• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.7 no.4
• /
• pp.56-61
• /
• 2008

Cropping metal materials is widely used for feeding processes of various forming method, such as forging, extrusion, drawing, and upsetting. However, cropping has many weak points, which are material loss in part of cutting, chip creation, and much use of lubrication oil, etc. In this study, instead of cropping, a novel process is proposed to cut metal materials, especially stainless steel bar which is known very difficult to crop. Results of FE-analysis will be shown to verify the proposed method comparing with those of the conventional cropping process. Also, fitting products were successfully forged using the fabricated billet by the proposed process.

• Corrosion Science and Technology
• /
• v.14 no.2
• /
• pp.54-58
• /
• 2015

A heavy oil of low quality has been mainly used in the diesel engine of the merchant ship as the oil price has been significantly jumped for several years. Thus, a combustion chamber of the engine has been often exposed to severely corrosive environment more and more because temperature of the exhaust gas of the combustion chamber has been getting higher and higher with increasing of using the heavy oil of low quality. As a result, wear and corrosion of the engine parts such as exhaust valve, piston crown and cylinder head surrounded with combustion chamber are more serious compared to the other parts of the engine. Therefore, an optimum repair welding for these engine parts is very important to prolong their lifetime in a economical point of view. In this study, 1.25Cr-0.5Mo filler metal was welded with SMAW method in the forged steel which would be generally used with piston crown material. And the corrosion properties of weld metal, heat affected and base metal zones were investigated using electrochemical methods such as measurement of corrosion potential, anodic polarization curves, cyclic voltammogram and impedance etc. in 35% $H_2SO_4$ solution. The weld metal and base metal zones exhibited the highest and lowest values of hardness respectively. And, the corrosion resistance of the heat affected and weld metal zones was also increased than that of the base metal zone. Furthermore, it appeared that the corrosive products with red color and local corrosion like as a pitting corrosion were more frequently observed on the surface of the base metal zone compared to the heat affected and weld metal zones. Consequently, it is suggested that the mechanical and corrosion characteristics of the piston crown can be predominantly improved by repair welding method using the 1.25Cr-0.5Mo electrode.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.4 no.3
• /
• pp.155-158
• /
• 2003

The effects of Mn, V addition on the behavior of structure and the effects of cooling rate of S20C steel for use of Tn housing and valve for automotive parts have been investigated. Transformation start temperature measured from inflection point of cooling curves has been found out to decrease with increasing cooling rate and to be more sensitive to Mn contents when cooling rate is fast. It was therefore shown that the grain was refined. If there is a big compacting pressure, it is indicated that hardness becomes much greater at surface than inside.

• Plant Journal
• /
• v.10 no.2
• /
• pp.48-59
• /
• 2014

Coupons which have same figure as weld joint of the forged steel valves and 1 inch nominal weld thickness were manufactured using ASTM A182 F92 material. After welding with GTAW method, the welded specimens have been post-weld heat treated at $705^{\circ}C$, $735^{\circ}C$, $750^{\circ}C$, $765^{\circ}C$, $795^{\circ}C$ and $825^{\circ}C$ for 1 hour per 1 inch nominal weld thickness each (Group 1) to evaluate characteristics of welds based on various holding temperature. Indeed, 3 welded specimens were post-weld heat treated for 30 minutes, 1 hour and 2 hour (Group 2) at $735^{\circ}C$ to evaluate characteristics of welds based on various holding time. Hardness values were measured at the weld metal, heat affected zone and base metal to observe hardness change depending on the condition. As a result of the evaluation, appropriate holding temperature for PWHT is proved as $750^{\circ}C$ and $765^{\circ}C$ for 1hour per 1 inch nominal weld thickness. Indeed, holding for 1 hour per 1 inch nominal weld thickness was insufficient for PWHT effect when the holding temperature was at $735^{\circ}C$. The microstructure of post-weld heat treated weld metal was determined as tempered-martensite structure.

• Journal of Ocean Engineering and Technology
• /
• v.30 no.4
• /
• pp.334-340
• /
• 2016

The combustion chamber of a diesel engine is often exposed to a more serious wear and corrosion environment than other parts of the engine because its temperature increases as a result of using heavy oil of low quality. Therefore, repair and built-up welding methods must be performed on worn or corroded parts of the piston crown, exhaust valve, etc. from an economical point of view. In this study, Inconel 718 filler metal was used in repair welding on the groove of a forged steel specimen for a piston crown, along with built-up welding on the surface of another forged steel specimen. Then, the corrosion characteristics of the weld metal zone for the repair welding and the deposited metal zone for the built-up welding were investigated using electrochemical methods in a 35% H₂SO₄ solution. The deposited metal zone indicated better corrosion resistance than the weld metal zone, showing a nobler corrosion potential, higher impedance, and smaller corrosion current density. It is considered that metal elements with good corrosion resistance were generally included in the filler metal, and these elements were also greatly involved in the deposited meta by built-up welding, whereas the weld metal consisted of metal elements mixed with both the filler metal and base metal elements because of the molten pool produced by the repair welding. Finally, it is considered that the hardness of the weld metal was increased by the repair welding, whereas the built-up welding improved the corrosion resistance of the deposited metal.