• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.7
• /
• pp.718-723
• /
• 2004

Crystal structure of $(Ba-{1-x}La_x)[Mg_\frac{1+x}{3}}Nb_\frac{{2-x}{3}}]O_3$ (BLMN) ceramics with 0\leq1x \geq was investigated using synchrotron X-ray powder diffraction (XRD) and high reso(B $a_{l-x}$L $a_{x}$)[M $g_{(1+x)}$3/N $b_{(2-x)/3}$］ $O_3$lution transmission electron microscopy (HRTEM). When the La content, x, is above 0.1, the 1:2 ordered hexagonal structure found in Ba($Mg_\frac{1}{3}Nb_\frac{2}{3}})O_3$(BMN) was transformed into 1:1 ordered cubic structure. The 1:1 ordered cubic structure was maintained up to x=0.7. When x exceeded 0.7, however, BLMN was transformed into 1:1 ordered structure which has cation displacement and in-phase and anti-phase tilt of octahedra.

• Proceedings of the KIEE Conference
• /
• 2004.11a
• /
• pp.67-69
• /
• 2004

ZnO varistor ceramics which were fabricated with variation of added of 0.01, 0.02, 0.03, 0.05, 0.1mol% $Nb_2O_5$ sintered at $1150^{\circ}C$. In the specimen added 0.05mol% $Nb_2O_5$, sintered density was $5.87g/cm^3$ and electrical properties were superior to any other components. The nonlinear coefficient was 75, and clamping voltage ratio was 1.40. And, endurance surge current in the specimen added 0.05mol% $Nb_2O_5$ was $6500A/cm^2$, and deviation of varistor voltage was -1.7%. As P.C.T and T.C.T environment test were succeed in all specimens, and deviation of varistor voltage in the specimen added 0.3mol% $Nb_2O_5$ was -0.81%. All specimens showed a good leakage current property in the High Temperature Continuous Load Test for 1000hr, at $85^{\circ}C$, and variation rate of the varistor voltage was -1.71%.

• Journal of Surface Science and Engineering
• /
• v.50 no.3
• /
• pp.206-211
• /
• 2017

$BiNbO_4:RE^{3+}$ (RE = Dy, Eu, Sm, Tb) phosphors were prepared by solid-state reaction at $1100^{\circ}C$ and their structural, photoluminescent, and morphological properties were investigated. XRD patterns exhibited that all the synthesized phosphors exhibited a triclinic system with a dominant (210) diffraction peak, irrespective of the type of activator ions. The surface morphologies of rare-earth-ion-doped $BiNbO_4$ phosphors were found to depend strongly on the type of activator ions. The $Eu^{3+}$ and $Dy^{3+}$ doped $BiNbO_4$ phosphors revealed a strong red (613 nm) emission resulting from the $^5D_0{\rightarrow}^7F_2$ transition of $Eu^{3+}$ and a dominant yellow (575 nm) emission originating from the $^4F_{9/2}{\rightarrow}^6H_{13/2}$ transition of $Dy^{3+}$ respectively, which were the electric dipole transitions, indicating that the activator ions occupy sites of non-inversion symmetry in the $BiNbO_4$ phosphor. The main reddish-orange emission spectra of $Sm^{3+}$-doped $BiNbO_4$ phosphors were due to the $^4G_{5/2}{\rightarrow}^6H_{7/2}$ (607 nm) magnetic dipole transition, indicating that the $Sm^{3+}$ ions were located at inversion symmetry sites in the $BiNbO_4$ host lattice. As for $Tb^{3+}$-doped phosphors, green emission was obtained under excitation at 353 nm and its CIE chromaticity coordinates were (0.274, 0.376). These results suggest that multicolor emission can be achieved by changing the type of activator ions incorporated into the $BiNbO_4$ host crystal.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.27-28
• /
• 2005

본 연구에서는$Cr_2O_3$ 와 $Nb_2O_5$ 를 첨가한 $Pb(Zr_{0.54}Ti_{0.48})O_3$ 세라믹스에서 $Nb_2O_5$ 첨가량에 따른 소결 및 압전, 유전특성을 조사하였다. $Pb(Zr_{0.54}Ti_{0.48})O_3$ + 0.2 wt% $Cr_2O_3$ + wt% $Nb_2O_5$ ($0.{\sim}2wt.%$)의 첨가량에 따른 압전, 유전특성 및 미세구조에 관해 연구하였다. 본조성에서 $Nb_2O_5$ 첨가량이 증가함에 따라 입경의 크기는 증가하였으며, 0.5 wt% $Nb_2O_5$ 첨가조성에서 $4\sim5\mu m$의 최대 평균입경을 보이다가 그 이상의 첨가 조성에서 급격히 감소하였다. 유전상수와 kp 는 $Nb_2O_5$ 첨가량이 1.0 wt% 조성까지 증가하였다가 그 이상 조성에서 감소하였다. $Nb_2O_5$ 첨가량이 증가함에 따라 삼방정(rhombohedral)구조에서 정방정(tetragonal)구조로 상전이 일어났으며, 본 조성의 상경계 영역인 0.5 wt% 조성에서 $\varepsilon_r$ = 730, $k_p$ = 0.72, $d_{33}$ = 450, $g_{33}$ = 70의 우수한 압전 특성을 나타내었다. 이러한 조성은 접촉센서용 복합압전소재의 실용가능성을 제시하였다.

