• Journal of the Korean Recycled Construction Resources Institute
• /
• v.12 no.2
• /
• pp.152-161
• /
• 2024

This paper investigates the manufacturing and fundamental quality characteristics of potassium magnesia phosphate-based non-cement high-volume fly ash repair mortar. To derive the optimal mix for non-cement mortar, the manufacturing characteristics were evaluated based on the magnesia ratio, and the mortar manufacturing characteristics were assessed with the fly ash mixture. Additionally, the non-cement magnesia repair mortar was produced considering the effects of fly ash mixture and basalt fiber. The evaluation results determined the optimal mix of non-cement magnesia repair mortar, and the feasibility was examined through workability and fundamental quality assessments. The optimal magnesia ratio was found to be P:M 1:0.5, with W/B at 30 %. It was also confirmed that mixing FA and basalt fiber improves fiber dispersion and workability. Even with over 50 % FA mixture, the target strength was achieved within six hours, with a flow increase of up to 18 % and a flexural strength decrease of about 1-2 MPa.

• Korean Journal of Agricultural Science
• /
• v.12 no.1
• /
• pp.75-85
• /
• 1985

This study is intended to find out the influence of Lignosulfonic Acid Type Admixture on compressive, tensile, flexural strength and dispersing action of mortar, and fixation of by-product of pulp industry. 1. The more Pozzolith-84 is added, the larger flow value is. The admixture of lignosulfonic acid type adhere to cement particles and the surface potential of particles is generated. On account of the repulsion among the cement particles, they are dispersed and the mortar get workable, so the production cost of precast product is curtailed and the amount of cement is reduced in a certain workability of mortar. 2. The strength of mortar is greater than plain mortar when P/C added is 0.2 and 0.4%. As time passed the potential energy is reduced and the distance of particles which lignosulfonic acid adhered to get near according as the amount of adhesion is increased. The setting and hardening reaction of morter is occurred in close state, so the strength of mortar is increased a little. The strength of mortar is less than plain mortar when amount P/C added is 0.8%. Pozzolith-84 is mainly composed of lignosulfonic acid and lignin does not influence the hardening of mortar, therefore the remained $SO_3$, $SO_3H$ are the reason of decrease of strength. 3. There is high significance between specific gravity and compressive strength. The larger specific gravity is, the more compressive strength is increased. There is high significance between 7 day's strength and 28 day's strength. The larger compressive strength is, the more tensile and flexural strength are increased. 4. Since Pozzolith-84 is a by-product of pulp industry, by using the Pozzolith-84 admixture the concreate quality is improved. The water pollusion is reduced according to fix by-products in concrete structure.

• Journal of the Korea Concrete Institute
• /
• v.19 no.5
• /
• pp.549-555
• /
• 2007

Although blast furnace slag has been widely used in concrete as a cementitious admixture or aggregate for many years, the slowly cooled steel slag is not used in concrete but mainly in road. Its use in concrete operates problem such as the lack of volume stability due to high free CaO content, which can be potentially hazardous in concrete. However, the rapidly cooled steel slag by atomization has a low free CaO content, a high density, and a spherical shape, so it is expected to use in concrete so much. This paper is to understand the probability that the rapid cooled steel slag can replace the silica sand used as aggregate in the epoxy mortar. We did the experimental study on the properties of the epoxy mortar having various replacement proportion of rapidly cooled steel slag. This study shown that increasing content of the rapidly cooled steel slag in epoxy mortar lead to increase largely the passing time of nozzle by O-lot, compressive strength and flexural strength. However except the flow is almost same level. So we understand that the rapidly cooled steel slag has positive effect on increasing of properties in epoxy mortar.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.2
• /
• pp.117-125
• /
• 2014

This paper examines the fundamental properties of alkali-activated slag cement (AASC) activated by sodium hydroxide (NaOH). The water to binder (W/B) ratio was 0.4 and 0.5. And concentration of activator were 2M and 4M. Five mix design of each W/B ratios was considered. The N0 mixture was KS L 5109 method and N1~N4 were varied in different mixing time, mix step and entering points of fine aggregate. Test results clearly showed that the flow value, strength and drying shrinkage development of AASC were significantly dependent on the entering point of fine aggregate. The flow value tended to decreases with delaying entering point of fine aggregate. The compressive strength and flexural strength increases with delaying entering point. Moreover, the XRD analysis confirmed that there were sustain these results. The drying shrinkage increases with delaying entering point of fine aggregate. Futhermore, a modified mixing method incorporating all hereby experimentally derived parameters, is proposed to improvement the physical properties of AASC.

• Journal of the Korean Society of Radiology
• /
• v.11 no.5
• /
• pp.297-302
• /
• 2017

Recently, building materials and air purification filters with eco-friendly charcoal are actively studying to reduce the concentration of radon gas in indoor air. In this study, radon reduction performance was assessed by designing and producing new panel-type activated carbon filter that can be handled more efficiently than conventional charcoal filters, which can reduce radon gas. For the fabrication of our panel-type activated carbon filter, first the pressed molding product after mixing activated carbon powder and polyurethane. Then, through diamond cutting, the activated carbon filter of 2 mm, 4 mm and 6 mm thickness were fabricated. To investigate the physical characteristics of the fabricated activated carbon filter, a surface area and flexural strength measurement was performed. In addition, to evaluate the reduction performance of radon gas in indoor, the radon concentration of before and after the filter passes from a constant amount of air flow using three acrylic chambers was measured, respectively. As a result, the surface area of the fabricated activated carbon was approximately $1,008m^2/g$ showing similar value to conventional products. Also, the flexural load was found to have three times higher value than the gypsum board with 435 N. Finally, the radon reduction efficiency from indoor gas improved as the thickness of the activated carbon increases, resulting in an excellent radon removal rate of more than 90 % in the 6 mm thick filter. From the experimental results, the panel-type activated carbon is considered to be available as an eco-friendly building material to reduce radon gas in an enclosed indoor environment.

