• Journal of the Korea Concrete Institute
• /
• v.12 no.2
• /
• pp.43-51
• /
• 2000

This study is to investigate for the frost resistance of high-flowing concrete using finely ground granulated blast-furnace slag with experimental parameters, such as type of binder, type of superplasticizer and method of curing. The resistance to freezing and thawing of high-flowing concrete by type of binder and superplasticizer is presented differently. Though the frost resistance of high-flowing concrete is satisfactory under standard condition, it is required that high-flowing concrete has entrained air like plain concrete. Because the critical spacing factor, being capacity of frost resistance, of high-flowing concrete is longer that of plain concrete, the frost resistance of high-flowing concrete, using finely ground granulated furnace blast slag, is superior to that of plain concrete.

• Journal of Advanced Marine Engineering and Technology
• /
• v.39 no.5
• /
• pp.536-541
• /
• 2015

Copper has been used extensively as an electric wire or as a base material in various types of machineries owing to its good electrical and thermal conductivity and good fabricating property, as well as its good corrosion resistance compared to iron. Furthermore, the copper-nickel alloy has significant corrosion resistance in severely corrosive environments. Although, cupro-nickel alloy shows better corrosion resistance than the brass and bronze series, this alloy also corroded in severely corrosive environments, including aggressive chloride ions, dissolved oxygen, and condition of fast flowing seawater. In this study, and annealing treatment at various annealing temperatures was carried out on the cupro-nickel (Cu-10%Ni) alloy, and the effects of annealing were investigated using electrochemical methods, such as measuring the polarization and impedance behaviors under flowing seawater conditions. The corrosion resistance increased by annealing compared to non heat treatment in the absence of flowing seawater. In particular, the sample annealed at $200^{\circ}C$ exhibited the best corrosion resistance. The impedance in the presence of flowing seawater showed higher values than in the absence of flowing seawater. Furthermore, the highest impedances was observed in the sample annealed at $800^{\circ}C$, irrespective of the present of flowing seawater. Consequently, the corrosion resistance of cupro-nickel (Cu-10%Ni) alloy in a severely corrosive environment can be improved somewhat by annealing.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.385-390
• /
• 1997

In the mixing proportion of high flowing concrete we have to use quantity of power such as cement and superplasticizer, and increase the proportion of fine aggregate more than that of plain concrete to increase flowability and segregation resistance. Therefore, the fresh state of high flowing concrete is largely affected by superplasticizer and change of grade the percentage of surface water. This study aims at development of self-filling up high flowing concrete without compaction, in case of using the fine aggregate of standard grade range, by examination on the influence of fresh state of high flowing concrete, and by understanding influence on various fluidity such as flowability, reinforcement passibility, fillingability, segregation resistance.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.45 no.7
• /
• pp.27-37
• /
• 2003

This study was performed to examine the flowing ability and filling ability of polypropylene fiber reinforced high performance concrete. The slump flow was decreased with increasing the polypropylene fiber content, rapidly. At the box-type filling ability, the difference of box height was increased with increasing the fiber content and the box-type passing ability was closed in fiber content 1 %. The final flowing distance of L-type was decreased with increasing the fiber content. Also, it was decreased above 0.75% of polypropylene fiber content, rapidly. The filling ability of L-type was badly showed above polypropylene fiber content 0.75%. Also, the compressive strength was decreased with increasing the fiber content, but the flexural strength was shown higher than that of the concrete without fiber. At the impact resistance, drop numbers for reaching in final fracture were increased with increasing the fiber content. Also, the drop numbers for reaching initial fracture of 1mm were increased with increasing the fiber content. At the acid resistance, the percent of original mass was decreased with increasing the fiber content.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.04a
• /
• pp.220-226
• /
• 1997

High flowing concrete has flowability, passability, segregation resistance and so on, and there are so many influence factor to affect to fluidity of high flowing concrete, therefore it is so difficult to evaluate exactly the properties in fresh state. This study is to analyze and evaluate thefluidity of high flowing concrete affected by fine aggregate with test method such as, slump-flow test, V-lot test, L-flow test, Box filling test.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.6
• /
• pp.281-289
• /
• 1998

