• 한국전기전자재료학회논문지
• /
• 제17권5호
• /
• pp.541-544
• /
• 2004

Multi- wall carbon nanotubes(MWNTs) were synthesized by thermal chemical vapor deposition. The paste for screen printing was composed of MWNTs, organic vehicle and glass frit. Carton nanotube paste was screen-printed on ITO(indium tin oxide) deposited soda lim을 glass, and then heat treatment was performed. Before the surface treatment, turn on field of derive was 2.6 V/$\mu\textrm{m}$. After the surface treatment, the value was changed into 1.8 V/$\mu\textrm{m}$. The anode current of the derive with 2.83 V/$\mu\textrm{m}$(turn on field) was changed 4 $\mu\textrm{A}$ into 390 $\mu\textrm{A}$ at 1,700 V. Adsorption effect of MWNTs onto phosphor of anode plate was observed by the field emission measurement and resulted in bad effects on properties of devices lifetime and emission lighting.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.431-432
• /
• 2007

In this study, we used screen printing on the rear glass with silver electrodes, phosphor and a dielectric which is on the silver electrodes, and carried out firing in the temperature of $550^{\circ}C$, $570^{\circ}C$, $450^{\circ}C$ each. To seal the rear and top glass together, we used crystalline frit paste as a sealing material with dispenser and carried out firing up to $450^{\circ}C$. As using this panel, we focused on optimizing the condition which influences characteristics of discharging by the distance between electrodes, electrode structure, type and pressure of gases for FFL.

• 한국세라믹학회지
• /
• 제45권8호
• /
• pp.459-463
• /
• 2008

$P_2O_5-SnO_2$ system $0.5SnO_2-xP_2O_5-(0.5-x)B_2O_3$(x=0.1, 0.2, 0.3, 0.4, 0.5) glasses have been prepared for Pb-free low temperature glass frit. A investigation about the effect of $B_2O_3$ substitution on properties of $P_2O_5$ glasses, including glass structure properties, thermal properties, and mechanical properties was presented. Substance that is responsible for in moisture absorption existing circumstances supposes by phosphate, and excess moisture tolerance that state funeral's structure is improved breaking does not affect in state funeral bond that only most single bond remains, and can know that does not suffer big impact in boric oxide anomaly present state. This phenomenon estimates that connect with structure change. It is thought according to link this result the phosphoric acid happened structural change. $B_2O_3$ displacement quantity 0.3 mole put out $BO_4$ structures, but above 0.3 mole it changed with the case $BO_3$ structure which it displaces.

• 한국세라믹학회지
• /
• 제48권1호
• /
• pp.63-68
• /
• 2011

The investigation is directed to lead free (Pb-free) frits that can be used for organic light emitting diode, plasma display screen devices and other sealing materials. $P_2O_5$-SnO system glasses have been prepared for Pb-free low temperature glass frit. Structure and properties of the glasses with the composition SnO-$xB_2O_3-(60-x)P_2O_5$ (x=0, 5, 10, 15, 20, 25, 30, 35, 40 mol%) were characterized by infrared spectra (IR), X-ray diffraction(XRD), Density, Molar volume, Thermo mechanical analysis(TMA) and weight loss after immersion test. Glass transition temperature($T_g$), dilatometric softening temperature($T_d$) and chemical durability increased, and coefficient of thermal expansion($\alpha$) decrease with the substitution of $B_2O_3$ for $P_2O_5$ in the range of 0~25 mol%.

• 한국세라믹학회지
• /
• 제50권6호
• /
• pp.454-459
• /
• 2013

Recently, remote phosphors have been reported for application to white LEDs to provide enhanced phosphor efficiency compared with conventional phosphor-based white LEDs. In this study, a remote phosphor was produced by coating via screen printing on a glass substrate with different numbers of phosphor coating. The paste consists of phosphor, lowest softening glass frits, and organic binders. The remote phosphor could be well controlled by varying the phosphor content rated paste. After mounting the remote phosphor on top of a blue LED chip, CCT, CRI, and luminance efficiency were measured and values of 5300 K, 62, and 117 lm/W were respectively obtained in the 80 wt% phosphor with 3 coating layers sintered at $800^{\circ}C$.

• 한국전기전자재료학회논문지
• /
• 제26권8호
• /
• pp.614-619
• /
• 2013

Recently, remote phosphor is reported for white LED enhancing of phosphor efficiency compared with conventional phosphor-based W-LED. In this study, Remote phosphor was produced by screen printing coating on glass substrate with phosphor contents rated paste and heat treatment. The paste consists of phosphor, lowest softening glass frit and organic binders. Remote phosphor can be well controlled by varying the phosphor content rated paste. After mounting remote phosphor on top of blue LED chip, CCT, CRI, and luminance efficiency were measured. The measurement results showed that CCT, CRI, and luminance efficiency were 6,645, 68, and 1,16l m/W in phosphor 80 wt.% remote phosphor sintered at $600^{\circ}C$.

