borosilicate(ZBS), bismuth-borosilicate(BBS) glass 조성을 사용하였고 1100~$1400^{\circ}C$에서 melting시킨 후 quenching하여 frit화하였다. $Al_2O_3$와 $TiO_2$ filler에 10~50 vol%로 glass frit을 각각 혼합한 후 600~$950^{\circ}C$에서 2시간 동안 소결한 결과 50 vol% glass frit 일 때 $900^{\circ}C$ 이하에서 소성이 가능하였다. 유전특성은 $900^{\circ}C$에서 $Al_2O_3$-50vol%PBS($\varepsilon_{r}$=8.8, $Q{\times}f_o$=4,900, $\tau_f$=-24), $Al_2O_3$-50vol% ZBS($\varepsilon_{r}$=5.7, $Q{\times}f_o$=17,800, $\tau_f$=-21), $Al_2O_3$-50vol%BBS($\varepsilon_{r}$=11.1, $Q{\times}f_o$= 2,080, $\tau_f$=-48), $TiO_2$-50vol%PBS($\varepsilon_{r}$=18.6, $Q{\times}f_o$=3,800, $\tau_f$=+135), $TiO_2$-50vol%ZBS($\varepsilon_{r}$=36.4, $Q{\times}f_o$= 7,500, $\tau_f$=+159), $TiO_2$-50vol%BBS($\varepsilon_{r}$=56.4, $Q{\times}f_o$=520, $\tau_f$=+119)을 나타내었다. 따라서 LTCC용 기판재료 및 마이크로파 유전체로 응용이 가능한 것으로 확인되었다.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.4
• /
• pp.63-70
• /
• 2011

Anorthite forming glass frits in amounts up to 25 vol% of the silver powder were added to improve the adhesion between the conductor pattern formed by thick film photoimageable process and the low temperature co-fired ceramics (LTCC) substrate. The sheet resistance of the conductor pattern was raised from 0.13 ${\Omega}/{\square}$ to 2.25 ${\Omega}/{\square}$ as the volume percentage of glass frit increased up to 25 vol%. The adhesion strength was improved with this glass frit increase, but it decreased when the glass content exceeded 20 vol% which are possibly attributed to the liquid pool effect and the reduced fracture toughness in the interface between conductor and LTCC layer. The shrinkage of the width of the conductor pattern decreased with the addition of glass contents.

• Korean Journal of Materials Research
• /
• v.22 no.12
• /
• pp.669-674
• /
• 2012

Yellow phosphor dispersed color conversion glasses are promising phosphor materials for white LED applications because of their good thermal durability, chemical stability, and anti-ultraviolet property. Six color conversion glasses were prepared with high Tg and low Tg specimens of glass. Luminous efficacy, luminance, CIE (Commission Internationale de l'Eclairage) chromaticity, CCT (Correlated Color Temperature), and CRI (Color Rendering Index) of the color conversion glasses were analyzed according to the PL spectrum. Color conversion glasses with high Tg glass frit, sintered at higher temperature, showed better luminous properties than did color conversion glasses with low Tg glass frit. The characteristics of the color conversion glass depended on the glass composition rather than on the sintering temperature. The XRD peaks of the YAG phosphor disappeared in the color conversion glass with major components of $B_2O_3$-ZnO-$SiO_2$-CaO and, in the XRD results, new crystalline peaks of $BaSi_2O_5$ appeared in the color conversion glass with major components of $Bi_2O_3$-ZnO-$B_2O_3$-MgO. The characteristics of CIE chromaticity, CCT, and the CRI of low Tg color conversion glasses showed worse color properties than those of high Tg color conversion glasses. However, these color characteristics of low Tg glasses were improved by thickness variation. So color conversion glasses with good characteristics of both luminous and color properties were attained.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.468-470
• /
• 2004

CNT pastes with different inorganic binder such as glass frit and spin on glass (SOG) were synthesized by using multi-walled nanotube (MWNT) grown by CVD. The uniformity of cathode layer after firing was enhanced and the emission current density at an applied field of 7.95V/${\mu}m$ increased from 133${\mu}A$/$cm^2$ to 265${\mu}A$/$cm^2$ when inorganic binder changed from glass frit to SOG. The emission properties of CNT pastes with SOG were stable and uniform although firing was carried out at relatively high temperature of 450$^{\circ}C$ under air. It is concluded that SOG is more suitable inorganic binder than glass frit for field emission application.