This study has been performed to test the flowability and filling ability of high flowing concrete as well as distribution of aggregate and pore of core specimen, heat of hydration, compressive strength and core strength of concrete. In addition, the resistance to chloride ion penetration and chemical solutionof concrete was tested in order to evaluate the resistance to sea water of concrete and its application of high flowing concrete using blended low heat cement in the field of Seohae Grand Bridge. The properties of high flowing concrete with blended low heat cement were compared with ordinary 25-240-15 concrete using Type V cement. As the results of this study, the flowability and filling ability of high flowing concrete with blended low heat cement is satisfied without vibration. Though the cement content of high flowing concrete with blended low heat cement was 400kg/m$^2$, the rising temperature of it was relatively lower than that of the ordinary 25-240-15 concrete with Type V cement. Also, the compressive of high flowing concrete with blended low heat cement is similar to that of the ordinary 25-240-15 concrete with Type V cement.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10a
• /
• pp.307-312
• /
• 1998

Recently the study on high flowing concrete which has high workability and Self-compacting is being proceeded actively in the university and corporative laboratory. There are some cases that has been applied to the field. This high flowing concrete has higher fluidity and segregation resistance than Plain of flowing concrete. And it is being focused as a remarkable know-how which can make high-quality concrete and reduction effect of labor force. This properties of high flowing concrete are influenced by the relationship of several factors; binder content, water binder ratio and unit water content. It is the aim of this study to propose reference data at mix design of high flowing concrete, after comparing and analyzing the fluidity and strength properties of high flowing concrete according to water binder content ratio and unit water content.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10a
• /
• pp.301-306
• /
• 1998

Aggregate as the component of High Flowing Concrete has much influence on the properties of High Flowing Concrete according to the quality and condition because the aggregate occupy a lot of concrete volume. The shape and size of aggregate affect a lot spatial passibility and fillingability. The segregation is easy to occur when the rate of Fine aggregate is high so that Fluidity is much affected by aggregate factor. In this study, therefore, we try to understand the various fluidity according to the fine aggregate of standard grade rang, the size of Coarse aggregate and the rate of fine aggregate to confirm the manufacturing possibility of High Flowing Concrete by examination on the influence of fresh state of high flowing concrete such as flowability, reinforcement passibility, fillingability, segregation resistance.

• Journal of the Korea Institute of Building Construction
• /
• v.4 no.2
• /
• pp.129-136
• /
• 2004

High fluidity concrete(HFC) requires high dosage of superplasticizer to acquire sufficient fluidity, and high contents of fine powder and viscosity enhancing admixtures to resist segregation. The use of high amount of admixtures to make HFC at batcher plant in ready mixed concrete company is one of the reasons to raise the manufacturing cost of HFC. For this reason, new type of manufacturing method of HFC are described using both flowing concrete method and segregation reducing superplasticizer(SRS) in order to gain economical profit and offer the convenience for quality control.. As dosage of melamine based superplasticizer increases, it shows that fluidity and bleeding increase, while air contents and ratio of segregation resistance decrease. It also shows that addition of viscosity agent into superplasticizer reduce bleeding and improve segregation resistance of concrete. Dosage of AE agent into superplasticizer containing viscosity agent recovers loss of air contents during flowing procedure. Combination of proper contents of superplasticizer, viscosity agent and AE agent make possible to develope segregation reducing type superplasticizer. Compressive strength of high fluidity concrete applying flowing method with it is higher than that of base concrete. No differences of compressive strength between compacting methods are found. For the estimation of construction cost of high fluidity concreting using segregation reducing type superplasicizer, under same strength levels, although material cost of high fluidity concrete is somewhat higher than that of plain concrete due to segregation reducing type superplasticizer cost, labor cost and equipment cost of high fluidity concrete is cheaper than that of plain concrete. However, based on the strength differences, high fluidity concrete shows lower material cost, labor cost and equipment cost than that of plain concrete due to decreasing in size of member and re-bar caused by high strength development of concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.743-746
• /
• 2004

This research investigates experimentally an effect on the properties of the high flowing concrete according to variations of concrete materials and site conditions. Variations of sensitivity test are selected items as followings; (1)Concrete temperature, (2)Unit water(Surface moisture of fine aggregate), (3)Fineness modulus of fine aggregate, (4)Addition ratio of high-range water reducing agent. And fresh conditions of the high flowing concrete should be satisfied with required range including slump flow$(65{\pm}5cm)$, 50cm reaching time of slump flow$(4\~10sec)$, V-box flowing time$(10\~20sec)$, U-box height(min.300mm) and air content$(4{\pm}1\%)$. As results of sensitivity test, material variations and site conditions should be satisfied with the range as followings; (1)Concrete temperature is $10\~20^{\circ}C$ (below $30^{\circ}C$), (2)Surface moisture of fine aggregate is within ${\pm}0.6\%$, (3)Fineness modulus of fine aggregate is $2.6{\pm}0.2$ and (4)addition ratio of high range water reducing agent is within $1\%$ considered flow-ability, self-compaction and segregation resistance of the high flowing concrete.