• Corrosion Science and Technology
• /
• v.20 no.6
• /
• pp.367-372
• /
• 2021

The effect of carbon addition on the general corrosion behavior of high-chromium cast iron (HCCI) was studied by a scanning electron microscope with energy dispersive spectroscopy (SEM-EDS) or electron back-scattered diffraction (EBSD), or electrochemical polarization techniques in 0.1 mol dm^-3 H₂SO₄ + 0.05 mol dm^-3 HCl at room temperature. The addition of 2.1-2.8 wt% carbon to HCCI increased the fraction of eutectic austenite and eutectic carbide phases, while that of HCCI decreased the fraction of the primary austenitic phase. Potentiostatic polarization of the HCCI at -0.35 V_SSCE or 0.0 V_SSCE resulted in preferential general corrosion of the primary austenitic or eutectic austenitic phases, respectively. The decrease in corrosion current density and the shift in noble corrosion potential direction with increasing carbon content in the HCCI indicated that the fraction and the chemical composition of austenitic (primary and eutectic) and carbide phases were strongly related to the general corrosion behavior of the HCCI.

• Korean Journal of Metals and Materials
• /
• v.49 no.10
• /
• pp.780-789
• /
• 2011

The effects of alloyed carbon on the pitting corrosion, the general corrosion, and the passivity behavior of Fe18Cr10Mn0.4NxC (x=0~0.38 wt%) alloys were investigated by various electrochemical methods and XPS analysis. The alloyed carbon increased the general corrosion resistance of the FeCrMnN matrix. Carbon enhanced the corrosion potential, reduced the metal dissolution rate, and accelerated the hydrogen evolution reaction rate in various acidic solutions. In addition, carbon promoted the pitting corrosion resistance of the matrix in a chloride solution. The alloyed carbon in the matrix increased the chromium content in the passive film, and thus the passive film became more protective.

• Corrosion Science and Technology
• /
• v.7 no.3
• /
• pp.173-178
• /
• 2008

Recently an electrochemical noise method (ENM) with three electrodes has gained attention as a corrosion monitoring system in chemical plants. So far a few studies have been carried out for localized corrosion and environmental cracking of chemical plant materials. In this paper the ENM system is briefly summarized. Then an application of ENM to general corrosion for chemical plant materials is described. The emphasis is focused upon the analysis of stress on the corrosion cracking process of austenitic stainless steel in 30% $MgCl_2$ aqueous solution and the corrosion fatigue crack initiation process of 12 Cr stainless steel in 3% NaCl aqueous solution by ENM. Finally future problems for ENM to monitor regarding corrosion and environmental cracking in chemical plants are discussed.

• Journal of Welding and Joining
• /
• v.13 no.3
• /
• pp.89-95
• /
• 1995

Effect of boron on corrosion resistance of Type 304 stainless steel has been studied. Boron tends to segregate at the grain boundaries during cooling after solution treatment, and so boron treated steel usually exhibits a ditch structure under the 10% oxalic acid test. However, it was found that the addition of 25 ppm boron in Type 304 steel has no effect on the general and pitting corrosion resistance while it has a little effect on the intergranular corrosion resistance.

• Journal of Welding and Joining
• /
• v.14 no.4
• /
• pp.71-78
• /
• 1996

The effect of chemical composition on mechanical properry and corrosion resistance of austenitic stainless steel was investigated. The main results obtained were as follows : 1. There was a linear relationship between the tensile strength of stainless steel and the $Cr_{eq}/Ni_{eq}$. The larger the $Cr_{eq}/Ni_{eq}$ was the higher the tensile strength of stainless steel. 2. There was a good correlationship between $Cr_{eq}/Ni_{eq}$ and intergranular, gerneral corrsion rate. 3. Intergranular corrosion rate decreased linearly with increasing Cr content. 4. General corrosion rate decreased linearly with increasing Ni content. 5. Logarithm corrosion rate of intergranular and general corrosion has a linear relationship with all of the factor of $Cr_{eq}/Ni_{eq}$, Cr and Ni content.