• Journal of Information Display
• /
• v.2 no.4
• /
• pp.34-38
• /
• 2001

We suggested new PDP packaging technology using the direct joint method, which does not need an exhausting hole and tube. The advantages of this method are simple process, short process time and time panel package. To packaging, we drew the seal line of glass frit by dispenser followed by forming the lump, which provide pumping-out path during the packaging process. And, we have performed a pretreatment of glass frit to reduce the out-gases. After which, both front and rear glass plates were aligned and loaded into vacuum packaging chamber. The 4-inch monochrome AC-PDP was successfully packaged and fully emitted with brightness of 1000 $cd/m^2$. Also, glass frit properties for pretreatment condition was investigated by AES and SEM analyses.

• Korean Journal of Materials Research
• /
• v.8 no.11
• /
• pp.1005-1010
• /
• 1998

실험계획법을 이용하여 유리분말의 소결시 그 기공량에 영향을 미치는 각종 소결조건의 영향을 정량적으로 조사하였다. 본 실험범위내에서 결합제 유리의 총기공량, 개기공량 그미고 폐기공량은 모두 소결온도에 의해 가장 큰 영향을 받고 그 다음으로 소결온도에서의 유지시간에 의해 영향을 받으며 승온속도의 경우 그 영향이 상대적으로 미미함을 확인할 수 있었다. 이러한 결과들로부터 실제공정에 있어 승온속도보다는 다른 소결인자, 특히 소결온도를 조절하는 것이 결합제 유리의 기공량 조절에 가장 중요하리라 판단되며 실험계획법을 이용함으로써 보다 정확한 공전조건을 모색할 수 있었다.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.149.2-149
• /
• 2003

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.3
• /
• pp.181-185
• /
• 2016

One of the important issues for fabricating the microelectronic display devices such as FED, PDP, and VFD is to obtain a high vacuum level inside the panel. In addition, sustaining the initial high vacuum level permanently is also very important. In the conventional packing technology using a tabulation method, it is not possible to obtain a satisfiable vacuum level for a proper operation. In case of FED, the poor vacuum level results in the increase of operating voltage for electron emission from field emitter tips and an arcing problem, resultantly shortening a life time. Furthermore, the reduction of a sealing process time in the PDP production is very important in respect of commercial product. The most probable method for obtaining the initial high vacuum level inside the space with such a miniature and complex geometry is a vacuum in-line sealing which seals two glass plates within a high vacuum chamber. The critical solution for the vacuum sealing is to develop a frit glass to avoid the bubbling or crack problems during the sealing process at high temperature of about $400^{\circ}C$ under the vacuum environment. In this study, the suitable frit power was developed using a mixture of vitreous and crystalline type frit powders, and a vacuum sealed CNT FED with 2 inch diagonal size was fabricated and successfully operated.

• Journal of the Korean Ceramic Society
• /
• v.44 no.10
• /
• pp.548-553
• /
• 2007

Ceramic green sheets consisting Bi-based glass frit were fabricated for an application to PDP transparent dielectric front panel. The dispersion condition of the slurry for tape casting was pre-examined, and two kinds of hinder and plasticizer were used in the non-aqueous slurry system. In the fabrication process for the frit film, the properties such as dry and firing shrinkage, elongation, and transmittance were examined at the condition of various mixing ratio of plasticizers. In the mixing ratio of polyethylene glycol to dibutyl phthalate of 3:5wt%, a good adhesion, elongation and transmittance were observed at the firing temperature of $580^{\circ}C$. The photograph for the cross section of the interface was also showed a dense microstructure.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.307-307
• /
• 2008

전자부품에서 기존에 봉착, 코팅, 결합용 glass frit로 사용되어 왔던 Pb계 glass frit는 낮은 융점을 가지고 있고, 화학적으로도 매우 안정한 특성을 가지고 있다. 그러나 Pb계 glsss frit은 환경에 심각한 문제를 초래하기 때문에 이를 대체하기 위하여 저온에서 소성이 가능한 인산주석계를 기본조성계로 설정하였다. 인산주석계 glass의 취약한 내화학성, 내수성과 SnO의 환원에 의한 결정 석출 등의 문제를 해결하기 위하여 $R_2O_3$, RO 등을 첨가하여 glass frit의 특성을 향상시키고자하였다. 수분에 취약한 $P_2O_5$계 glass의 $R_2O_3$를 첨가하여 항온항습기를 이용하여 흡습성을 측정하고, 내수성에 가장 안정한 특성을 보이는 SnO-$P_2O_5-R_2O_3$ 계 glass 조성에 RO를 첨가하여 RO 첨가량에 따른 내산성과 내알칼리성의 변화를 관찰하였다. SnO-$P_2O_5-R_2O_3$계 glass의 RO첨가량에 따른 melting 특성의 변화를 flow-button test를 통해 관찰하였다. SnO-$P_2O_5-R_2O_3$계는 RO계의 변화에 따라 전이온도가 증가하고, 열팽창계수가 감소하는 결과를 보였다.