• Korean Chemical Engineering Research
• /
• v.51 no.4
• /
• pp.513-517
• /
• 2013

This study focused on the synthesis of $Nb_xSrTi_{1-x}O_3$ photocatalysts which partially inserted Nb ions with excellent ability of fluorescence into the perovskite structured $SrTiO_3$ frameworks and their photocatalytic hydrogen productions from methanol/water splitting corresponding to the molar ratios of Ti and Nb. The characteristics of the synthesized $SrTiO_3$ and $Nb_xSrTi_{1-x}O_3$ powders were analyzed by X-ray diffraction (XRD), energy dispersive X-ray spectrometer (EDS), and UV-Visible spectrometer. The hydrogen evolution from methanol/water photo-splitting was enhanced over $Nb_{0.05}SrTi_{0.95}O_3$ compared to those over $SrTiO_3$ and another $Nb_xSrTi_{1-x}O_3$; 4.9 mL of hydrogen gases was collected after 8 h when 0.5g of $Nb_{0.05}SrTi_{0.95}O_3$ catalyst was used in pH 10.

• Journal of the Korean Data and Information Science Society
• /
• v.25 no.1
• /
• pp.119-130
• /
• 2014

This paper is based on water information system of NIE, National Institute of Environmental Research. We used monthly data of water quality from January, 2013 to August, 2013 starting from measuring point A (nbA) to measuring point N (nbN) located along the Nakdong river main stream. Statistical water quality analysis of BOD (biological oxygen demand) is specified by R programming depending on month, year, and points. Based on BOD measured from Nakdong river's measuring points, we used exploratory data analysis and locally weighted scatter plot smoother (Lowess) trend analysis, which is a method of non-parametic regression analysis, to analyze long-term water tendency and water quality distribution depending on points. Also, we analyzed the period and the measuring point of which the outliers are abundant. As a result, compared to BOD measured in nbM located in Busan along the downstream, BOD measured in nbG located in Daegu and nbI located in Changwon along the midstream showed higher rate of water pollution at a severe level.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.3
• /
• pp.293-300
• /
• 1996

A continuous growth method (Orr's method) were developed to grow LiNbO3 single crystals. The optimum growth condition established are as follows; When the controlled temperature of a platinum crucible were 1190℃∼1210℃, the pulling rate was 2 mm/hr, the feeding rate was 1.5∼2.5 g/hr, and the rotation speed was 20 rpm. The phase and growth orientation of the grown LiNbO3 crystals wer characterized by a X-ray diffraction method. The overflowing phenomena, which induced cracking into the grown crystal during the process, was effectively suppressed by the control of the growth parameter.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1993.05a
• /
• pp.109-112
• /
• 1993

In this paper, We have studied about the microstructure of the piezoceramics PZT that were added with some kinds of additives, such as Niobium(Nb), Iron(Fe) or Manganese(Mn). The grain size of PZT ceramics was decreased with increasing the amounts of additive of Nb or Fe, while increased with increasing Mn. The curie temperature was changed slightly for the PZT ceramics containing $Fe^{3+}$, which is not dependent on the amounts, but $Nb^{5+}$ or $Mn^{2+}$ ion added PZT was lowered. The resistivity was increased with increasing the amounts of $Nb^{5+}$ additive, while decreased for $Mn^{2+}$ additive.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.291-294
• /
• 2000

The crystallization behavior and dc Conductivities of CuO-P$_2$O$_{5}$ -Nb$_2$O$_{5}$ -V$_2$O$_{5}$ glasses prepared by quenching on the copper plate were investigated. The conductivities of the glasses were range from 10$^{-5}$ s.$cm^{-1}$ / at room temperature, but the conductivities of the glass-ceramics were 10$^{-3}$ s.$cm^{-1}$ / increased by 10$^2$order. The crystalline product in the glass-ceramics was CuV$_2$O$_{6}$ . The linear relationship between in($\sigma$T) and T$^{-1}$ suggested that the electrical conduction in the present glass-ceramics would be due to a small polaron hopping mechanism.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.9
• /
• pp.702-710
• /
• 2012

Eco-friendly $(Na,K)NbO_3$ (NKN)-based piezoelectric ceramic materials were fabricated by conventional ceramic method for shear mode piezoelectric energy harvesting application. $NKN-LiTaO_3$ (LT) based compositions were adopted for the high $d_{15}{\times}g_{15}$ which is proportional to harvested energy density. The composition $0.935(Na_{0.535}K_{0.485})NbO_3-0.065LiTaO_3$ was found to be lie on the boundary of tetragonal and orthorhombic phases. With reducing Ta content, the dielectric constant decreased gradually while maintaining high $d_{15}$, which resulted in increased $d_{15}{\times}g_{15}$. The composition $0.935(Na_{0.535}K_{0.485})NbO_3-0.065Li(Nb_{0.990}Ta_{0.010})O_3$ was found to possess excellent piezoelectric and electromechanical properties ($d_{15}{\times}g_{15}=29\;pm^2/N$, $d_{15}$ = 417 pC/N, $k_{15}$ = 0.55), and high curie temperature ($T_c=455^{\circ}C$).