• Corrosion Science and Technology
• /
• v.20 no.1
• /
• pp.22-25
• /
• 2021

In the past, Alloy 600 nickel-based alloys have been widely used in steam generators. However, most of them have been replaced by thermally treated alloy 690 tubes in recent years because mill annealed alloy 600 materials are known to be susceptible to stress corrosion cracking. Unlike this general perception, some steam generators using mill annealed alloy 600 tubes show excellent performance even though they are designed, manufactured, and operated in the same way. Therefore, various analyses were carried out to determine causes for the degradation of steam generators. Based on the general stress corrosion cracking mechanism, tube material susceptibility, residual stress, and sludge deposits of steam generators were compared to identify factors affecting stress corrosion cracking. It was found that mill annealed alloy 600 steam generator tubes showed higher resistance to stress corrosion cracking when the amount of sludge deposits on tube surface was smaller and residual stress generated during the fabrication was lower.

• Korean Journal of Metals and Materials
• /
• v.48 no.8
• /
• pp.741-748
• /
• 2010

We studied the corrosion and oxidation properties of Fe-18Cr-0.4Nb-(0.1~0.6)Ti-(1~3)Si-(0.5~2)Mo stainless steel. The resistance to general and pitting corrosion was evaluated and the results were analyzed by Response Surface Methodology (RSM) as a function of alloy composition. The effects of alloy composition and heat treatment on the oxidation resistance were also examined. Mo increased both general corrosion resistance and pitting corrosion resistance. Si improved the resistance of the alloys to pitting corrosion. Si was also beneficial for general corrosion resistance of the alloys containing Mo at more than 1 wt.%. However, Mo was detrimental when its content was lower. Effects of Ti on general corrosion properties appeared to be weak and a high concentration of Ti appeared to deteriorate pitting resistance. The thickness of the oxidation scale increased and adhesion of the scale worsened as the temperature increased from $800^{\circ}C$ to $900^{\circ}C$. Weight gain of the alloys due to oxidation at $900^{\circ}C$ clearly showed that the resistance to oxidation is improved by annealing at $860^{\circ}C$ and an increase of Si content.

• Journal of Industrial Technology
• /
• v.17
• /
• pp.291-295
• /
• 1997

The tests of stress corrosion cracking in structural carbon steel were carried out under the conditions of acid fog and general water. As the result of measurement SCC rupture time under acid fog was observed to be much shorter than that of general water at the same stress level. Therefore, acid fog drops the SCC strength in structural carbon steel due to strong corrosion. In the SCC process by acid fog, crack initiation was caused by pit corrosion and local stress concentration, and distinctive feature of crack growth shows branching since crack grows to the corrosion direction. Moreover, corrosion products were observed by clevage corrosion on the crack surfaces.

• Corrosion Science and Technology
• /
• v.14 no.6
• /
• pp.280-287
• /
• 2015

The German Guidelines for stainless steel in buildings (Z.30.3-6) issued by the German Institute for Building Technology (DIBt) categorizevarious stainless steel grades into five corrosion resistance classes (CRCs). Only 21 frequently used grades are approved and assigned to these CRCs. To assign new or less commonly used materials, a large program of outdoor exposure tests and laboratory tests is required. The present paper shows theresults of stress corrosion cracking (SCC) tests that can distinguish between different CRCs. Slow strain rate tests (SSRT) were performedin various media and at different temperatures. CRC IV could be distinguished from CRC II and CRC III with a 31.3 % $Cl^-$ as $MgCl_2$ solutionat $140^{\circ}C$. CRC II and CRC III could be differentiated by testing in a 30% $Cl^-$ as $MgCl_2$ solutionat $100^{\circ}C$.

• Corrosion Science and Technology
• /
• v.11 no.5
• /
• pp.196-204
• /
• 2012

Corrosion failure of petrochemical facilities is one of the difficulties in maintenance, since operating conditions of crude oil production, storage, and refinement are very aggressive. UNS N08810, which has been used for crude oil transportation pipes and storage tanks in petrochemical industries, shows good resistance to general corrosion and localized corrosion in several environments. Among its environments, UNS N08810 showed better corrosion resistance in fuel gas containing sulfuric acid and phosphoric acid and sulfur. However, ductility and toughness at high temperature over about $500^{\circ}C$ were greatly reduced due to microstructural change. In general, welding process is the representative method to join the parts in industrial components. Because the alloy by welding can be sensitized and corroded, the manufacturing process should be controlled. In this work, UNS N08810 was used and heat treatment conditions including solution and stabilization treatments were controlled. Oxalic acid etch test by ASTM A262 Practice A was done to evaluate the qualitative sensitization in room temperature. Huey test by ASTM A262 Practice C was done to evaluate the intergranular corrosion rate in boiling 65% $HNO_3$ solution. Also, the microstructure by thermal history was analyzed. Experimental alloy showed high intergranular corrosion rate and its corrosion mechanism was elucidated.