• Macromolecular Research
• /
• v.9 no.3
• /
• pp.171-178
• /
• 2001

We report the diffraction behavior of the functionalized sol-gel film composed of two different silanes. One silane (SGDR1) contains disperse red 1 (DR1) that is composed of an azobenzene unit. The other silane (SGCHC) bears a chalcone derivative that is photocrosslinkable under UV irradiation. Two-beam coupling method was employed for fabricating the diffraction gratings. The dynamics of formation and erasure of the gratings was studied in term of the variation of the diffraction efficiency. The decaying behavior of the polarization efficiency was also observed after turning off the two pump beams. For complete erasure of the diffraction gratings, we irradiated the linearly polarized single beam. During two-beam coupling, we irradiated UV light on the film surface. The effects of the photocrosslink between the double bonds in chalcone units on the value and dynamic properties of diffraction efficiency are mainly studied in this work.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.11C no.2
• /
• pp.18-22
• /
• 2001

The thin films of high permitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)TiO$_3$ thin as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Sio$_2$/Si substrate at 4,000 [rpm] for 10 seconds. The structural characteristics of the surface were analyzed by fractal dimension. The thickness of BST ceramics thin films was about 260∼280 [nm]. The property of the leakage current was stable with 10-9∼10-11[A] when the applied voltage was 0∼3[V]. BST thin films ha low leakage current properties when fractal dimension was low and a coating area was high.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.4
• /
• pp.1177-1182
• /
• 2012

The corrosion resistance of 316L stainless steel coated with NiO-YSZ (Ni added yttria stabilized zirconia) was examined in a proton exchange membrane fuel cell (PEMFC) environment. The NiO-YSZ coating was carried out using a sol-gel dip coating method, and the corrosion resistance and interfacial contact resistance (ICR) were determined by the composition and morphology of the NiO-YSZ film. The corrosion resistance increased with increasing Ni content in the NiO-YSZ film, but rapid corrosion was observed when the YSZ film contained more than 15 wt % Ni due to surface cracks. The polarization resistance was improved by several orders of magnitude when 316L stainless steel was coated with a 15 wt % NiO-YSZ film compared to bare 316L. The ICR of the NiO-YSZ film was decreased to that of bare 316L when the YSZ film contained 25 wt % NiO, suggesting the possible application of NiO-YSZ coated stainless steel for a bipolar plate.

• Journal of the Korean Ceramic Society
• /
• v.30 no.11
• /
• pp.897-904
• /
• 1993

CdS doped SiO2 glass coating films which are good candidates for the nonlinear optical materials were prepared by the Sol-Gel method. TEOS, C2H5OH, H2O and HCl were used as starting materials to obtain SiO2 matrix solutions. Then Cd(NO3)2.2H2O and CS(NH2)2 were dissolved into the SiO2 matrix solutions. Coating was performed several times in order to increase the thickness of coated film by the dip-coating method. Then heat treatments were carried out to control the size of CdS microcrystals doped in SiO2 glass matrix with respect to temperatures and times. CdS-doped SiO2 transparent coating films were successfully obtained. CdS crystals were changed from cubic to hexagonal type about $600^{\circ}C$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2010.05a
• /
• pp.31.2-31.2
• /
• 2010

질화물계 발광다이오드는 소비전력이 낮고 발광효율이 높은 조명용 반도체소자로서 다양한 분야에 적용되고 있으나 질화갈륨 반도체 층 및 외부 공기와의 계면에서 발생하는 전반사로 인하여 광추출특성이 매우 낮은 문제점이 있다. 이를 해결하기 위하여 다양한 연구가 진행되고 있으며 투명전극 또는 p형 질화갈륨 층에 주기적인 나노 패턴을 형성하고 이에 따른 난반사 효과를 통해 전반사를 억제시키는 연구가 주로 진행되고 있다. 현재까지의 연구에서 발광다이오드의 광추출향상을 위한 나노 패턴은 플라즈마 식각공정을 통하여 형성되었지만 플라즈마 데미지에 의해 소자의 전기적 특성이 저하되는 문제점이 있었다. 본 연구에서는 플라즈마 식각 공정이 요구되지 않는 sol-gel 임프린팅 공정을 이용하여 발광다이오드의 ITO 투명전극 위에 산화아연 나노 패턴을 직접 형성하였다. Sol 솔루션은 에탄올에 zinc acetate dihydrate와 diethanolamine을 희석하여 제작하였고 이를 스핀코팅 방법을 통해 발광다이오드의 ITO 투명전극 층 위에 도포하였다. 이 후, 고 투습성의 PDMS (Polydimethylsiloxane) 몰드를 이용하여 $190^{\circ}C$에서 임프린팅을 진행하였고 이 과정에서 대부분의 솔벤트(에탄올)는 PDMS 몰드로 흡수되어 임프린팅 후에는 나노 패턴이 형성된 산화아연 gel 박막을 얻을 수 있었다. 최종적으로 $500^{\circ}C$에서 1시간 동안 열처리 하여 발광다이오드의 ITO 투명전극 위에 산화아연 나노 패턴을 형성하였다. 나노임프린팅 기반의 직접 패터닝 공정을 통하여 형성된 산화아연 패턴 층을 XRD 측정을 통해 결정성을 분석하였고 형성된 패턴의 형상을 SEM을 통해 확인하였다. 또한, 산화아연 패턴 유무에 따른 발광다이오드 소자의 광추출효율 비교를 위해 electroluminescence를 측정하였으며, 소자의 전기적 특성은 I-V 측정을 통해 분석하였다.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.3
• /
• pp.305-312
• /
• 2018