• 한국세라믹학회지
• /
• 제51권6호
• /
• pp.533-538
• /
• 2014

Today, silicon and epoxy resin are used as materials of conversion lenses for white LEDs on the basis of their good bonding and transparency in LED packages. But these materials give rise to long-term performance problems such as reaction with water, yellowing transition, and shrinkage by heat. These problems are major factors underlying performance deterioration of LEDs. In this study, in order to address these problems, we fabricated a conversion lenses using glass, which has good chemical durability and is stable to heat. The fabricated conversion lenses were applied to a remote phosphor type. In this experiment, the conversion lens for white LED was coated on a glass substrate by a screen printing method using paste. The thickness of the coated conversion lens was controlled during 2 or 3 iterations of coating. The conversion lens fabricated under high heat treatment temperature and with a thin coating showed higher luminance efficiency and CCT closer to white light than fabricated lenses under low heat treatment temperature or a thick coating. The conversion lens with $32{\mu}m$ coating thickness showed the best optical properties: the measured values of the CCT, CRI, and luminance efficiency were 4468 K, 68, and 142.22 lm/w in 20 wt% glass frit, 80 wt% phosphor with sintering at $800^{\circ}C$.

• 한국결정성장학회지
• /
• 제16권2호
• /
• pp.82-87
• /
• 2006

붕규산염계 유리 프리트에 중금속이 다량 함유된 전기로 EAF dust(전기로 제강분진, 이하 더스트)를 $10{\sim}80wt%$ 범위로 첨가한 후 용융하여 유리 시편을 얻었다. 제조된 유리의 DTA분석 결과로부터 유리전이온도, $T_g$가 $550^{\circ}C$ 부근임을 확인하였고 이로부터 결정화에 필요한 열처리 조건을 $700^{\circ}C$/10 hr으로 정하였다. 더스트 첨가량이 70wt% 이상인 유리시편은 XRD 분석 결과 spinel 결정 피크만이 나타났으며, 결정화 시편의 경우, 더스트 첨가량이 40wt% 이상부터 spinel 결정이, 80wt% 부터는 spinet과 willemite 피크가 함께 검출되었다. XRD 분석으로는 결정상이 검출되지 않았던 조성의 유리시편에서도 aspect ratio=$0.7{\sim}1.0$인 수십 nm 크기의 결정상 존재가 SEM으로 확인되었고 결정화 시편에서도 더스트 함량이 l0wt%부터 결정상이 관찰되었다. 결정화 시편에서 관찰된 결정상은 그 형태와 분포가 첨가량에 따라 다양하고 비균일 하였으나 더스트 첨가량이 70wt%인 시편에서는 aspect ratio가 1에 가까운 6면체 형상을 나타내었다.

• 한국세라믹학회지
• /
• 제41권11호
• /
• pp.851-857
• /
• 2004

전기로 제강분진(EAF dust)이 첨가된 규산염 유리, 붕규산염 유리 그리고 납규산염 유리 내의 중금속 안정화 특성을 독성용출 시험법(TCLP)으로 조사하였다. 또한 XRD와 FT-IR 방법을 통하여 EAF dust 첨가량에 따른 유리의 구조변화가 TCLP 결과에 미치는 영향을 고찰하였다. 모유리에 EAE dust를 30 wt%까지 첨가하여도 규산염 유리, 붕규산염 유리, 납규산염 유리 계열의 시편 모두 결정화가 발생되지 않고 비정질을 나타내었다. TCLP법에 의한 유리시편의 중금속 용출량은 EAF dust의 첨가량과 함께 증가되었다. 중금속 용출이 가장 적은 시편은 규산염 유리 계열이었으며 납규산염 유리 계열의 시편은 붕규산염 유리 계열에 비해 중금속 용출량이 상대적으로 적었다. 단, 납규산염 유리 계열 모유리 조성에 포함되어 있는 납의 영향으로 Pb용출은 납규산염 유리 계열시편에서 가장 많았다. Oxygen/network former ratio 값을 이용하여 같은 계열 시편 간의 화학적 내구성을 비교할 수 있었으나 다른 계열 시편 간에는 적절치 않았다. EAF dust가 첨가되면 규산염 유리 계열의 시편에서는 유리구조 내 Si-O-Si 대칭성이 감소되고 비가교 산소가 증가되어 유리의 구조를 약화시키고 화학적 내구성을 감소시켰다 붕규산염 유리 계열 시편에서 EAF dust가 첨가되면 tetraborate group이 diborate group으로 변화되고 2차원 층상구조인 pyre-와 ortho-borate도 형성되어 결국 구조약화를 가져왔다. 3가지 계열의 유리조성 중에서 EAF dust내의 중금속들을 안정화하는데 가장 적합한 것은 규산염 유리 계열의 시편으로 판단되었다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 추계학술발표강연 및 논문개요집
• /
• pp.195-195
• /
• 2003

PDP, FED 등의 디스플레이와 각종 IC 칩부품에 적용 가능한 저융점 유리 프릿 중에서 환경규제가 이루어지고 있는 납성분이 포함되어 있지 않은, Bi계 유리 프릿의 열적 거동 연구를 행하였다. 열처리 온도에 따른 열거동에 따라 프릿의 소성온도 및 미세구조가 결정되므로, 열처리 온도에 따른 유리 프릿의 젖음각을 측정하였고, DTA와 TMA를 통해 유리전이온도, 연화점, 열팽창계수 변화 경향성을 관찰하였다. 본 연구에서 제조된 유리는 조성에 따라 전이온도가 390-50$0^{\circ}C$, 연화점이 400-55$0^{\circ}C$, 열팽창계수가 65-120$\times$10-7/$^{\circ}C$ 범위를 나타내었으며, 고온현미경 측정 결과 Pb-계 유리와 비교시 유사한 열거동을 나타내었다.