• Journal of the Korea Concrete Institute
• /
• v.13 no.1
• /
• pp.30-37
• /
• 2001

Generally, polymer mortar made with unsaturated polyester(UP) resin has a high curing shrinkage. This is an inadequate as repair material and construction products that have been widely used for years recently. To overcome these problems, polymer researchers and engineers have used shrinkage-reducing additives, which are usually specific thermoplastic polymers. The objective of this study is to evaluate the effects of shrinkage-reducing additive on the curing shrinkage and strengths of UP mortar. UP mortars are prepared with expanded polystyrene(EPS) ratio in styrene monomer(SM), (EPS/PS, PS=EPS+SM), and the ratio of total polystyrene resin(PS) to UP resin, (PS/UP). And it is tested for viscosity of UP resin, slump-flow, working life, flexural and compressive strengths, and curing shrinkage tests. From the test results, viscosity of resin for UP mortar increases with increasing PS content. Curing shrinkage of UP mortar is considerably smaller than that of plain UP mortar, nevertheless, reduction in the strengths is not recognized according to adding PS resin. In this study, we can obtain the optimum mix proportions of UP mortar using PS resin which made of waste expanded polystyrene.

• Journal of the Korea Concrete Institute
• /
• v.21 no.1
• /
• pp.3-11
• /
• 2009

The increased demand and consumption of coal has intensified problems associated with disposal of solid waste generated in utilization of coal. Major utilization of coal by-products has been in construction-related applications. Since fly ash accounts for the part of the production of utility waste, the majority of scientific investigations have focused on its utilization in a multitude of use, while little attention has been directed to the use of bottom ash. As a consequence of this neglect, a large amount of bottom ash has been stockpiled. However, the need to obtain safe and economical solution for its proper utilization has been more urgent. The study presented herein is designed to ascertain the performance characteristics of bottom ash, as autoclaved lightweight foamed concrete product. The laboratory test results indicated that tobermorite was generated when bottom ash was used as materials for hydro-thermal reaction. According to the analysis of variance, at the fresh state, water ratio affects on flow and slurry density of autoclaved lightweight foamed concrete, but foam ratio influences on slurry density, while, at the hardened state, foam ratio affects on the density of dry and the compressive strength but doesn't affect on flexural and tensile strength. In the results of response surface analysis, to obtain target performance, the most suitable mix condition for lightweight foamed concrete using bottom ash was water ratio of 70$\sim$80% and foaming ratio of 90$\sim$100%.

• Elastomers and Composites
• /
• v.38 no.3
• /
• pp.262-272
• /
• 2003

Maleic anhydride-grafted-polypropylene(PP-g-MA) were used as a blend component and a compatibilizer, respectively, for two reactive blends of polyamide 66(PA 66)PP-g-MA binary blends and PA 66/polypropylene(PP)/PP-g-MA ternary blends. The goal of this work was to investigate the property differences between binary and ternary blends. Tensile strength, flexural modulus, heat deflection temperature, impact strength, melt flow index, and the dependence of melt viscosity on the shear rate were examined. The impact strengths of binary blends were higher than those of ternary blends at all compositions, since the in situ synthesis of PP-g-PA 66 copolymer through the imide formation between the amine end group of PA 66 and the anhydride group of PP-g-MA gave the increase of molecular weight and was more popular in binary blends than in ternary blends. In case of ternary blends, most of the properties were superior to those of binary blends, owing to the better properties of PP compared with PP-g-MA. The toughened binary blends with 70/30(PA 66/PP-g-MA) and 80/20 ratios were not commercially applicable due to their poor processibility. So, the ternary blends which showed lower melt viscosities were recommended for the commercial applications.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.1
• /
• pp.1-8
• /
• 2019

Phase change material(PCM) has the capacity to absorb or release energy in heat when the phase changes. This study conducted to investigate the effect of strontium-based PCM on the hydration heat and mechanical properties of mortar with fly ash and blast furnace slag. The amounts of PCM were 1%, 2%, 3%, 4%, and 5% by the cementitious materials weight. The tests about mortar flow, semi-adiabatic temperature rise, compressive and flexural strength tests were carried out for twelve types of mortar mixtures. The test results indicated that the use of PCM was effective to reduce hydration heat and retard hydration of mortar with industrial by-products. In particular, the heat generation rate of mortars with fly ash was lower than that of mortars with blast furnace slag. The compressive strength of mortar with fly ash and blast furnace slag were decreased with increasing PCM ratio.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.1
• /
• pp.92-100
• /
• 2022

In this paper, to evaluate the effect of SC on the crack self-healing performance and mechanical recovery performance of cement composites, encapsulated intumescent inorganic material-based solid healing materials were prepared. SC was mixed with cement composite materials to evaluate the basic properties, permeability test, and load reload test. SC slightly improved the flow of cement composites, and the compressive strength decreased by about 10 %. Also, the flexural strength decreased by about 30 %. It was found that when SC was mixed with the cement composite material by 5 %, the crack self-healing rate of Plain was improved by about 𝜟10 %. As a result of the load reload test, it was found that the mechanical recovery rate of Plain was improved by about 𝜟20 %. In addition, as a result of analyzing the correlation between the crack self-healing rate and the mechanical recovery rate by the load reload test, it is judged that the healing area of the Plain can be increased due to SC.