This study is about the development of a non-sintered binder (NSB) which does not require a sintering process by using the industrial by-products Phosphogypsum (PG), Waste Lime (WL) and Granulated Blast Furnace Slag (GBFS). In this report, through SEM analysis of the NSB paste hardening body, micropore analysis of paste using the mercury press-in method and microstructure observation were executed to consider the influence of the formation of the pore structure and the distribution of pore volume on strength, and the following conclusions were reached. 1) Pore structure of NSB paste of early age is influenced by hydrate generation amount by GBFS and activator. 2) Through observing the internal microstructure of NSB binder paste, it was found that the strength expression at early age due to hydration reaction was achieved with a large amount of ettringite serving as the frame with C-S-H gel generated at the same time. It was confirmed that C-S-H gel wrapped around ettringite, and as time passed, the amount generated continually increased, and C-S-H gel tightly filled the pores of hardened paste, forming a dense network-type web structure. 3) For NSB-type cement, the degree of formation of gel pores below $10{\mu}m$ had a greater influence on strength improvement than simple pore reduction by charging capillary pores, and the pore size that had the greatest effect on strength was micropores with diameter below $10{\mu}m$.

• Korean Journal of Metals and Materials
• /
• v.49 no.7
• /
• pp.583-588
• /
• 2011

$Cd_xZn_{1-x}O$ thin films were grown on quartz substrates by using the sol-gel spin-coating method. The mole fraction, x, of the $Cd_xZn_{1-x}O$ thin films was controlled from 0 to 1 by changes in the content ratio of the cadmium acetate dehydrate [$Cd{(CH_3COO)}_2{\cdot}2H_2O$] and zinc acetate dehydrate [$Zn{(CH_3COO)}_2{\cdot}2H_2O$]. The effects of the mole fraction on the morphological, structural, and optical properties of the $Cd_xZn_{1-x}O$ thin films were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), and UV-visible spectroscopy. The $Cd_xZn_{1-x}O$ thin films exhibited the polygonal surface morphology and their grain size was increased ranging from 42.1 to 63.9 nm with the increase in the mole fraction. It was observed that the absorption bandgap of the $Cd_xZn_{1-x}O$ thin films decreased from 3.25 to 2.16 eV as the mole fraction increased and the Urbach energy ($E_U$) values changed inversely to the optical bandgap of the $Cd_xZn_{1-x}O$ thin films.

• Journal of Powder Materials
• /
• v.30 no.5
• /
• pp.394-401
• /
• 2023

Li_1.5Al_0.5Ti_1.5(PO₄)₃ (LATP) is considered to be one of the promising solid-state electrolytes owing to its excellent chemical and thermal stability, wide potential range (~5.0 V), and high ionic conductivity (~10^-4 S/cm). LATP powders are typically prepared via the sol-gel method by adding and mixing nitrate or alkoxide precursors with chelating agents. Here, the thermal properties, crystallinity, density, particle size, and distribution of LATP powders based on chelating agents (citric acid, acetylacetone, EDTA) are compared to find the optimal conditions for densely sintered LATP with high purity. In addition, the three types of LATP powders are utilized to prepare sintered solid electrolytes and observe the microstructure changes during the sintering process. The pyrolysis onset temperature and crystallization temperature of the powder samples are in the order AC-LATP > CA-LATP > ED-LATP, and the LATP powder utilizing citric acid exhibits the highest purity, as no secondary phase other than LiTi₂PO₄ phase is observed. LATP with citric acid and acetylacetone has a value close to the theoretical density (2.8 g/cm³) after sintering. In comparison, LATP with EDTA has a low sintered density (2.2 g/cm³) because of the generation of many pores after sintering.

• Corrosion Science and Technology
• /
• v.22 no.6
• /
• pp.447-456
• /
• 2023

In this work, we performed a comparative study examining two coatings on Ti Gr.1 for use in fuel cell bipolar plates. The coatings consisted of carbon black as the conductor along with acrylic polymer and Ti Sol-Gel binder as the binder. Ti Sol-Gel that had precipitated as TiO₂ in areas impregnated between carbon black gaps, thereby acting as a binder for carbon black and serving as a polymer coating. Neither of the coatings peeled off during the 90° bend test to check formability. The contact resistance of the TiO₂ coating was found to be lower than that of the polymer binder coating. Moreover, due to coating shrinkage (denser) that occurred during the heat treatment process, the TiO₂ binder coating showed almost the same level of corrosion resistance, as measured by potentiostatic and EIS tests, despite being thinner than the polymer coating. However, both the polymer binder coating and the TiO₂ binder coating had many pores and irregularities internally (around 10 ~ 100 nm) and on the surface (0.1 ~ 2 ㎛). We considered that these pores and irregularities contributed to the lower corrosion resistance.

• Journal of the Korean Applied Science and Technology
• /
• v.17 no.2
• /
• pp.144-148
• /
• 2000

A modification of the sol-gel method to obtain phase pure superconducting oxides is described. The method starts from organic salts of yttrium, barium and copper, such as acetates, and avoids the sudden and uncontrollable decomposition of the organic fraction which occurs if nitrates are used as starting materials. The aqueous solution obtained with citric acid in an alkaline medium is concentrated under vacuum. The solid so prepared is decomposed at about $300^{\circ}C$ thus giving an oxide precursor containing well dispersed yttrium, barium and copper. Pyrolysis at 850 - $920^{\circ}C$ followed by oxygen annealing gives the superconducting orthorhombic 123 phase. The results of TGA/DTA of the precursor, as well as XRD, electrical and magnetic property measurements on the pyrolysis products are presented and discussed.